Exemplary deposition methods may include introducing hydrogen into a processing chamber, a powder disposed within a processing region of the processing chamber. The method may include striking a first plasma in the processing region, the first plasma including energetic hydrogen species. The method may include exposing the powder to the energetic hydrogen species in the processing region. The method may include chemically reducing the powder through a reaction of the powder with the energetic hydrogen species. The method may include removing process effluents including unreacted hydrogen from the processing region. The method may also include forming a layer of material on grains of the powder within the processing region.

Nanopowders containing nanoparticles having a core particle with a thin film coating. The core particles and thin film coatings are, independently, formed from at least one of a rare earth metal-containing oxide, a rare earth metal-containing fluoride, a rare earth metal-containing oxyfluoride or combinations thereof. The thin film coating may be formed using a non-line of sight technique such as atomic layer deposition (ALD). Also disclosed herein are nanoceramic materials formed from the nanopowders and methods of making and using the nanopowders.

A method of manufacturing a multilayer ceramic electronic component includes: preparing a dielectric magnetic composition including base material powder particles including BaTi.sub.2O.sub.5 or (Ba.sub.(1-x)Ca.sub.x)Ti.sub.2O.sub.5 (0≤x≤0.1), the base material powder particles having surfaces coated with one or more of Mg, Mn, V, Ba, Si, Al and a rare earth metal; preparing ceramic green sheets using dielectric slurry including the dielectric magnetic composition; applying an internal electrode paste to the ceramic green sheets; preparing a green sheet laminate by stacking the ceramic green sheets to which the internal electrode paste is applied; and preparing a ceramic body including dielectric layers and a plurality of first and second internal electrodes arranged to face each other with each of the dielectric layers interposed therebetween by sintering the green sheet laminate.

The present invention discloses magnesia and a method for manufacturing same, wherein the magnesia can be produced into granules of various shapes and sizes and can be improved in moisture resistance with the formation of a moisture resistant surface oxide layer by donor addition and then thermal treatment. The magnesia according to the present invention comprises a MgO granule; and a surface oxide layer formed on a surface of the MgO granule and a composition of the surface oxide layer is different from a composition of an inside of the MgO granule.

A magnetizable abrasive particle comprises a ceramic body having an outer surface and a magnetizable layer disposed on a portion, but not the entirety, of the outer surface. The ceramic body comprises a platelet having two opposed major facets connected to each other by a plurality of side facets. The magnetizable layer completely covers one of the two opposed major facets, and the magnetizable layer has a magnetic dipole oriented perpendicular or parallel to the facet which it completely covers. A plurality of the magnetizable abrasive particles, and abrasive articles including them are also disclosed. Methods of making the foregoing are also disclosed.

A ceramic electronic component includes a body, including a dielectric layer and an internal electrode. The dielectric layer includes a plurality of dielectric grains, and at least one of the plurality of dielectric grains has a core-dual shell structure having a core and a dual shell. The dual shell includes a first shell, surrounding at least a portion of the core, and a second shell, surrounding at least a portion of the first shell. The dual shell includes different types of rare earth elements R1 and R2, and R2.sub.S1/R1.sub.S1 is 0.01 or less and R2.sub.S2/R1.sub.S1 is 0.5 to 3.0, where R1.sub.S1 and R1.sub.S2 denote concentrations of R1 included in the first shell and the second shell, respectively, and R2.sub.S1 and R2.sub.S2 denote concentrations of R2 included in the first shell and the second shell, respectively.

The present invention provides a method for producing a powder containing zirconia particles and a fluorescent agent that enables easy production of a zirconia sintered body having both high translucency and high strength despite containing a fluorescent agent. The present invention relates to a method for producing a zirconia particle- and fluorescent agent-containing powder, comprising: a mixing step of mixing a zirconia particle-containing slurry and a liquid-state fluorescent agent; and a drying step of drying the slurry containing the zirconia particles and the fluorescent agent. Preferably, the fluorescent agent comprises a metallic element, and the powder comprises the fluorescent agent in an amount of 0.001 to 1 mass % in terms of an oxide of the metallic element relative to a mass of zirconia. Preferably, the zirconia particles have an average primary particle diameter of 30 nm or less. Preferably, the zirconia particles comprises 2.0 to 9.0 mol % yttria.

The present invention provides a zirconia sintered body containing a fluorescent agent and having excellent translucency and excellent strength. The present invention also provides a zirconia shaped body and a zirconia calcined body from which the zirconia sintered body can be obtained. The present invention relates to a zirconia sintered body comprising a fluorescent agent, wherein the zirconia sintered body comprises 4.5 to 9.0 mol % yttria, and has a crystal grain size of 180 nm or less, and a three-point flexural strength of 500 MPa or more. The present invention relates to a zirconia shaped body comprising a fluorescent agent, wherein the zirconia shaped body comprises 4.5 to 9.0 mol % yttria, and has a three-point flexural strength of 500 MPa or more after being sintered at 1,100° C. for 2 hours under ordinary pressure, and a crystal grain size of 180 nm or less after being sintered at 1,100° C. for 2 hours under ordinary pressure. The present invention relates to a zirconia calcined body comprising a fluorescent agent, wherein the zirconia calcined body comprises 4.5 to 9.0 mol % yttria, and has a three-point flexural strength of 500 MPa or more after being sintered at 1,100° C. for 2 hours under ordinary pressure, and a crystal grain size of 180 nm or less after being sintered at 1,100° C. for 2 hours under ordinary pressure.

The present invention provides a ceramic composition, comprising a primary mixture and a secondary mixture, wherein the primary mixture comprises a first primary ingredient powder and a second primary ingredient powder, and the first primary ingredient powder comprises BaTiO.sub.3, the second primary ingredient powder comprises any of SrTiO.sub.3, Ba.sub.0.95Ca.sub.0.05TiO.sub.3, BaZr.sub.0.1Ti.sub.0.9O.sub.3 or a combination thereof, and the secondary mixture comprises a rare earth oxide, a silicon oxide and an alkaline-earth metal oxide. The present invention further provides a ceramic sintered body obtained by sintering the ceramic composition, and a capacitor comprising the ceramic sintered body and a method for manufacturing the same; wherein the capacitor satisfies EIA-X8R specification, and has a high dielectric constant.

A method of manufacturing a multilayer ceramic electronic component includes: preparing a dielectric magnetic composition including base material powder particles including BaTi.sub.2O.sub.5 or (Ba.sub.(1-x)Ca.sub.x)Ti.sub.2O.sub.5 (0x<0.1), the base material powder particles having surfaces coated with one or more of Mg, Mn, V, Ba, Si, Al and a rare earth metal; preparing ceramic green sheets using dielectric slurry including the dielectric magnetic composition; applying an internal electrode paste to the ceramic green sheets; preparing a green sheet laminate by stacking the ceramic green sheets to which the internal electrode paste is applied; and preparing a ceramic body including dielectric layers and a plurality of first and second internal electrodes arranged to face each other with each of the dielectric layers interposed therebetween by sintering the green sheet laminate.