A dielectric composition includes dielectric particles, grain boundary phases, and segregations. The dielectric particles each include a perovskite compound represented by ABO.sub.3 as a main component. The grain boundary phases are located between the dielectric particles. The segregations exist in a part of the grain boundary phases and include at least Al, Si, and O. A molar ratio (Al/(Al+Si)) of an Al content to a total content of Al and Si in the segregations is 0.45 or more and 0.75 or less.

A coating composition is described, for use in the foundry, in particular comprising particulate, amorphous silicon dioxide (SiO.sub.2) and an aqueous phase having a pH of at most 5, and also coated, waterglass-bound foundry molding elements, especially coated, waterglass-bound foundry molds and foundry cores, which each comprise a coating composition of the invention. Further described is the use of a coating composition of the invention for producing a coating on a waterglass-bound foundry molding element and a method for producing a waterglass-bound foundry molding element (mold or core) coated with a water-containing refractory coating. Likewise specified is a kit whose contents include a coating composition of the invention.

Green ceramic mixtures include at least one inorganic component, at least one organic binder, and a stable emulsion including at least one lubricant, at least one aqueous solvent, and at least one emulsifier. Methods for forming ceramic bodies include forming a green ceramic mixture including a stable emulsion and extruding the green ceramic mixture. The methods and green ceramic mixtures can be used to produce green and fired ceramic bodies.

Batch mixtures comprising alumina trihydrate for forming ceramic honeycomb bodies comprised of cordierite and methods of manufacturing honeycomb bodies from such batch mixtures are provided.

A method for producing a honeycomb structure, the method comprising the steps of: kneading a forming raw material containing a cordierite forming material and then forming it to produce a honeycomb formed body; and firing the honeycomb formed body to provide a honeycomb structure. In the producing method, from 0.1 to 6.0 parts by mass of a magnesium silicate mineral having a 2:1 ribbon type structure per 100 parts by mass of the cordierite forming material is added to the forming raw material.

Aluminum titanate-containing particles made up of a conglomerate of multiple partial grains. The aluminum titanate-containing particles are formed by breaking apart ceramic bodies along cracks, which are formed predominantly through the grains, rather than between the grains. Batch mixtures forming the aluminum titanate-containing particles, as well as batch mixtures utilizing the aluminum titanate particles are disclosed. Green bodies, such as green honeycomb bodies having peak intensity ratios (PIRs) in an axial direction of less than or equal to 0.50, ceramic honeycomb bodies, methods of manufacturing green honeycomb bodies, and ceramic honeycomb bodies are provided, as are other aspects.

A SiC powder containing 70% by mass or more of a β-SiC, wherein in a volume-based cumulative particle size distribution measured by a laser diffraction method, a D50 is 8 to 35 μm and a D10 is 5 μm or more.

A dielectric composition includes a dielectric grain including a perovskite compound and a first segregation phase including at least Ca, Al, Si, and O.

The present invention relates to a sintering agent for dry particulate refractory compositions and dry particulate refractory compositions. The use of dry particulate refractory compositions also form part of the present invention.

The invention discloses a sound-absorbing material particle and a preparation method thereof. The method for preparing the sound-absorbing material particle comprises: mixing a sound-absorbing raw material with a solvent to form a sound-absorbing slurry; filling the sound-absorbing slurry into a mechanical compression die, and performing compression molding on the sound-absorbing slurry to form a particle; performing a hydrothermal crystallization reaction on the particle to crystallize the sound-absorbing raw material in the particle; and drying the particle to produce the sound-absorbing material particle.