The present invention relates to an ultra-high strength, hot-dip galvanized steel sheet having excellent surface quality and coating adherence and to a method for manufacturing thereof, the ultra-high strength, hot-dip galvanized steel sheet comprising: 0.1-0.3% by weight carbon (C); 0.1-2.0% by weight silicon (Si); 0.005-1.5% by weight aluminum (Al); 1.5-3.5% by weight manganese (Mn); 0.04% by weight or less phosphorus (P) (excluding 0% by weight); 0.015% by weight or less sulphur (S) (excluding 0% by weight); 0.02% by weight or less nitrogen (N) (excluding 0% by weight); the balance being Fe; and other inevitable impurities, and further comprising 0.01 wt.% to 0.07 wt.% of at least one kind of element selected from the group consisting of bismuth (Bi), tin (Sn) and antimony (Sb).

A hot-dip plated steel according to one aspect includes a base steel and a hot-dip plating layer disposed on a surface of the base steel, a chemical composition of the hot-dip plating layer contains, by mass%, Al: 10.00% to 30.00%, Mg: 3.00% to 12.00%, Sn: 0% to 2.00%, Si: 0% to 2.50%, Ca: 0% to 3.00%, Ni: 0% or more and less than 0.25%, Fe: 0% to 5.00%, and the like, a remainder consists of Zn and impurities, a metallographic structure of the hot-dip plating layer contains 5 to 45 area% of an α phase having a grain diameter of 0.5 to 2 .Math.m, the metallographic structure of the hot-dip plating layer contains 15 to 70 area% of a MgZn.sub.2 phase, and, among the α phases having the grain diameter of 0.5 to 2 .Math.m, an area ratio of an α phase having a (111).sub.α//(0001).sub.MgZn2 orientation relationship to the adjacent MgZn.sub.2 phase is 25% to 100%.

A galvannealed steel sheet includes: a scale-removed rolled steel sheet; and a galvannealed layer arranged on the scale-removed rolled steel sheet. When ten measurement points of the galvannealed steel sheet are set in a transverse direction by equally dividing a line-segment having a reference length of 50 mm by 10, a minimum P content of the galvannealed layer in the ten measurement points is 50% or more as compared with a maximum P content therein.

A plated steel material comprising a steel base material and an Al—Zn—Mg-based plating layer formed on a surface of the steel base material, wherein the plating layer has a predetermined chemical composition, and in a surface structure of the plating layer, there is, by area ratio, 2.0% or more of an acicular Al—Zn—Si—Ca phase.

A high strength galvanized steel sheet has a composition including, C: 0.02% or more and 0.30% or less, Si: 0.01% or more and 2.5% or less, Mn: 0.1% or more and 3.0% or less, P: 0.003% or more and 0.08% or less, S: 0.01% or less, Al: 0.001% or more and 0.20% or less, Ti: 0.03% or more and 0.40% or less and the balance being Fe and inevitable impurities, and a zinc-coated layer having a coating weight per surface of 20 g/m.sup.2 or more and 120 g/m.sup.2 or less. The concentration ratio of C to Ti (C/Ti) in a portion within 10 μm from the surface of the base steel sheet is 0.8 or more and 1.5 or less, and the total amount of oxides of one or more selected from Fe, Si, Mn, P, Al and Ti formed in a surface portion within 100 μm from the surface of the base steel sheet is 0.05 g/m.sup.2 or less.

The present invention relates to a hot-rolled steel sheet for a high strength galvanized steel sheet, having excellent surface quality, and a method for producing the same, the hot-rolled steel sheet comprising, by weight %: C: 0.05 to 0.15%, Si: 0.03 to 0.10%, Mn: 0.7 to 1.39%, P: 0.001 to 0.05%, S: 0.001 to 0.03%, Al: 0.002 to 0.035%, and the remainder being Fe and unavoidable impurities. The weight ratio of Mn/Si is 15 to 25, the weight ratio of C/Si is 1 to 5, and the weight ratio of Si/P is 3 to 10. The hot-rolled steel sheet has a microstructure consisting of, in area fraction, 10 to 40% of bainite, 20 to 30% of pearlite and 40 to 60% of ferrite, and includes a ternary eutectic compound of FeO, Fe.sub.2SiO.sub.4 and Fe.sub.3(PO).sub.4 formed within 50 μm from the surface.

The present disclosure relates to an ultra-high-strength plated steel sheet and a method for molding the same, and more particularly, to an ultra-high-strength plated steel sheet having high tensile strength without the occurrence of plating peeling and hydrogen delayed fracture phenomenon during roll forming molding, and a method for molding the same.

Provided is a galvannealed steel sheet with excellent anti-powdering property when press forming is performed, without controlling the contents of chemical elements in steel which are effective for strengthening a steel sheet, such as Si and P, to be low in order to achieve required material properties and without increasing cost due to, for example, processes being complicated. A galvannealed steel sheet with excellent anti-powdering property has a coated layer taking in grains of a base steel sheet such that the grains constitute 2.0% or more and 15.0% or less of the coated layer in terms of cross section area ratio.

The present invention provides steel sheet products having controlled compositions that are subjected to two-step annealing processes to produce sheet products having desirable microstructures and favorable mechanical properties such as high strength and ultra-high formability. Steels processed in accordance with the present invention exhibit combined ultimate tensile strength and total elongation (UTS.Math.TE) properties of greater than 25,000 MPa-%. Steels with these properties fall into the category of Generation 3 advanced high strength steels, and are highly desired by various industries including automobile manufacturers.

High strength steel sheet having a tensile strength of 800 MPa or more comprising a middle part in sheet thickness and a soft surface layer arranged at one side or both sides of the middle part in sheet thickness, wherein each soft surface layer has a thickness of more than 10 μm and 30% or less of the sheet thickness, the soft surface layer has an average Vickers hardness of 0.60 time or less the average Vickers hardness of the sheet thickness ½ position, and the soft surface layer has a nano-hardness standard deviation of 0.8 or less is provided.