Provided is a zinc-based plated steel sheet having a post-treated coating filmed thereon including: a steel sheet; a zinc plated layer formed on the steel sheet; and a post-treated coating formed on the plated layer, wherein the atomic ratio (O/M) of oxygen (O) to metals (M) contained in the post-treated coating is greater than 2 and less than 20, and a method for post-treating a zinc-based plated steel sheet. According to this, the zinc-based plated steel sheet having the post-treated coating formed thereon has the effects excellent in lubricity, weldability, adhesiveness, film-removing property and paintability. As the method of post-treating a zinc-based plated steel sheet of the present invention employs a simple coating method irrespective of the kind of plating layer, the process is simple and economical and the process operation cost is low.

A superalloy component such as a gas turbine engine blade (40) having a ceramic thermal barrier coating (41) is repaired using a textured repair foil (30). A degraded region of the thermal barrier coating is removed (14) and the underlying superalloy material surface is prepared (16) for re-coating. The repair foil is includes a layer of boron-free braze material (34) and a layer of superalloy material (32) having a textured surface (36). The foil is brazed (18) to the prepared surface during a solution heat treatment effective to homogenize the braze (20). A new area of thermal barrier coating (46) is applied over the foil with a bond that is enhanced by the texturing of the foil surface.

A high-strength galvanized steel sheet comprising a cold-rolled steel sheet, an intermetallic compound formed on the cold-rolled steel sheet, and a galvanizing layer formed on the intermetallic compound, the cold-rolled steel sheet having a specific composition and a microstructure having a martensite area ratio of 7% or more and less than 25% and a ferrite area ratio of 50% or more and which includes a base metal surface portion in which the amount of internal oxides per single side is 0.05 g/m.sup.2 or less.

A high-strength galvanized steel sheet comprising a cold-rolled steel sheet, an intermetallic compound formed on the cold-rolled steel sheet, and a galvanizing layer formed on the intermetallic compound, the cold-rolled steel sheet having a specific composition and a microstructure having a martensite area ratio of 7% or more and less than 25% and a ferrite area ratio of 50% or more and which includes a base metal surface portion in which the amount of internal oxides per single side is 0.05 g/m.sup.2 or less.

A configuration for joining a ceramic layer has a thermal insulating material to a metallic layer. The configuration includes an interface layer made of metallic material located between the ceramic layer and the metallic layer, which includes a plurality of interlocking elements on one of its sides, facing the ceramic layer, the ceramic layer comprising a plurality of cavities aimed at connecting with the corresponding interlocking elements of the interface layer. The configuration also includes a brazing layer by means of which the interface layer is joint to the metallic layer. The invention also refers to a method for obtaining such a configuration.

A flat steel product for hot forming may be produced from a steel substrate that includes a steel comprising 0.1-3% by weight Mn and up to 0.01% by weight B, along with a protective coating that is applied to the steel substrate. The protective coating may be based on Al and may contain up to 20% by weight of other alloy elements. Also disclosed are methods for producing such flat steel products, steel components, and methods for producing steel components. Absorption of hydrogen is minimized during heating necessary for hot forming. This is achieved at least in part through an alloy constituent of 0.1-0.5% by weight of at least one alkaline earth or transition metal in the protective coating, wherein an oxide of the alkaline earth or transition metal is formed on an outer surface of the protective coating during hot forming of the flat steel product.

A component includes a film containing polycrystalline yttrium oxide. In an X-ray diffraction pattern of the film, a ratio I.sub.m/I.sub.c of a maximum intensity I.sub.m of a peak attributed to monoclinic yttrium oxide to a maximum intensity I.sub.c of a peak attributed to cubic yttrium oxide satisfies an expression: 0≤I.sub.m/I.sub.c≤0.002.

A coated metallic substrate is provided, including, at least; one layer of oxides, such layer being directly topped by an intermediate coating layer comprising Fe, Ni, Cr and Ti wherein the amount of Ti is above or equal to 5 wt. % and wherein the following equation is satisfied: 8 wt. %<Cr+Ti<40 wt. %, the balance being Fe and Ni, such intermediate coating layer being directly topped by a coating layer being an anticorrosion metallic coating.

A hot-dip Sn—Zn-based alloy-plated steel sheet according to an aspect of the present invention includes: a steel sheet having a predetermined chemical composition; a diffusion alloy layer provided on one surface or both surfaces of the steel sheet; and a Sn—Zn-plated layer provided on the diffusion alloy layer, in which the diffusion alloy layer contains Fe, Sn, Zn, Cr, and Ni, an area ratio of a Sn—Fe—Cr—Zn phase to a Sn—Fe—Ni—Zn phase in the diffusion alloy layer is 0.01 or more and less than 2.5, the diffusion alloy layer has a coverage of 98% or more with respect to the one surface, the Sn—Zn-plated layer contains 1% to 20% of Zn by mass % and a remainder consisting of Sn and impurities, and an adhesion amount of the Sn—Zn-plated layer is 10 to 80 g/m.sup.2 per one surface.

There is provided a hot-stamped body including: a steel base metal; and a metallic layer formed on a surface of the steel base metal, wherein the metallic layer includes: an interface layer that contains, in mass %, Al: 30.0 to 36.0%, has a thickness of 100 nm to 5 μm, and is located in an interface between the metallic layer and the steel base metal; and a principal layer that includes coexisting MgZn.sub.2 phases and insular FeAl.sub.2 phases, is located on the interface layer, and has a thickness of 3 μm to 40 μm.