This disclosure relates to a continuous solution polymerization process wherein production rate is increased. Process solvent, ethylene, optional comonomers, optional hydrogen and a single site catalyst formulation are injected into a first reactor forming a first ethylene interpolymer. Process solvent, ethylene, optional comonomers, optional hydrogen and a heterogeneous catalyst formulation are injected into a second reactor forming a second ethylene interpolymer. The first and second reactors may be configured in series or parallel modes of operation. Optionally, a third ethylene interpolymer is formed in an optional third reactor, wherein an optional heterogeneous catalyst formulation may be employed. In a solution phase, the first, second and optional third ethylene interpolymers are combined, the catalyst is deactivated, the solution is passivated and following a phase separation process an ethylene interpolymer product is recovered.

This disclosure relates to a continuous solution polymerization process wherein production rate is increased. Process solvent, ethylene, optional comonomers, optional hydrogen and a single site catalyst formulation are injected into a first reactor forming a first ethylene interpolymer. Process solvent, ethylene, optional comonomers, optional hydrogen and a heterogeneous catalyst formulation are injected into a second reactor forming a second ethylene interpolymer. The first and second reactors may be configured in series or parallel modes of operation. Optionally, a third ethylene interpolymer is formed in an optional third reactor, wherein an optional heterogeneous catalyst formulation may be employed. In a solution phase, the first, second and optional third ethylene interpolymers are combined, the catalyst is deactivated, the solution is passivated and following a phase separation process an ethylene interpolymer product is recovered.

This disclosure relates to a continuous solution polymerization process wherein production rate is increased. Process solvent, ethylene, optional comonomers, optional hydrogen and a single site catalyst formulation are injected into a first reactor forming a first ethylene interpolymer. Process solvent, ethylene, optional comonomers, optional hydrogen and a heterogeneous catalyst formulation are injected into a second reactor forming a second ethylene interpolymer. The first and second reactors may be configured in series or parallel modes of operation. A third ethylene interpolymer is formed in a third reactor, wherein an optional heterogeneous catalyst formulation may be employed. In a solution phase, the first, second and optional third ethylene interpolymers are combined, the catalyst is deactivated, the solution is passivated and following a phase separation process an ethylene interpolymer product is recovered.

This disclosure relates to a continuous solution polymerization process wherein production rate is increased. Process solvent, ethylene, optional comonomers, optional hydrogen and a single site catalyst formulation are injected into a first reactor forming a first ethylene interpolymer. Process solvent, ethylene, optional comonomers, optional hydrogen and a heterogeneous catalyst formulation are injected into a second reactor forming a second ethylene interpolymer. The first and second reactors may be configured in series or parallel modes of operation. A third ethylene interpolymer is formed in a third reactor, wherein an optional heterogeneous catalyst formulation may be employed. In a solution phase, the first, second and optional third ethylene interpolymers are combined, the catalyst is deactivated, the solution is passivated and following a phase separation process an ethylene interpolymer product is recovered.

This disclosure relates to ethylene interpolymer compositions. Specifically, ethylene interpolymer products having: a Dilution Index (Y.sub.d) greater than 0; total catalytic metal 3.0 ppm; 0.03 terminal vinyl unsaturations per 100 carbon atoms, and; optionally a Dimensionless Modulus (X.sub.d) greater than 0. The disclosed ethylene interpolymer products have a melt index from about 0.3 to about 500 dg/minute, a density from about 0.869 to about 0.975 g/cm.sup.3, a polydispersity (M.sub.w/M.sub.n) from about 2 to about 25 and a CDBI.sub.50 from about 20% to about 97%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.

This disclosure relates to ethylene interpolymer compositions. Specifically, ethylene interpolymer products having: a Dilution Index (Y.sub.d) greater than 0; total catalytic metal 3.0 ppm; 0.03 terminal vinyl unsaturations per 100 carbon atoms, and; optionally a Dimensionless Modulus (X.sub.d) greater than 0. The disclosed ethylene interpolymer products have a melt index from about 0.3 to about 500 dg/minute, a density from about 0.869 to about 0.975 g/cm.sup.3, a polydispersity (M.sub.w/M.sub.n) from about 2 to about 25 and a CDBI.sub.50 from about 20% to about 97%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.

This disclosure relates to ethylene interpolymer compositions. Specifically, ethylene interpolymer products having: a Dilution Index (Y.sub.d) greater than 0; total catalytic metal ?3.0 ppm; ?0.03 terminal vinyl unsaturations per 100 carbon atoms, and; optionally a Dimensionless Modulus (X.sub.d) greater than 0. The disclosed ethylene interpolymer products have a melt index from about 0.3 to about 500 dg/minute, a density from about 0.869 to about 0.975 g/cm.sup.3, a polydispersity (M.sub.w/M.sub.n) from about 2 to about 25 and a CDBI.sub.50 from about 20% to about 97%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.

This disclosure relates to ethylene interpolymer compositions. Specifically, ethylene interpolymer products having: a Dilution Index (Y.sub.d) greater than 0; total catalytic metal ?3.0 ppm; ?0.03 terminal vinyl unsaturations per 100 carbon atoms, and; optionally a Dimensionless Modulus (X.sub.d) greater than 0. The disclosed ethylene interpolymer products have a melt index from about 0.3 to about 500 dg/minute, a density from about 0.869 to about 0.975 g/cm.sup.3, a polydispersity (M.sub.w/M.sub.n) from about 2 to about 25 and a CDBI.sub.50 from about 20% to about 97%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.

This disclosure relates to ethylene interpolymer compositions. Specifically, ethylene interpolymer products having: a Dilution Index (Y.sub.d) greater than 0; total catalytic metal 3.0 ppm; 0.03 terminal vinyl unsaturations per 100 carbon atoms, and; optionally a Dimensionless Modulus (X.sub.d) greater than 0. The disclosed ethylene interpolymer products have a melt index from about 0.3 to about 500 dg/minute, a density from about 0.869 to about 0.975 g/cm.sup.3, a polydispersity (M.sub.w/M.sub.n) from about 2 to about 25 and a CDBI.sub.50 from about 20% to about 97%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.

This disclosure relates to ethylene interpolymer compositions. Specifically, ethylene interpolymer products having: a Dilution Index (Y.sub.d) greater than 0; total catalytic metal 3.0 ppm; 0.03 terminal vinyl unsaturations per 100 carbon atoms, and; optionally a Dimensionless Modulus (X.sub.d) greater than 0. The disclosed ethylene interpolymer products have a melt index from about 0.3 to about 500 dg/minute, a density from about 0.869 to about 0.975 g/cm.sup.3, a polydispersity (M.sub.w/M.sub.n) from about 2 to about 25 and a CDBI.sub.50 from about 20% to about 97%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.