Using the systems and methods discussed herein, CMAS corrosion is inhibited via CMAS interception in an engine environment and/or is prevented or reduced by the formation of a metal oxide protective coating on a hot engine section component. The CMAS interception can occur while the engine is in operation in flight or in a testing or quality control environment. The metal oxide protective coating can be applied over other coatings, including Gd-zirconates (GZO) or yttria-stabilized zirconia (YSZ). The metal oxide protective coating is applied at original equipment manufacturers (OEM) and can also be applied in-situ using a gas injection system during engine use in-flight or during maintenance or quality testing. The metal oxide protective coating contains a rare earth element, aluminum, zirconium, chromium, or combinations thereof.

Air compressor comprising a centrifugal-type compression wheel defining an axial direction and a radial direction, an air intake opening extending circumferentially around the compression wheel and opening onto a compression part, the compression part comprising a first portion forming a volute for the ejection of compressed air which is mounted facing the compression wheel in the radial direction, and an at least partly annular second portion extending around the first portion, the second portion comprising a central orifice receiving at least part of the compression wheel and an air deflection torus, the volute being made of metallic material and the torus made of thermoplastic material filled with non-metallic elements, the thermoplastic material having a thermal expansion corresponding to that of the metallic material.

The use of especially an aluminum alloy on a metal substrate in a PVD-AlTiN coating results in good corrosion and erosion protection.

Using the systems and methods discussed herein, CMAS corrosion is inhibited via CMAS interception in an engine environment and/or is prevented or reduced by the formation of a metal oxide protective coating on a hot engine section component. The CMAS interception can occur while the engine is in operation in flight or in a testing or quality control environment. The metal oxide protective coating can be applied over other coatings, including Gd-zirconates (GZO) or yttria-stabilized zirconia (YSZ). The metal oxide protective coating is applied at original equipment manufacturers (OEM) and can also be applied in-situ using a gas injection system during engine use in-flight or during maintenance or quality testing. The metal oxide protective coating contains a rare earth element, aluminum, zirconium, chromium, or combinations thereof and can have a thickness from 1 nm to 3,000 nm.

Using the systems and methods discussed herein, CMAS corrosion is inhibited via CMAS interception in an engine environment and/or is prevented or reduced by the formation of a metal oxide protective coating on a hot engine section component. The CMAS interception can occur while the engine is in operation in flight or in a testing or quality control environment. The metal oxide protective coating can be applied over other coatings, including Gd-zirconates (GZO) or yttria-stabilized zirconia (YSZ). The metal oxide protective coating is applied at original equipment manufacturers (OEM) and can also be applied in-situ using a gas injection system during engine use in-flight or during maintenance or quality testing. The metal oxide protective coating contains a rare earth element, aluminum, zirconium, chromium, or combinations thereof.

An airfoil for a gas turbine engine according to an example of the present disclosure includes, among other things, an airfoil section extending from a root section. The airfoil section includes a sheath that receives a core. The core includes first and second ligaments received in respective internal channels defined by the sheath, and each one of the first and second ligaments includes at least one interface portion in the root section dimensioned to receive a retention pin.

A repaired oxidation and corrosion resistant coating may comprise a repair material applied to a damaged portion of the oxidation and corrosion resistant coating. The repair material may be free of hexavalent chromium and may be compatible with a plurality of oxidation and corrosion resistant materials that comprise hexavalent chromium. The repair material may be burnished. The oxidation and corrosion resistant coating may comprise hexavalent chromium.

A containment assembly is provided for an aircraft engine having a rotor with a set of blades. The containment assembly comprises a containment casing annularly surrounding the rotor radially outward of the set of blades. The containment casing is made of a material having a density less than that of steel. A layer of thermal insulation is disposed radially inward of the containment casing. The layer of thermal insulation is radially disposed between the containment casing and the set of blades.

Thermal sprayed coating made from a thermal spray powder material containing aluminum containing particles mechanically alloyed to a transition metal. The coating includes aluminum alloy portions alloyed to the transition metal. The thermal spray powder is made of aluminum containing particles mechanically alloyed to a transition metal.

The invention relates to turbo molecular pumps enabling high pumping speed. The disclosure suggests using one or more cage-like rotor stages to optimize pumping speed on vacuum systems with low gas flows and low ultimate pressures. This allows for a smaller motor as well as smaller overall form factor and makes it well suited, in particular, for compact mass spectrometers and desk-top mass spectrometers.