There is provided a hot-stamped body including: a steel base metal; and a metallic layer formed on a surface of the steel base metal, wherein the metallic layer includes: an interface layer that contains, in mass %, Al: 30.0 to 36.0%, has a thickness of 100 nm to 5 μm, and is located in an interface between the metallic layer and the steel base metal; and a principal layer that includes coexisting MgZn.sub.2 phases and insular FeAl.sub.2 phases, is located on the interface layer, and has a thickness of 3 μm to 40 μm.

Disclosed is a hot-pressed steel sheet member having a tensile strength of 1780 MPa or more and excellent bending collapsibility. The hot-pressed steel sheet member includes: a specific chemical composition; a microstructure in which an average grain size of prior austenite grains is 8 μm or less, a volume fraction of martensite is 90% or more, and a solute C content is 25% or less of a total C content; and a tensile strength of 1780 MPa or more.

Disclosed are a ferritic stainless steel capable of inhibiting high temperature oxidation through generation of an effective oxide scale, and manufacturing method thereof. The ferritic stainless steel excellent in oxidation resistance at high temperature according to an embodiment of the present disclosure includes, in percent (%) by weight of the entire composition, Cr: 10 to 30%, Si: 0.2 to 1.0%, Mn: 0.1 to 2.0%, W: 0.3 to 2.5%, Ti: 0.001 to 0.15%, Al: 0.001 to 0.1%, the remainder of iron (Fe) and other inevitable impurities, and satisfies a following equation (1).
W/(Ti+Al)≥10  (1)

Provided is a hot-dip galvanized steel sheet having excellent low-temperature adhesion and workability, and a manufacturing method therefor, the hot-dip galvanized steel sheet comprising: an inhibition layer formed on a base steel sheet and comprising an Fe—Al-based intermetallic alloy phase; a hot-dip galvanized layer formed on the inhibition layer; and an Al—Mn-based alloy phase discontinuously formed between the inhibition layer and the hot-dip galvanized layer.

A color coating layer is formed on the surface of a stainless steel plate by a chemical coloring method or an electrolytic coloring method. Thereafter, a colored stainless steel plate having the color coating layer is cold-rolled, the thickness of the color coating layer is adjusted to between 0.05 μm and 1.0 μm, and an entire plate thickness is adjusted to 0.5 mm or less. By the cold rolling a Vickers hardness Hv is between 250 and 550 to form a deformed band. As surface roughness, an arithmetic average roughness Ra is adjusted to between 0.05 μm and 5.0 μm. In this manner, the strength and rigidity of a thin colored stainless steel plate can be secured, and a color stainless steel plate and a colored stainless steel coil which do not easily cause galling and are excellent in press moldability can be obtained.

Provided is a plated steel material which can be used for an automobile, a household appliance, a building material, and the like and, more specifically, to a zinc alloy plated steel material having excellent surface quality and corrosion resistance, and a method for manufacturing the same.

A plated steel sheet includes: a steel sheet; and a plating layer that is formed on at least a part of a surface of the steel sheet, in which a chemical composition of the plating layer includes, by mass %, Al: more than 5.00% and 35.00% or less, Mg: 3.00% to 15.00%, Si: 0% to 2.00%, Ca: 0% to 2.00%, and a remainder of Zn and impurities, in which in a cross section of the plating layer in a thickness direction, the area ratio of a lamellar structure in which an (Al—Zn) phase and a MgZn.sub.2 phase are arranged in layers is 10% to 90%, a lamellar spacing of the lamellar structure is 2.5 μm or less, and the area ratio of an (Al—Zn) dendrite is 35% or less.

A plated steel sheet having excellent chemical convertibility includes: a steel; and a plating layer that is provided on a surface of the steel, in which the plating layer includes, by mass %, Al: 5.00% to 35.00%, Mg: 2.50% to 13.00%, Fe: 5.00% to 35.00%, Si: 0% to 2.00%, Ca: 0.03% to 2.00%, and a remainder consisting of Zn and impurities, and in a surface of the plating layer, the area fraction of a Fe—Al phase is 0% to 30%, the area fraction of a rod-like lamellar structure of Zn and MgZn.sub.2 is 5% to 90%, the area fraction of a massive MgZn.sub.2 phase is 10% to 70%, and the area fraction of a remainder is 10% or less.

A high-strength steel sheet satisfies a predetermined chemical composition in which a content of martensite is 93% by volume or more, contents of ferrite, pearlite, and bainite are 2% by volume or less in total, and a content of retained austenite is 7% by volume or less, based on an entire metal structure, a number of laths in martensite measured by a cutting method in a total length of 300 μm in an image of the metal structure observed under a scanning electron microscope is 240 or more, and a tensile strength of the high-strength steel sheet is 1470 MPa or more.

Provided is a steel sheet for a hot press formed member having excellent resistance to hydrogen delayed fracture, and a method for manufacturing the same. A steel sheet for a hot press formed member comprises: a base steel sheet; an aluminum alloy plating layer on a surface of the base steel sheet; and an oxide layer which is formed on a surface of the plating layer and has a thickness of 0.05 μm or more.