An iron-based oxide magnetic powder has good thermal stability and a small change in coercive force even in a high-temperature environment and is one composed of particles of ε-iron oxide in which Fe sites are partially substituted by another metal element. A production method for such an iron-based oxide magnetic powder includes allowing a phosphorus-containing ion to coexist when a precipitate of an iron hydroxide containing a substituent metal element produced by neutralizing an acidic aqueous solution containing a trivalent iron ion and an ion of a metal that partially substitutes Fe sites is coated with silicon oxide using a silane compound.

A substitution-type ε-iron oxide magnetic particle powder having a reduced content of a non-magnetic α-type iron-based oxide and Fe sites of ε-Fe.sub.2O.sub.3 partially substituted by another metal element is obtained by neutralizing an acidic aqueous solution containing a trivalent iron ion and an ion of a metal that partially substitutes Fe sites to a pH of 2.0 or higher and 7.0 or lower. A silicon compound having a hydrolyzable group is added to a dispersion liquid containing an iron oxyhydroxide having a substituent metal element or a mixture of an iron oxyhydroxide and a hydroxide of a substituent metal element. The dispersion liquid is neutralized to a pH of 8.0 or higher and the iron oxyhydroxide having a substituent metal element or the mixture of the iron oxyhydroxide and the hydroxide of a substituent metal element is coated with a chemical reaction product of the silicon compound and then heated.

A method of purifying a plurality of metal oxide particles produced from a synthesis process comprising the step of washing a plurality of metal oxide particles in a first solvent composition comprising of at least one aliphatic ether, and at least one flocculant. In one embodiment, the plurality of metal oxide particles are iron oxide particles produced from a thermal decomposition synthesis process between an iron-oleate complex and oleic acid in 1-octadecene, wherein the first solvent composition comprises a 1:1 (vol/vol) ratio of an aliphatic ether in the form of diethyl ether and a flocculant in the form of methanol. The washed iron oxide particles are further washed in a second solvent composition comprising a 1:1 (vol/vol) ratio of hexane and ethanol, and then finally dispersed in hexane. The resulting iron oxide particles find use as a contrast agent for magnetic resonance imaging (MRI) or as magnetic particles in magnetic separation, magnetism-directed targeting or magnetism-induced heating.

A method of purifying a plurality of metal oxide particles produced from a synthesis process comprising the step of washing a plurality of metal oxide particles in a first solvent composition comprising of at least one aliphatic ether, and at least one flocculant. In one embodiment, the plurality of metal oxide particles are iron oxide particles produced from a thermal decomposition synthesis process between an iron-oleate complex and oleic acid in 1-octadecene, wherein the first solvent composition comprises a 1:1 (vol/vol) ratio of an aliphatic ether in the form of diethyl ether and a flocculant in the form of methanol. The washed iron oxide particles are further washed in a second solvent composition comprising a 1:1 (vol/vol) ratio of hexane and ethanol, and then finally dispersed in hexane. The resulting iron oxide particles find use as a contrast agent for magnetic resonance imaging (MRI) or as magnetic particles in magnetic separation, magnetism-directed targeting or magnetism-induced heating.

Disclosed herein are embodiments of composite hexagonal ferrite materials formed from a combination of Y phase and Z phase hexagonal ferrite materials. Advantageously, embodiments of the material can have a high resonant frequency as well as a high permeability. In some embodiments, the materials can be useful for magnetodielectric antennas.

Disclosed herein are embodiments of composite hexagonal ferrite materials formed from a combination of Y phase and Z phase hexagonal ferrite materials. Advantageously, embodiments of the material can have a high resonant frequency as well as a high permeability. In some embodiments, the materials can be useful for magnetodielectric antennas.

A magnetic compound having a small dielectric loss and an antenna constituted by the magnetic compound and an electronic device incorporating the antenna are provided by a metal magnetic powder which is well dispersed in a resin having small dielectric loss, and a magnetic powder composite including: a metal magnetic powder; and one or more elements selected from carboxylic acid or its anhydride, aromatic carboxylic acid ester, and a derivative thereof, having a property that real part μ′ permeability is 1.45 or more, tan δμ is 0.1 or less, tan δε is 0.05 or less at a measuring frequency of 2 GHz, when a magnetic powder composite is prepared by adding 5 parts by mass of one or more elements selected from the carboxylic acid or its anhydride, the aromatic carboxylic acid ester, and the derivative thereof to 100 parts by mass of the metal magnetic powder.

A method of producing a magnetic powder includes: performing heat treatment on first particles that contain triiron tetraoxide to prepare second particles that contain ε-iron oxide.

A method of producing a magnetic powder includes: performing heat treatment on first particles that contain triiron tetraoxide to prepare second particles that contain ε-iron oxide.

[Problem] To provide a method for producing iron based oxide magnetic powder that has a narrow particle size distribution and a small content of fine particles that do not contribute to the magnetic recording characteristics, and consequently has a narrow coercive force distribution and is suitable for the enhancement of the recording density of the magnetic recording medium. [Solution] ε-Type iron based oxide magnetic powder is obtained by a wet method, then a tetraalkylammonium salt as a surface modifier is added to a slurry containing the magnetic powder to make a concentration of 0.009 mol/kg or more and 1.0 mol/kg or less, and simultaneously to make pH of 11 or more and 14 or less, and the slurry is subjected to a dispersion treatment and then classified, so as to provide iron based oxide magnetic powder having a narrow particle size distribution and a narrow coercive force distribution.