Provided is a curable composition that has a sufficient pot life and does not cause a significant delay in curing time even after long-term storage at room temperature or higher. A separately packed curable composition includes: (A) a first pack containing: (a1) a polymerizable monomer having no acidic group, (b) a polymerizable monomer having an acidic group, and (c) a transition metal compound; and (B) a second pack containing: (a2) a polymerizable monomer having no acidic group, (d) an aromatic amine compound, and (e) at least one compound selected from sulfinic acid and a salt thereof.

Provided is a curable composition that has a sufficient pot life and does not cause a significant delay in curing time even after long-term storage at room temperature or higher. A separately packed curable composition includes: (A) a first pack containing: (a1) a polymerizable monomer having no acidic group, (b) a polymerizable monomer having an acidic group, and (c) a transition metal compound; and (B) a second pack containing: (a2) a polymerizable monomer having no acidic group, (d) an aromatic amine compound, and (e) at least one compound selected from sulfinic acid and a salt thereof.

The present invention provides a silicate glass that can reduce a color change in base material zirconia even when simultaneously fired with an unsintered zirconia. The present invention also provides a dental product using same. The present invention relates to a silicate glass comprising: 65.0 to 90.0 mol % SiO.sub.2, 4.0 to 15.0 mol % Al.sub.2O.sub.3, 1.0 to 10.0 mol % K.sub.2O, 0.1 to 7.0 mol % Na.sub.2O, and 0.01 to 15.0 mol % CaO, the silicate glass being essentially free of B.sub.2O.sub.3, and satisfying the relation {(number of moles of Al.sub.2O.sub.3)/(total number of moles of RO+R.sub.2O)}≥0.70, wherein R in the metal oxide represented by RO represents a metallic element in group 2 or 12 of the periodic table, and R in the metal oxide represented by R.sub.2O represents a metallic element in group 1 of the periodic table. The present invention also relates to a composite comprising the silicate glass and a base material formed of a ceramic; a sintered body as a fired product of the composite; and a dental product comprising the sintered body.

One aspect of the present invention relates to a dental fluoroaluminosilicate glass powder, a 50th percentile volume diameter of which is 5.0 pm or more and 9.0 pm or less, and a 10th percentile volume diameter of which is 2.4 pm or more.

One aspect of the present invention relates to a dental fluoroaluminosilicate glass powder, a 50th percentile volume diameter of which is 5.0 pm or more and 9.0 pm or less, and a 10th percentile volume diameter of which is 2.4 pm or more.

A curable mixture and method of using the mixture are disclosed. In some embodiments, the mixture comprises an alginate polymer, and comprises properties suitable for use as a tooth filling after curing.

A curable mixture and method of using the mixture are disclosed. In some embodiments, the mixture comprises an alginate polymer, and comprises properties suitable for use as a tooth filling after curing.

Provided is a dental bulk block for grinding processing. The dental bulk block includes a crystalloid, which includes lithium disilicate as a main crystal phase and silicate as a sub-crystal phase, and hyaline as a remainder. The dental bulk block is a functionally gradient material having a crystalline size gradient with respect to a depth thereof and having no interface at a change point of a crystalline size gradient value. The dental bulk block is useful for manufacturing an artificial dental prosthesis that is similar to natural teeth. Accordingly, the time and process for manufacturing the artificial dental prosthesis are shortened, and structural stability is increased in terms of dispersion of force due to gradient functionalization of mechanical properties.

Provided is a dental bulk block for grinding processing. The dental bulk block includes a crystalloid, which includes lithium disilicate as a main crystal phase and silicate as a sub-crystal phase, and hyaline as a remainder. The dental bulk block is a functionally gradient material having a crystalline size gradient with respect to a depth thereof and having no interface at a change point of a crystalline size gradient value. The dental bulk block is useful for manufacturing an artificial dental prosthesis that is similar to natural teeth. Accordingly, the time and process for manufacturing the artificial dental prosthesis are shortened, and structural stability is increased in terms of dispersion of force due to gradient functionalization of mechanical properties.

A dental formulation including: a bioactive glass composition as defined herein, in an effective amount; and a suitable carrier as defined herein, in an effective amount. Also disclosed is a method of making and using the dental formulation to treat, for example, dentin sensitivities.