Vapor-permeable, substantially water-impermeable, corrosion-inhibiting composites are disclosed herein. For instance, disclosed herein are composites comprising a first layer comprising a first nonwoven; and a second layer adjacent to and mechanically integrated with the first layer, the second layer comprising a polymer having a melt flow index of about 10 g/10 mins to about 200 g/10 mins, and a corrosion inhibitor, wherein the composite has a moisture vapor transmission rate of from about 25 g/m.sup.2/day to about 1000 g/m.sup.2/day when measured at about 23° C. and about 50% relative humidity. Also disclosed herein are methods of making and using the same.

A non-penetrating multi-layer continuous hose and a preparation method thereof are provided. The hose includes an outer coating, a reinforcement layer, and an inner coating. The inner coating and the outer coating can have one or more layers with different materials and have an adjustable thickness. The hose is prepared by simultaneously performing extrusion coating inside and outside the reinforcement layer rather than penetrating the fiber reinforcement layer. The hose exhibits improved layer-to-layer adhesion and has high strength, and continuous production can be achieved to meet the length requirement in various kinds of construction, which has high applicability.

The present disclosure relates generally to flame retarding building materials and methods for making them. More particularly, the present disclosure relates to flame retarding building materials that have both flame retardant character and desirable water vapor permeability values. In one embodiment, the disclosure provides a flame retardant vapor retarding membranes comprising: a building material substrate sheet having a melt viscosity of about 1 Pa.Math.s to about 100,000 Pa.Math.s at about 300° C. at 1 rad/s; and a polymeric coating layer disposed on the building material substrate layer, wherein the coating layer has a melt viscosity of about 1 Pa.Math.s to about 100,000 Pa.Math.s at about 300° C. at 1 rad/s.

The present invention relates to a composite comprising a nonwoven fabric being the substrate of the composite, wherein the nonwoven fabric comprises a polymer (A) selected from the group consisting of polyethylene, polypropylene, polyethylene terephthalate and polyamide; and a coating layer, wherein the coating layer comprises a polymer (B), wherein said polymer is an ethylene copolymer, preferably a polar ethylene copolymer; whereby the coating layer overlays at least one surface of the nonwoven fabric; and whereby the composite has a water vapor transmission rate (WTVR) according to ASTM E-96 ((water cup method) at 38° C. at 50% RH at the outside of the sample and 100% RH at the inside of the samples) of more than 50 g/[m.sup.2/24 h], preferably of more than 100 g/[m.sup.2/24 h].

A method for forming an antimicrobial coating on a substrate is provided. The method comprises dissipating and entrapping (embedding) sulfonated copolymer particles in void spaces or interstices of fibers of a fabric forming an outer layer of a substrate. The sulfonated copolymer is selected from the group of perfluorosulfonic acid polymers such as sulfonated tetrafluoroethylene, polystyrene sulfonates, sulfonated block copolymers, polysulfones such as polyether sulfone, polyketones such as polyether ketone, sulfonated poly(arylene ether), and mixtures thereof. The fibers comprise a thermoplastic polymer having a melting point of less than 120° C., or 45-110° C., or 45-80° C. The sulfonated copolymer forms an antimicrobial coating layer for killing at least 90% microbes in the air within 30 minutes of contact with the coating.

The invention provides a flame retardant material comprising a substrate, an optionally corona-treated coating on the substrate, the coating comprising a polyolefin composition comprising a) an ethylene based plastomer with a density in the range of 0.857 to 0.915 g/cm.sup.3 and an MFR.sub.2 in the range 0.5-30 g/10 min; b) a propylene based plastomer with a density in the range of 0.860 to 0.910 g/cm.sup.3 and an MFR.sub.2 in the range 0.01-30 g/10 min; and c) a flame retardant, a primer layer on top of the coating and a lacquer topcoat.

The present invention relates to a layered material and a method of producing the same.

The layered material has one or more layers, including at least one foamed layer, said foamed layer comprising a first polymer and a second polymer, said foamed layer having a high BBC.

A method for forming an antislip material. A flexible thermoplastic carrier is provided. A hot release surface is provided. Provided is a first layer of discrete thermoplastic particles, sitting on the hot release surface. The discrete particles are above their softening temperatures, providing in the first layer a tackiness. The method includes contacting the carrier with the tacky first layer for sticking the first layer to the carrier, and thereafter removing the carrier, and therewith the tacky first layer stuck to the carrier, from the release surface. Thereby the carrier is provided with a hot, preferably discontinuous and/or elastomeric antislip coating. With a heat energy of the hot coating a bond is formed between the carrier and the coating. The removing of the carrier includes pulling the carrier out of the contact with a pulling-out force. The temperature of the hot release surface is above the melting temperature of the carrier. The carrier would be spoiled, if heated completely to the temperature of the release surface and simultaneously pulled with the pulling-out force. Therefore the contacting time is kept shorter than a minimum time required by a heat of the hot release surface for spoiling the carrier. Flat-topped roughening projections can be included in the antislip coating.

A coating composition which comprises a dispersion which is a melt blended product of one or more base polymers; one or more dispersants; one or more compatibilizers; water; and optionally base; wherein the dispersion exhibits an average volume mean particle size diameter of less than or equal to 2 microns, a solids content of from 50 to 70 wt %, and a pH of 8 or greater; one or more rheology modifiers; and optionally one or more neutralizing agents is provided. An article coated with the coating composition and a method of making the coated article are also provided.

A variety of plates for footwear are provided including a polyolefin resin. Sole structures and articles of footwear formed therefrom are also provided. Methods of making the polyolefin resin compositions, plates, sole structures, and articles of footwear are also provided. In some aspects, the polyolefin resin composition includes an effective amount of a polymeric resin modifier. The effective amount can be an amount effective to allow the resin composition to pass a flex test, and in particular to pass a flex test without significant change in abrasion loss. In some aspects, the resin composition also includes a clarifying agent to improve optical clarity of the plate. In some aspects, the plates include a textile disposed on one or both of a first side and the second side of the plate. The textile can provide for improved bonding of the plate to other components such as a chassis or an upper.