Zn alloy plated steel material having excellent weldability and processed-part corrosion resistance and a method for production of Zn alloy plated steel material are provided. In the Zn alloy plated steel material comprising base steel material and a Zn alloy plating layer, the Zn alloy plating layer includes, by wt %, Al: 0.1-5.0%, Mg: 0.1-5.0%, as well as a remainder of Zn and inevitable impurities. The Zn alloy plated steel material includes a lower interface layer and an upper interface layer between the base steel material and the Zn alloy plating layer, wherein the lower interface layer is formed on the base steel material and has a dense structure, and the upper interface layer is formed on the lower interface layer and has a network-type or island-type structure.

A flat steel product for hot forming may be produced from a steel substrate that includes a steel comprising 0.1-3% by weight Mn and up to 0.01% by weight B, along with a protective coating that is applied to the steel substrate. The protective coating may be based on Al and may contain up to 20% by weight of other alloy elements. Also disclosed are methods for producing such flat steel products, steel components, and methods for producing steel components. Absorption of hydrogen is minimized during heating necessary for hot forming. This is achieved at least in part through an alloy constituent of 0.1-0.5% by weight of at least one alkaline earth or transition metal in the protective coating, wherein an oxide of the alkaline earth or transition metal is formed on an outer surface of the protective coating during hot forming of the flat steel product.

Disclosed is a hot-dip Al—Zn alloy coated steel sheet having excellent anti-corrosion property after coating, and a method for producing the same. In the disclosure, the hot-dip Al—Zn alloy coated steel sheet has a hot-dip coating layer containing by mass %, Al: 25% to 90%, and at least one of Sn: 0.01% to 2.0%, In: 0.01% to 10%, and Bi: 0.01% to 2.0%.

A hydrocarbon fluid containment article having a wall with a surface that is wetted by hydrocarbon fluid. The surface includes an anti-coking coating. The anti-coking coating includes a copper salt, a silver salt, or a combination thereof. A gas turbine engine component including a wall having a first surface and an anti-coking coating on the first surface of the wall that is wetted by hydrocarbon fluid. The anti-coking coating including a copper salt, a silver salt, or a combination thereof that prevents the formation of gum or coke on a surface thereon. Methods for reducing the deposition of thermal decomposition products on a wall of an article are also provided.

Provided is a multilayer zinc alloy plated steel material comprising a base steel material and multiple plating layers formed on the base steel material, wherein each of the multiple plating layers includes one of a Zn plating layer, a Mg plating layer, and a Zn—Mg alloy plating layer, and the ratio of the weight of Mg contained in the multiple plating layers to the total weight of the multiple plating layers is from 0.13 to 0.24.

Provided is a steel sheet for a hot press formed member having excellent coating adhesion, and a method for manufacturing the same. A steel sheet for hot press forming is an aluminum alloy plated steel sheet, wherein an average Fe content in a plating layer may be 40 wt % or more, and a concentration gradient of a section having a Fe content of 45 wt % to 80 wt % in the plating layer may 7 wt %/μm or less of a concentration gradient at a section having an Fe content of 45% to 80% in the plating layer in a thickness direction from a surface of the plating layer according to a result of GDS analysis.

Provided is a zinc alloy-plated steel material used in automobiles, building materials, home appliances, or the like, and more specifically, to a zinc alloy-plated steel material having excellent corrosion resistance and surface quality, and a method for producing same.

A surface-treated steel sheet for a battery container, including a steel sheet, an iron-nickel diffusion layer formed on the steel sheet, and a nickel layer formed on the iron-nickel diffusion layer and constituting the outermost layer, wherein when the Fe intensity and the Ni intensity are continuously measured from the surface of the surface-treated steel sheet for a battery container along the depth direction with a high frequency glow discharge optical emission spectrometric analyzer, the thickness of the iron-nickel diffusion layer being the difference between the depth at which the Fe intensity exhibits a first predetermined value and the depth at which the Ni intensity exhibits a second predetermined value is 0.04 to 0.31 μm; and the total amount of the nickel contained in the iron-nickel diffusion layer and the nickel contained in the nickel layer is 4.4 g/m.sup.2 or more and less than 10.8 g/m.sup.2.

A coated metallic substrate is provided, including, at least; one layer of oxides, such layer being directly topped by an intermediate coating layer comprising Fe, Ni, Cr and Ti wherein the amount of Ti is above or equal to 5 wt. % and wherein the following equation is satisfied: 8 wt. %<Cr+Ti<40 wt. %, the balance being Fe and Ni, such intermediate coating layer being directly topped by a coating layer being an anticorrosion metallic coating.

A hot-dip-coated, non-skin-passed, cold-rolled metal strip is provided. The metal coating of the metal strip includes a waviness Wa.sub.0.8 of less than or equal to 0.70 μm, 0.2 to 8% by weight of aluminum and magnesium, and up to 0.3% by weight of additional elements, the balance being zinc and inevitable impurities. Metal parts are also provided.