A magnetic PCB generated by simultaneously spin-spraying a ferrite ion solution and an oxidant solution on a substrate plate while the substrate plate is rotated at a speed 40 rpm to about 300 rpm and heated at 40? C. to 300? C.

Present disclosure relates to magnetic materials, chips having magnetic materials, and methods of forming magnetic materials. In certain embodiments, magnetic materials may include a seed layer, and a cobalt-based alloy formed on seed layer. The seed layer may include copper, cobalt, nickel, platinum, palladium, ruthenium, iron, nickel alloy, cobalt-iron-boron alloy, nickel-iron alloy, and any combination of these materials. In certain embodiments, the chip may include one or more on-chip magnetic structures. Each on-chip magnetic structure may include a seed layer, and a cobalt-based alloy formed on seed layer. In certain embodiments, method may include: placing a seed layer in an aqueous electroless plating bath to form a cobalt-based alloy on seed layer. In certain embodiments, the aqueous electroless plating bath may include sodium tetraborate, an alkali metal tartrate, ammonium sulfate, cobalt sulfate, ferric ammonium sulfate and sodium borohydride and has a pH between about 9 to about 13.

An inductor built-in substrate includes a core substrate having openings and first through holes formed therein, a magnetic resin filling the openings and having second through holes formed therein, first through-hole conductors formed in the first through holes of the core substrate and including metal films formed in the first through holes of the core substrate, respectively, and second through-hole conductors formed in the second through holes of the magnetic resin and including metal films formed in the second through holes of the magnetic resin such that the metal films are filling the second through holes of the magnetic resin, respectively.

An inductor built-in substrate includes a core substrate having openings and first through holes formed therein, a magnetic resin filling the openings and having second through holes formed therein, first through-hole conductors formed in the first through holes of the core substrate and including metal films formed in the first through holes of the core substrate, respectively, and second through-hole conductors formed in the second through holes of the magnetic resin and including metal films formed in the second through holes of the magnetic resin such that the metal films are filling the second through holes of the magnetic resin, respectively.

This invention relates to a magnetic composite powder, a method of preparing the same and an electromagnetic noise suppressing film comprising the same. The magnetic composite powder and the electromagnetic noise suppressing film can effectively suppress unwanted electromagnetic waves emitted by various parts of an advanced digital device having high performance characteristics in terms of speed, frequency and functionality.

This invention relates to a magnetic composite powder, a method of preparing the same and an electromagnetic noise suppressing film comprising the same. The magnetic composite powder and the electromagnetic noise suppressing film can effectively suppress unwanted electromagnetic waves emitted by various parts of an advanced digital device having high performance characteristics in terms of speed, frequency and functionality.

A fabrication method for fabricating a magnetic film provided body includes preparing a base body and forming a magnetic film on the base body. The magnetic film includes organic film(s) and ferrite film(s) alternately layered. The formation of the magnetic film alternately includes forming a ferrite film through a ferrite plating method, the ferrite film having a thickness of 20 m or less and forming an organic film having a thickness of 0.1 m to 20 m, both inclusive, and a ratio t/E of 0.025 m/GPa or more, where t indicates the thickness of the organic film while E indicates Young's modulus of the organic film.

A fabrication method for fabricating a magnetic film provided body includes preparing a base body and forming a magnetic film on the base body. The magnetic film includes organic film(s) and ferrite film(s) alternately layered. The formation of the magnetic film alternately includes forming a ferrite film through a ferrite plating method, the ferrite film having a thickness of 20 m or less and forming an organic film having a thickness of 0.1 m to 20 m, both inclusive, and a ratio t/E of 0.025 m/GPa or more, where t indicates the thickness of the organic film while E indicates Young's modulus of the organic film.

The present invention provides a process for production of a magnetic thin film which has insulation properties, serves as a permanent magnet, and has improved residual magnetization in comparison with prior arts, the magnetic thin film, and a magnetic material. When a magnetic thin film 3 is formed, an external magnetic field with a predetermined intensity is applied to a coating liquid containing magnetic particles containing epsilon-type iron-oxide-based compounds which have insulation properties and which serve as a permanent magnet, and the coating liquid is let cured in order to form the magnetic thin film 3. Accordingly, the magnetic particles containing the epsilon-type iron-oxide-based compounds can be fixed while being oriented regularly in a magnetization direction. This realizes the process for production of the magnetic thin film 3 which has insulation properties and which serve as a permanent magnet, the magnetic thin film 3, and a magnetic material 1.

The present invention provides a process for production of a magnetic thin film which has insulation properties, serves as a permanent magnet, and has improved residual magnetization in comparison with prior arts, the magnetic thin film, and a magnetic material. When a magnetic thin film 3 is formed, an external magnetic field with a predetermined intensity is applied to a coating liquid containing magnetic particles containing epsilon-type iron-oxide-based compounds which have insulation properties and which serve as a permanent magnet, and the coating liquid is let cured in order to form the magnetic thin film 3. Accordingly, the magnetic particles containing the epsilon-type iron-oxide-based compounds can be fixed while being oriented regularly in a magnetization direction. This realizes the process for production of the magnetic thin film 3 which has insulation properties and which serve as a permanent magnet, the magnetic thin film 3, and a magnetic material 1.