A heat dissipation member includes a thermal radiation ceramic material, and the thermal radiation ceramic material contains silicon nitride and boron nitride as main components. The ratio of the mass of boron nitride to the mass of silicon nitride and boron nitride is 10 mass % to 40 mass %.

The present invention is directed to a method for producing a silicon nitride sintered material, the method including heating a molded article, which contains a silicon nitride powder having a β phase ratio of 80% or more, a dissolved oxygen content of 0.2% by mass or less, and a specific surface area of 5 to 20 m.sup.2/g, and a sintering auxiliary containing a compound having no oxygen bond, and which has an overall oxygen content controlled to be 1 to 15% by mass and an aluminum element overall content controlled to be 800 ppm or less, to a temperature of 1,200 to 1,800° C. in an inert gas atmosphere under a pressure of 0 MPa.Math.G or more and less than 0.1 MPa.Math.G to sinter the silicon nitride.

In the present invention, there can be provided a method for producing a silicon nitride sintered material, which method is advantageous in that a silicon nitride sintered material having high thermal conductivity can be obtained even when using a silicon nitride powder having a high β phase ratio and conducting calcination under normal pressure or substantially normal pressure.

A method for manufacturing a C/C part includes fabricating an oxidized PAN fiber preform comprising a stack of sheets of multi-axial, non-crimp, OPF fabric. The method includes positioning the oxidized PAN fiber preform with a female forming tool, the female forming tool comprising a die recess, and forming the oxidized PAN fiber preform into a shaped body. The shaped body is removed from the female forming tool and moved into a graphite fixture for carbonization. The carbonized shaped body may also be densified into the final C/C part. The carbonized shaped body can also be placed in a perforated graphite fixture for densification and removed from the perforated graphite fixture between densification processes for machining and for facilitating further densification.

A method of forming a ceramic matrix composite component includes forming a fiber preform, the fiber preform including a plurality of ceramic fiber plies, a non-reduced fiber region having an areal weight, and a reduced fiber region characterized by a reduced areal weight less than the areal weight of the non-reduced fiber region by at least 5 percent. The method further includes selectively applying ceramic particles to the reduced fiber region in such manner as to avoid applying the ceramic particles to the non-reduced fiber region, and subsequently densifying the preform.

A coating composition is described, for use in the foundry, in particular comprising particulate, amorphous silicon dioxide (SiO.sub.2) and an aqueous phase having a pH of at most 5, and also coated, waterglass-bound foundry molding elements, especially coated, waterglass-bound foundry molds and foundry cores, which each comprise a coating composition of the invention. Further described is the use of a coating composition of the invention for producing a coating on a waterglass-bound foundry molding element and a method for producing a waterglass-bound foundry molding element (mold or core) coated with a water-containing refractory coating. Likewise specified is a kit whose contents include a coating composition of the invention.

The present invention discloses a guide pin, which comprises a base support layer (1) and a protective layer (2). The base support layer (1) is a rod-shaped structure. The protective layer (2) tightly wraps the surface of the base support layer (1). A manufacturing method for the guide pin made of various materials is also disclosed. The guide pin manufactured by the method of the present invention is not prone to bending or deformation and has good corrosion resistance and acid/alkaline resistance properties; it is wear resistant and has of extended service life; it is easy to be processed and is low in cost.

The present disclosure relates to the technical field of ceramic powder preparation, and discloses a zirconia/titania/cerium oxide doped rare earth tantalum/niobate RETa/NbO.sub.4 ceramic powder and a preparation method thereof. A general chemical formula of the ceramic powder is RE.sub.1-x(Ta/Nb).sub.1-x(Zr/Ce/Ti).sub.2xO.sub.4, 0<x<1, the crystal structure of the ceramic powder is orthorhombic, the lattice space group of the ceramic powder is C222.sub.1, the particle size of the ceramic powder ranges from 10 to 70 μm, and particles of the ceramic powder are spherical. During preparation, the raw materials are ball-milled before a high temperature solid phase reaction, then mixed with a solvent and an organic binder to obtain a slurry C, then centrifuged and atomized to obtain dry pellets, and finally sintered to obtain a zirconia/titanium oxide/cerium oxide doped rare earth tantalum/niobate RETa/NbO.sub.4 ceramic powder, which satisfies the requirements of APS technology for ceramic powders.

A zirconia ceramic includes the following elements: 60.5-70.5 wt % of Zr, 2.5-5.45 wt % of Y, 0.05-2.65 wt % of Al, 0.015-1.07 wt % of Si, and 0.34-2.8 wt % of M. M includes at least one of Nb or Ta. The zirconia ceramic has a phase composition which includes tetragonal zirconia, alumina and zirconium silicate. The total content of alumina and zirconium silicate is 0.2-12 wt %, and the content of the tetragonal zirconia is 84-99.3 wt %. The tetragonal zirconia includes a solid solution of zirconia formed with yttrium oxide and M.sub.xO.sub.y, x satisfies 1≤x≤3, and y satisfies 3≤y≤6.

A method includes molding a raw material powder containing a ceramic powder and a thermoplastic resin having a glass transition temperature higher than room temperature into a shape by isostatic pressing and in which a raw material powder slurry is prepared by adding the ceramic powder and the thermoplastic resin to a solvent so that the thermoplastic resin is 2% by weight or more and 40% by weight or less with respect to a total weight of the ceramic powder and the thermoplastic resin, a cast-molded body is to formed by wet-casting the raw material powder slurry into a shape, dried, and subjected to first-stage isostatic press molding at a temperature lower than the glass transition temperature of the thermoplastic resin, then this first-stage press-molded body is heated to the glass transition temperature of the thermoplastic resin or above, and warm isostatic press (WIP) molding is performed.

Disclosed herein is a ceramic particle comprising a core substrate chosen from yttria-stabilized zirconia, partially stabilized zirconia, zirconium oxide, aluminum nitride, silicon nitride, silicon carbide, and cerium oxide, and a conformal coating of a sintering aid film having a thickness of less than three nanometers and covering the core substrate, and methods for producing the ceramic particle.