A homopolypropylene has i) a molecular weight distribution of less than 2.4; ii) a melt index (measured at 230 C. under a load of 2.16 kg in accordance with ASTM D1238) of 5 to 3000 g/10 min; iii) a remaining stress ratio of 0.5% or less; and iv) a complex viscosity of 5 to 600 Pa.Math.s at an angular frequency of 1 rad/s and a complex viscosity of 5 to 300 Pa.Math.s at an angular frequency of 100 rad/s. A method for preparing the homopolyproylene is also provided. A molded article and a non-woven fabric are also provided.

Processes are provided which include copolymerization using two different metallocene catalysts, one capable of producing high Mooney-viscosity polymers and one suitable for producing lower Mooney-viscosity polymers having at least a portion of vinyl terminations. The two catalysts may be used together in polymerization to produce copolymer compositions of particularly well-tuned properties. For instance, polymerizations are contemplated to produce high-Mooney metallocene polymers that exhibit excellent processability and elasticity, notwithstanding their high Mooney viscosity. Other polymerizations are also contemplated in which lower-Mooney metallocene polymers are produced, which also exhibit excellent processability and elasticity, while furthermore having excellent cure properties suitable in curable elastomer compound applications. Many of the contemplated polymerizations include controlling the ratio of the two metallocene catalysts used in the polymerization so as to obtain the desired Mooney viscosity and desired rheology (indicated by Mooney Relaxation Area) of the copolymer compositions.

The invention relates to a process for the polymerization of olefins comprising the comprising the steps of a. Polymerizing olefins in a reaction mixture comprising monomers, diluent, processing aids to prepare a product stream comprising polyolefins, monomers and diluent; b. Removing the polyolefins from the product stream to obtain a purge stream; c. Removing gaseous components from the purge stream to obtain a liquid fraction; d. Treating the liquid fraction with at least one ionic liquid to obtain a fraction containing unsaturated hydrocarbons; e. Recycling the fraction containing unsaturated hydrocarbons to the reaction mixture, optionally after purification of said fraction containing unsaturated hydrocarbons. The invention also relates to an olefin polymerization system comprising a polymerization reactor, a purge vessel, a vent gas recovery and an ionic liquid separator for separating liquid alkenes from liquid alkanes, wherein the liquid alkenes which are separated from the alkanes in the ionic liquid separator can be recycled to the polymerization reactor.

Fluorided silica-coated alumina activator-supports have a bulk density from 0.15 to 0.37 g/mL, a total pore volume from 0.85 to 2 mL/g, a BET surface area from 200 to 500 m.sup.2/g, an average pore diameter from 10 to 25 nm, and from 80 to 99% of pore volume in pores with diameters of greater than 6 nm. Methods of making the fluorided silica-coated alumina activator-supports and using the fluorided silica-coated aluminas in catalyst compositions and olefin polymerization processes also are described. Representative ethylene-based polymers produced using the compositions and processes have a melt index of 0.1 to 10 g/10 min and a density of 0.91 to 0.96 g/cm.sup.3, and contain from 70 to 270 ppm solid oxide and from 2 to 18 ppm fluorine.

The present disclosure relates to a novel metallocene compound. The metallocene compound according to the present disclosure may be used for the preparation of an olefin-based polymer, may have excellent ability, and may produce an olefin-based polymer having a relatively high molecular weight compared with the case of using a catalyst composition having a similar structure due to the structural and electrical steric hindrance effect.

Fluorided silica-coated alumina activator-supports have a bulk density from 0.15 to 0.37 g/mL, a total pore volume from 0.85 to 2 mL/g, a BET surface area from 200 to 500 m.sup.2/g, an average pore diameter from 10 to 25 nm, and from 80 to 99% of pore volume in pores with diameters of greater than 6 nm. Methods of making the fluorided silica-coated alumina activator-supports and using the fluorided silica-coated aluminas in catalyst compositions and olefin polymerization processes also are described. Representative ethylene-based polymers produced using the compositions and processes have a melt index of 0.1 to 10 g/10 min and a density of 0.91 to 0.96 g/cm.sup.3, and contain from 70 to 270 ppm solid oxide and from 2 to 18 ppm fluorine.

Fluorided silica-coated alumina activator-supports have a bulk density from 0.15 to 0.37 g/mL, a total pore volume from 0.85 to 2 mL/g, a BET surface area from 200 to 500 m.sup.2/g, an average pore diameter from 10 to 25 nm, and from 80 to 99% of pore volume in pores with diameters of greater than 6 nm. Methods of making the fluorided silica-coated alumina activator-supports and using the fluorided silica-coated aluminas in catalyst compositions and olefin polymerization processes also are described. Representative ethylene-based polymers produced using the compositions and processes have a melt index of 0.1 to 10 g/10 min and a density of 0.91 to 0.96 g/cm.sup.3, and contain from 70 to 270 ppm solid oxide and from 2 to 18 ppm fluorine.

Fluorided silica-coated alumina activator-supports have a bulk density from 0.15 to 0.37 g/mL, a total pore volume from 0.85 to 2 mL/g, a BET surface area from 200 to 500 m.sup.2/g, an average pore diameter from 10 to 25 nm, and from 80 to 99% of pore volume in pores with diameters of greater than 6 nm. Methods of making the fluorided silica-coated alumina activator-supports and using the fluorided silica-coated aluminas in catalyst compositions and olefin polymerization processes also are described. Representative ethylene-based polymers produced using the compositions and processes have a melt index of 0.1 to 10 g/10 min and a density of 0.91 to 0.96 g/cm.sup.3, and contain from 70 to 270 ppm solid oxide and from 2 to 18 ppm fluorine.

Fluorided silica-coated alumina activator-supports have a bulk density from 0.15 to 0.37 g/mL, a total pore volume from 0.85 to 2 mL/g, a BET surface area from 200 to 500 m.sup.2/g, an average pore diameter from 10 to 25 nm, and from 80 to 99% of pore volume in pores with diameters of greater than 6 nm. Methods of making the fluorided silica-coated alumina activator-supports and using the fluorided silica-coated aluminas in catalyst compositions and olefin polymerization processes also are described. Representative ethylene-based polymers produced using the compositions and processes have a melt index of 0.1 to 10 g/10 min and a density of 0.91 to 0.96 g/cm.sup.3, and contain from 70 to 270 ppm solid oxide and from 2 to 18 ppm fluorine.