The disclosure provides a fabric structure, which includes a base fabric and a coating layer. The base fabric is woven from multiple yarns. Each of the yarns is composed of a fiber. The coating layer is disposed on the base fabric. The fiber and the coating layer do not include polyvinyl chloride. A manufacturing method of the fabric structure is also provided.

A floor protector has a pair of non-woven material layers. A film layer is bonded between the pair of non-woven material layers. The film layer provides a moisture barrier. A non-skid layer is applied on one of the non-woven material layers.

The present invention pertains to a method for manufacturing a laminated textile product comprising providing a first intermediate product comprising a primary backing having a front surface and a back surface, and yarns stitched into the primary backing, the yarns extending from the front surface of the backing material, feeding the intermediate product along a body having a heated surface, the back surface being pressed against the said heated surface, to at least partly melt the yarns present in the intermediate product to bond the yarns to the backing, wherein the part of the back surface that is pressed against the heated surface has a relative speed with respect to the heated surface, so as to provide a second intermediate product having a calendered back surface, providing a dimensionally stable carrier sheet or secondary backing, and connecting the second intermediate product to the carrier sheet by providing a hot melt adhesive between the calendered surface and the sheet, and pressing the sheet to the second intermediate product to form the textile product.

A microporous laminate comprising a microporous polymeric surface coating comprising polypropylene copolymer on a nonwoven substrate, the microporous polymeric surface coating having a matrix phase of polypropylene homopolymer chain segments and a plurality of domains of ethylene-containing copolymer chain segments within said matrix phase, the domains of the ethylene-containing copolymer chain segments further comprising an inclusion phase of said polypropylene homopolymer chain segments, wherein the domains of said ethylene-containing copolymer chain segments are fractured to form micropores in the microporous polymeric surface coating, wherein (a) the microporous polymeric surface coating has an average thickness of 0.4 to 3.9 mils (10 to 100 micrometers) and the microporous laminate has a trapezoid tear of 40 to 225 Newtons (9 to 50 lbs-force); or (b) the microporous polymeric surface coating has an average thickness of 0.5 to 3.0 mils (12.7 to 76.2 micrometers) and the microporous laminate has a Gurley air permeability of 20 to 150 seconds/100 cm.sup.3 of air.