Disclosed is a grain-finished artificial leather including an artificial leather base material, and a grain layer stacked on the artificial leather base material. The artificial leather base material includes a fiber-entangled body including ultrafine fibers having an average fineness of 0.4 dtex or less, an elastic polymer, and fine particles having an average particle size of 10 μm or less. The content ratio of the fine particles is 10 to 40 mass %, and the ratio of the elastic polymer to the total amount of the elastic polymer and the fine particles is 20 to 80 mass %. Also, a total of an apparent density of the elastic polymer and an apparent density of the fine particles is 0.23 to 0.55 g/cm.sup.3.

The present invention relates to a modified polyvinyl butyral material, comprising a polyvinyl butyral composite material, a filler, an anti-hydrolysis agent, a first plasticizer, zinc stearate, calcium stearate, and a polymeric dispersant; wherein the polyvinyl butyral composite material is obtained by plasticizing a composition comprising polyvinyl butyral and a second plasticizer. The present invention also relates to a preparation method of the modified polyvinyl butyral material, a modified polyvinyl butyral product comprising at least one modified polyvinyl butyral layer prepared from a material comprising the modified polyvinyl butyral material, and the preparation method of the modified polyvinyl butyral product.

A textile fabric having improved properties, variously including surface stability, abrasion resistance, resistance to edge fraying, moisture control, and resistance to fluid penetration is created by introducing a polymeric solution or a plurality of low-melting particles suspended in a liquid into the textile fabric while leaving a plurality of surface fibers exposed and maintaining a textile feel on the surface.

A textile fabric having improved properties, variously including surface stability, abrasion resistance, resistance to edge fraying, moisture control, and resistance to fluid penetration is created by introducing a polymeric solution or a plurality of low-melting particles suspended in a liquid into the textile fabric while leaving a plurality of surface fibers exposed and maintaining a textile feel on the surface.

Disclosed is a fabric having a first side and a second side, that is provided at least on part of the first side with a pattern of protrusions, wherein the protrusions comprise an expanded heat-expanding material, namely a heat-expanding material that has been expanded by heating. A polymeric layer is provided to the woven fabric to coat at least part of the protrusions. Also disclosed is a process for the production of the fabric and a garment comprising the fabric.

An aqueous emulsion comprising an aqueous continuous phase and a discontinuous oil phase comprising particles having an interpenetrating network (IPN) comprising: i) an MQ resin, ii) a polyorganosiloxane and iii) an organic polymer.

An article comprising a polymeric foam, wherein the polymeric foam contains a continuous polymer matrix defining cells therein, the polymer matrix containing: (a) from 25 to 65 weight percent of one or more olefin block copolymer having a melt index of two grams per ten minutes or more, (b) from 65 to 25 weight percent of one or more chlorinated olefin polymer having a Mooney viscosity less than 60 (ML 1+4, 125° C.), and (c) from 5 to 30 weight parts of antimony trioxide relative to 100 weight parts of polymers in the polymeric foam, with weight percent values relative to total polymer weight in the polymeric foam; a process for preparing the article.

A radiative cooling fabric comprises a flexible substrate layer and a functional layer stacked in order. The first functional layer comprises a first functional resin and a first functional filler dispersed in the first functional resin. A mass fraction of the first functional filler in the first functional layer is in a range of 1% to 20%. An emissivity of the radiative cooling fabrics in the wavelength of 7 μm to 14 μm is not less than 80%. A reflectivity of the radiative cooling fabrics in the wavelength of 300 nm to 2500 nm is not less than 80%. An average value of warp recovery angles of the radiative cooling fabrics is greater than or equal to 95°, and an average value of the weft recovery angles of the radiative cooling fabrics is greater than or equal to 91°.

An interior material of a vehicle includes: a fabric layer made of a tricoat fabric, a foam layer disposed on a lower surface of the fabric layer, and an antifouling layer disposed at least between an upper surface of the fabric layer or the fabric layer and the foam layer. The tricoat fabric includes a combination of at least one of a polyurethane yarn, a high-elongation polyester yarn, or a polyester yarn.

A fabric comprising a cut-resistant polymeric coating including by weight 1 to 10 percent para-aramid particles, the particles having an average particle size of 20 to 500 microns.