Disclosed herein is a method of forming a multilayer thin film by depositing target particles, detached from a target by plasma discharge of inert gas, on a metal object using a multilayer thin film deposition apparatus and a multilayer thin film formed by the method. More specifically, a sputtering deposition apparatus is used as the multilayer thin film deposition apparatus. The method includes coating a metal object with a coating layer, depositing at least one hardness-enhancing layer on the coating layer, and depositing a color layer on the at least one hardness-enhancing layer.

The invention relates to a component having a coating containing chromium, nitrogen and carbon. According to the invention the coating comprises a sliding layer having a ceramic phase and a carbon phase, the ceramic phase forms a crystalline ceramic phase from Crx(C.sub.1-yN.sub.y) with 0.8=x=1.2 and y>0.7, and the crystalline ceramic phase and the carbon phase form a layer system of alternating individual layers (A, B), wherein the carbon phase has interstices that are filled with the crystalline ceramic phase.

A coating system for a surface of a superalloy component is provided. The coating system includes a MCrAlY coating on the surface of the superalloy component, where M is Ni, Fe, Co, or a combination thereof. The MCrAlY coating generally has a higher chromium content than the superalloy component. The MCrAlY coating also includes a platinum-group metal aluminide diffusion layer. The MCrAlY coating includes Re, Ta, or a mixture thereof. Methods are also provided for forming a coating system on a surface of a superalloy component.

The present invention relates to a hot-rolled steel sheet for a high strength galvanized steel sheet, having excellent surface quality, and a method for producing the same, the hot-rolled steel sheet comprising, by weight %: C: 0.05 to 0.15%, Si: 0.03 to 0.10%, Mn: 0.7 to 1.39%, P: 0.001 to 0.05%, S: 0.001 to 0.03%, Al: 0.002 to 0.035%, and the remainder being Fe and unavoidable impurities. The weight ratio of Mn/Si is 15 to 25, the weight ratio of C/Si is 1 to 5, and the weight ratio of Si/P is 3 to 10. The hot-rolled steel sheet has a microstructure consisting of, in area fraction, 10 to 40% of bainite, 20 to 30% of pearlite and 40 to 60% of ferrite, and includes a ternary eutectic compound of FeO, Fe.sub.2SiO.sub.4 and Fe.sub.3(PO).sub.4 formed within 50 μm from the surface.

A method for depositing a coating comprising a polymer and pharmaceutical agent on a substrate, comprising the following steps: discharging at least one pharmaceutical agent in a therapeutically desirable morphology in dry powder form through a first orifice; discharging at least one polymer in dry powder form through a second orifice; depositing the polymer and/or pharmaceutical particles onto said substrate, wherein an electrical potential is maintained between the substrate and the pharmaceutical and/or polymer particles, thereby forming said coating; and sintering said coating under conditions that do not substantially modify the morphology of said pharmaceutical agent.

An example hydraulic system component of a machine includes a protective coating deposited by high velocity air fuel (HVAF) thermal spray, exhibiting high adhesion strengths and surface morphologies that promote lubricant adhesion and reduce the leakage of oil and/or hydraulic fluid from the hydraulic system. The coating may have surface roughness with Rz values less than 2 μm and hardness of 1000 Vickers or greater. The HVAF coating may be thinner than conventional coatings with thicknesses less than 100 μm. The HVAF coating may be deposited on a variety of steel components with adhesion strengths greater than those achieved by high velocity oxygen fuel (HVOF). The HVAF coating may be formed without time consuming roughening and/or post-grind operations, resulting in cost savings compared to conventional coatings. The coatings may have operational lifetimes of 1000 hours or more.

The invention relates to an aluminum alloy strip with improved surface optics, which is fabricated via hot and/or cold rolling, and consists of a type AA 3xxx, AA 5xxx, AA 6xxx or AA 8xxx aluminum alloy. The object of proposing an aluminum alloy strip that is suitable for attractive and precious surface optics despite the elevated percentage of alloy constituents is achieved in that, after degreasing, the finish-rolled aluminum alloy strip exhibits an increase in the luminance value L*(ΔL) in relation to the rolled-greasy state of more than 5 while measuring the color of the surface in the CIE L*a*b* color space using a standard illuminant D65 and a normal observation angle of 10°, excluding direct reflection in 45°/0° geometry.

A hot-dip galvanized steel sheet wherein the hot-dip galvanized steel sheet comprises a base steel sheet and a hot-dip galvanized layer, a ferrite phase is, by volume fraction, 50% or less in a range of ⅛ thickness to ⅜ thickness centered at a position of ¼ thickness from the surface of the base steel sheet, a hard structure is 50% or more, wherein the hot-dip galvanized steel sheet has the hot-dip galvanized layer in which Fe is 5.0% or less and Al is 1.0% or less, and columnar grains formed of a ζ phase is 20% or more in an entire interface between the plated layer and the base steel sheet, on the surface of the base steel sheet in which a volume fraction of a residual austenite is 3% or less and a ratio of a volume fraction of the hard structure is 0.10 times or more to 0.90 times or less of that of the hard structure in the range of ⅛ thickness to ⅜ thickness in a range of 20 μm depth in a steel sheet direction originating an interface between the hot-dip galvanized layer and the base steel sheet, and wherein the hot-dip galvanized steel sheet has a refined layer at the side of the interface in the base steel sheet, and wherein an average thickness of the refined layer, an average grain size of ferrite in the refined layer and a maximum size of the oxide included in the refined layer are defined respectively.

A tin-plated copper alloy terminal material in which an Sn-based surface layer is formed on a surface of a base material that is made of copper or a copper alloy, and a Cu—Sn alloy layer and an Ni layer or an Ni alloy layer are sequentially formed between the Sn-based surface layer and the base material from the Sn-based surface layer side: the Cu—Sn alloy layer is a layer that is formed only of an intermetallic compound alloy which is obtained by substituting some of Cu in Cu.sub.6Sn.sub.5 alloy with Ni; and parts of the Cu—Sn alloy layer are exposed from the Sn-based surface layer, thereby forming a plurality of exposed portions; an average thickness of the Sn-based surface layer is from 0.2 μm to 0.6 μm (inclusive); and an area rate of the exposed portions of the Cu—Sn alloy layer relative to a surface area of is 1% to 40% (inclusive).

Provided is a zinc-based plated steel sheet having a post-treated coating filmed thereon including: a steel sheet; a zinc plated layer formed on the steel sheet; and a post-treated coating formed on the plated layer, wherein the atomic ratio (O/M) of oxygen (O) to metals (M) contained in the post-treated coating is greater than 2 and less than 20, and a method for post-treating a zinc-based plated steel sheet. According to this, the zinc-based plated steel sheet having the post-treated coating formed thereon has the effects excellent in lubricity, weldability, adhesiveness, film-removing property and paintability. As the method of post-treating a zinc-based plated steel sheet of the present invention employs a simple coating method irrespective of the kind of plating layer, the process is simple and economical and the process operation cost is low.