An apparatus and method for transferring nanofiber structures (e.g., nanofiber films, nanofiber sheets, stacks of nanofiber grids, nanofiber films, nanofiber sheets, and combinations thereof) between various substrates are described. The techniques described use a soluble layer on a substrate that is subsequently dissolved, thus freeing the nanofiber structure from the substrate. This liquid phase techniques preserves the mechanical integrity and the purity of the nanofiber structures.

A nanofiber yarn placement system includes a yarn dispenser assembly, and a placement assembly. The placement assembly includes a compliant flange, and a guide connected to the compliant flange. The guide defining a channel. The channel includes at least one internal surface and at least one corner defined by the at least one internal surface.

A carbon nanotube-resin composite includes: a carbon nanotube assembled wire including a plurality of carbon nanotubes; and a resin, wherein in the carbon nanotube assembled wire, the carbon nanotubes are oriented at a degree of orientation of 0.9 or more and 1 or less.

A carbon nanotube-resin composite includes: a carbon nanotube assembled wire including a plurality of carbon nanotubes; and a resin, wherein in the carbon nanotube assembled wire, the carbon nanotubes are oriented at a degree of orientation of 0.9 or more and 1 or less.

Provided is a method of producing a catalyst-bearing support that produces a catalyst-bearing support used in production of a fibrous carbon nanostructure. The production method includes: a stirring step of rotating an approximately circular tube-shaped rotary drum around a central axis so as to stir a particulate support; a spraying step of spraying a catalyst solution against the particulate support inside of the rotary drum; and a drying step causing a drying gas to flow to inside of the rotary drum from outside of the rotary drum so as to dry catalyst solution attached to the particulate support. In this production method, at least part of an implementation period of the stirring step and at least part of an implementation period of the spraying step overlap with each other.

A carbon nanotube assembled wire includes a plurality of carbon nanotubes, wherein in a Raman spectrum of the carbon nanotube assembled wire, a ratio IB/IA of an integrated intensity IA in a range of a Raman shift of 120 cm.sup.−1 or more and 210 cm.sup.−1 or less and an integrated intensity IB in a range of a Raman shift of more than 210 cm.sup.−1 and 280 cm.sup.−1 or less is 0.1 or more.

Systems comprising a carbon fiber reactor for fabricating carbon fiber, the reactor comprising a receptacle for containing a carbon-metal melt, and a plurality of nozzles through which a plurality of menisci are formed by the carbon-metal melt for contact with a carbon seed to fabricate the carbon fiber; and a heater for heating the carbon-metal melt.

The purpose of the present disclosure is to provide a CNT fiber that is constituted of aligned carbon nanotubes (CNTs), is thin, has little irregularity in thickness, has excellent winding properties when undergoing coiling processing, and has superior conductivity. Provided is a CNT fiber constituted of carbon nanotubes (CNTs) having a thickness of 0.01 μm-3 mm, having a coefficient of variation for irregularity in thickness of 0.2 or less, having a distribution rate a for deviation from roundness of 40% or greater, and a distribution rate b of 70% or greater. Also provided is a method for manufacturing the CNT fiber.

By using CNF excellent in dispersibility, conductivity, and crystallinity, a conductive polymer material having high conductivity even with a low CNF content and a shaped article thereof and a conductive polymer material with a less CNF content for same conductivity and a shaped article thereof are provided. A conductive polymer material with high conductivity is produced by using carbon nanofiber with a median diameter D50 value from 0.1 to 8 μm, powder resistivity of 0.03 Ωcm or less measured under a load of 9.8 MPa, and D/G from 0.5 to 1.3.

By using CNF excellent in dispersibility, conductivity, and crystallinity, a conductive polymer material having high conductivity even with a low CNF content and a shaped article thereof and a conductive polymer material with a less CNF content for same conductivity and a shaped article thereof are provided. A conductive polymer material with high conductivity is produced by using carbon nanofiber with a median diameter D50 value from 0.1 to 8 μm, powder resistivity of 0.03 Ωcm or less measured under a load of 9.8 MPa, and D/G from 0.5 to 1.3.