A sliding member of the present invention includes a coating on a base material. The coating contains hard metal particles and corrosion-resistant metal particles that have hardness lower than that of the hard metal particles. The hard metal particles contain particles that have at least Vickers hardness of 600 Hv or higher. The corrosion-resistant metal particles are made of at least one kind of metal selected from the group consisting of copper (Cu), cobalt (Co), chromium (Cr), and nickel (Ni), or are made of an alloy containing said metal. The coating has a cross section in which the hard metal particles are dispersed in an island manner in a particle aggregate of the corrosion-resistant metal particles and in which an area ratio of the corrosion-resistant metal particles is 30% or larger. Thus, corrosion of the hard metal particles in the coating is prevented, whereby the sliding member maintains wear resistance for a long time.

Proposed is a novel coupling mechanism capable of applying a preload to a ball portion and a socket portion which constitute a coupling mechanism of a titling pad bearing, without using a spring element.

The invention relates to a copper alloy having the following composition (in % by weight): from 10.6 to 18% of Al, from 10.5 to 14.5% of Ni, optionally up to 2% of Fe, optionally up to 1% of Co, optionally up to 0.5% of Ti, optionally up to 0.5% of Mn, optionally up to 0.15% of B, optionally up to 0.1% of Ca, optionally up to 0.1% of C,

a balance copper and unavoidable impurities. Nickel aluminides of the NiAl type are embedded as precipitates in the microstructure of the alloy. The invention further relates to a number of uses of this copper alloy.

A metal matrix self-lubricating composite and a manufacturing method therefor. The metal matrix self-lubricating composite comprises a metal matrix and a mixture layer compounded on a surface of the metal matrix, the mixed layer comprising a copper alloy and a self-lubricating material. The method for manufacturing the metal matrix self-lubricating composite comprises the following steps: a) sintering copper alloy powder on a surface of a metal matrix to form a copper alloy layer on the surface of the metal matrix; b) blade-coating or dip-coating a lubricating material on a surface of the copper alloy layer, and performing vacuumization to obtain a metal plate, and drying the metal plate; c) repeating step b) for multiple times; and d) sintering the metal plate obtained in step c) to obtain the metal matrix self-lubricating composite. In the present invention, a vacuumization mode is used and vacuumization operations are repeated, so that a dense mixture layer on which a self-lubricating material is dispersed on a copper alloy is formed, and the metal matrix self-lubricating composite has good lubricity and abrasion resistance.

A bearing material including a substrate, and a sliding layer overlying the substrate, where the sliding layer includes fillers including wollastonite in a wt % range between 10 and 30%, barium sulfate in a wt % range between 5 and 15%, and pigment in a wt % range between 0.1 and 5%.

Provided is a sintered bearing, including Al, Cu, and Ni, the sintered bearing having Al—Cu—Ni alloy structures (3) sintered together. The Al—Cu—Ni alloy structures (3) each have an Al—Cu—Ni matrix phase (α-phase) and an Al—Ni compound phase (κ-phase), and are free of an Al—Cu compound phase (γ-phase).

A plastic bearing material of a bearing may include a block copolymer. The block copolymer may include structural blocks of two or more different polymers. A first polymer may include at least one of polyamide-imide and polybenzimidazole. A second polymer may include at least one of polydimethylsiloxane, methyl vinyl ether and polyisobutene. A method for manufacturing a plastic bearing material may include synthesizing a structural block of a first polymer and a structural block of a second polymer to define a block copolymer via a condensation reaction.

Raw material powder containing metal powder as a main component is molded to form a metal powder molded body (3′), and the metal powder molded body (3′) is sintered to form a metal substrate (3). Further, a lubricating member (4) is made of an aggregate of graphite particles (13), and at least a part of a bearing surface (11) is formed of the fabricating member (4). The lubricating member (4) is fitted into the metal powder molded body (3′). After that, the metal powder molded body (3′) is sintered, and at this time, the lubricating member (4) is fixed onto the metal substrate (3) with a contraction force (F) generated in the metal powder molded body (3′).

The present application relates to a plain bearing, or a part thereof and to a method for producing same, characterised in that the plain bearing at least partially consists of a CuCrZr alloy. The application also relates to the use of the CuCrZr alloy as a plain bearing material.

Provided is a Cu-based sintered bearing comprising: 15-36 mass % of Ni; 3-13 mass % of Sn; 0.05-0.55 mass % of P; and 0.02-4 mass % of C in total, the balance consisting of Cu and inevitable impurities, wherein the content of C forming an alloy with a matrix within Cu—Ni-based main phase grains is 0.02-0.10 mass %.