Provided is a tantalum sputtering target, which includes an area ratio of crystal grains of which a {111} plane is oriented in a direction normal to a rolling surface (ND) is 35% or more when the ND, which is a cross section orthogonal to a sputtering surface of a target, is observed via Electron Backscatter Diffraction Pattern method. The object of the present invention is to provide a tantalum sputtering target in which a sputtered material can be uniformly deposited on a wafer surface under high-power sputtering conditions by increasing the straightness of the sputtered material. By using this kind of tantalum target for sputter-deposition, it is possible to improve the film thickness uniformity and the throughput of deposition even for fine wiring.

This method for manufacturing a high-temperature component formed of a Ni-based alloy includes a step of subjecting a workpiece of the Ni-based alloy to hot die forging using predetermined dies to form a forge-molded article, the step including: a die/workpiece co-heating substep of heating the workpiece interposed between the dies to a forging temperature; and a hot forging substep of taking out the workpiece and the dies into a room temperature environment and immediately performing hot forging on the workpiece using a press machine. The predetermined dies are formed of another Ni-based superalloy comprising and phases, and have features in that: a solvus temperature of the phase is 1050-1250 C.; and the phase precipitates at least 10 vol. % at 1050 C. and has two kinds of forms of intra-grain phase precipitations within the phase grains and inter-grain phase precipitations between/among the phase grains.

A calcium-bearing magnesium and rare earth element alloy consists essentially of, in mass percent, zinc (Zn): 1-3%; aluminum (Al): 1-3%; calcium (Ca): 0.1-0.4%; gadolinium (Gd): 0.1-0.4%; yttrium (Y): 0-0.4%; manganese (Mn): 0-0.2%; and balance magnesium (Mg).

A calcium-bearing magnesium and rare earth element alloy consists essentially of, in mass percent, zinc (Zn): 1-3%; aluminum (Al): 1-3%; calcium (Ca): 0.1-0.4%; gadolinium (Gd): 0.1-0.4%; yttrium (Y): 0-0.4%; manganese (Mn): 0-0.2%; and balance magnesium (Mg).

A description is given of a method and a device for forging a rod-shaped workpiece (5) which is deformed with the aid of forging tools (1, 2, 3, 4) in the sense of a cross-sectional displacement perpendicular to the forging axis (a) and is subjected to an axial advancement and possibly a rotation about the forging axis (a) during the pauses in the engagement of the forging tools (1, 2, 3, 4). In order to achieve an advantageous grain refinement, it is proposed that the workpiece (5) is deformed in the sense of the cross-sectional displacement perpendicular to the forging axis (a) in a bending zone (13) between two central supports (11) by means of the forging tools (1, 2, 3, 4) acting on the workpiece (5) radially in relation to the forging axis (a).

A constructing-and-forging method for preparing homogenized forged pieces comprises: preparing preformed billets: cutting off a plurality of continuous casting billets, milling and smoothing surfaces of the billets to be welded, performing vacuum plasma cleaning operation to the surfaces to be welded, stacking the plurality of billets and sealing around the surfaces in a vacuum chamber by electron beam welding; forge-welding and homogenizing the preformed billets: heating the preformed billets to a certain temperature in a heating furnace and taking the heated preformed billets out of the heating furnace, forging the preformed billets by a hydraulic press, then using three-dimensional forging to disperse the welded surfaces such that composition, structure and inclusion of the interface areas are at the same level as those of the bodies of the billets. Cheap continuous casting billets are stacked and forge welded.

A constructing-and-forging method for preparing homogenized forged pieces comprises: preparing preformed billets: cutting off a plurality of continuous casting billets, milling and smoothing surfaces of the billets to be welded, performing vacuum plasma cleaning operation to the surfaces to be welded, stacking the plurality of billets and sealing around the surfaces in a vacuum chamber by electron beam welding; forge-welding and homogenizing the preformed billets: heating the preformed billets to a certain temperature in a heating furnace and taking the heated preformed billets out of the heating furnace, forging the preformed billets by a hydraulic press, then using three-dimensional forging to disperse the welded surfaces such that composition, structure and inclusion of the interface areas are at the same level as those of the bodies of the billets. Cheap continuous casting billets are stacked and forge welded.

Methods of refining the grain size of titanium and titanium alloys include multiple upset and draw forging. Titanium and titanium alloy workpieces are heated to a workpiece forging temperature within a workpiece forging temperature range in the alpha+beta phase field. The workpiece may comprise a starting cross-sectional dimension. The workpiece is upset forged in the workpiece forging temperature range. After upsetting, the workpiece is multiple pass draw forged in the workpiece forging temperature range. Multiple pass draw forging may comprise incrementally rotating the workpiece in a rotational direction followed by draw forging the workpiece after each incremental rotation. Incrementally rotating and draw forging the workpiece is repeated until the workpiece comprises substantially the same starting cross-sectional dimension.

A constructing-and-forging method for preparing homogenized forged pieces comprises: preparing preformed billets: cutting off a plurality of continuous casting billets, milling and smoothing surfaces of the billets to be welded, performing vacuum plasma cleaning operation to the surfaces to be welded, stacking the plurality of billets and sealing around the surfaces in a vacuum chamber by electron beam welding; forge-welding and homogenizing the preformed billets: heating the preformed billets to a certain temperature in a heating furnace and taking the heated preformed billets out of the heating furnace, forging the preformed billets by a hydraulic press, then using three-dimensional forging to disperse the welded surfaces such that composition, structure and inclusion of the interface areas are at the same level as those of the bodies of the billets. Cheap continuous casting billets are stacked and forge welded.

A constructing-and-forging method for preparing homogenized forged pieces comprises: preparing preformed billets: cutting off a plurality of continuous casting billets, milling and smoothing surfaces of the billets to be welded, performing vacuum plasma cleaning operation to the surfaces to be welded, stacking the plurality of billets and sealing around the surfaces in a vacuum chamber by electron beam welding; forge-welding and homogenizing the preformed billets: heating the preformed billets to a certain temperature in a heating furnace and taking the heated preformed billets out of the heating furnace, forging the preformed billets by a hydraulic press, then using three-dimensional forging to disperse the welded surfaces such that composition, structure and inclusion of the interface areas are at the same level as those of the bodies of the billets. Cheap continuous casting billets are stacked and forge welded.