A chemical regeneration method of water glass used sand, which belongs to the field of resource recycling in the casting industry. The present invention adopts a two-component reagent composed of calcium oxide and tap water, an emulsion composed of sucrose and calcium oxide, and a calcium chloride aqueous solution to process the regeneration of the used sand, and prepares the sample of the reclaimed sand obtained after the reagent mixed with the used sand is sealed and placed for 0 to 24 hours respectively, and tests the properties of the sample including: initial strength, final strength and collapsibility, and sodium carbonate content, and compares the properties of raw sand and used sand after the tests. Among several regeneration methods, each property index of the reclaimed sand obtained by using calcium oxide and tap water to regenerate for 12 hours is the best.

A chemical regeneration method of water glass used sand, which belongs to the field of resource recycling in the casting industry. The present invention adopts a two-component reagent composed of calcium oxide and tap water, an emulsion composed of sucrose and calcium oxide, and a calcium chloride aqueous solution to process the regeneration of the used sand, and prepares the sample of the reclaimed sand obtained after the reagent mixed with the used sand is sealed and placed for 0 to 24 hours respectively, and tests the properties of the sample including: initial strength, final strength and collapsibility, and sodium carbonate content, and compares the properties of raw sand and used sand after the tests. Among several regeneration methods, each property index of the reclaimed sand obtained by using calcium oxide and tap water to regenerate for 12 hours is the best.

A casting slurry for the manufacture of shell molds, including powder particles and a binder, further including a surfactant. Use of such a casting slurry for the manufacture of a shell mold.

A casting slurry for the manufacture of shell molds, including powder particles and a binder, further including a surfactant. Use of such a casting slurry for the manufacture of a shell mold.

The present invention relates to a casting mold for casting components. The casting mold comprises at least one casting mold frame made of metal and/or of an alloy, and also one or more ceramic casting mold inserts introduced into the at least one casting mold frame. The casting mold insert or the casting mold inserts has/have the negative contour or part of the negative contour of a component to be produced or of the combination of a component to be produced with one or more casting cores. The present invention also relates to a method for producing the casting mold according to the invention and to the use of the casting mold according to the invention.

What are described is a process for producing casting molds, cores and mold base materials regenerated therefrom, a mixture for combination with a solution or dispersion comprising waterglass for production of casting molds and/or cores, a molding material mixture, a mold base material mixture, and a casting mold or a core. What is also described is the corresponding use of an amount of particulate sheet silicates having a d.sub.90 of less than 45 μm or a corresponding mixture as additive for production of a molding material mixture comprising waterglass and particulate amorphous silicon dioxide, which is cured by chemical reaction of constituents of the molding material mixture with one another, in the production of a casting mold or a core, to facilitate the breakdown and/or to increase the regeneratability of the casting mold or core.

What are described is a process for producing casting molds, cores and mold base materials regenerated therefrom, a mixture for combination with a solution or dispersion comprising waterglass for production of casting molds and/or cores, a molding material mixture, a mold base material mixture, and a casting mold or a core. What is also described is the corresponding use of an amount of particulate sheet silicates having a d.sub.90 of less than 45 μm or a corresponding mixture as additive for production of a molding material mixture comprising waterglass and particulate amorphous silicon dioxide, which is cured by chemical reaction of constituents of the molding material mixture with one another, in the production of a casting mold or a core, to facilitate the breakdown and/or to increase the regeneratability of the casting mold or core.

A composition for making a core for use in a moulding or casting process, a core comprising said composition, and a mould for producing an article by high pressure die casting or semi-solid casting. The composition comprises a particulate refractory material, a binder composition comprising at least one hydrophilic polymer, comprising at least one polysaccharide or polysaccharide derivative; and at least one pozzolanic additive. The mould comprises a core for defining an internal cavity of the article and the core comprises a solidified core composition. The solidified core composition comprises a particulate refractory material and a binder composition, degrades in water such that a cylinder of the solidified core composition having a maximum height of 80 mm and a maximum diameter of 50 mm disintegrates in no more than 10 minutes when immersed in water at a temperature of 20° C. and stirred at a speed of 60 rpm, and has a flexural strength of at least 300 N/cm.sup.2. The invention also resides in a method for producing an article by high pressure die casting or semi-solid casting.

A composition for making a core for use in a moulding or casting process, a core comprising said composition, and a mould for producing an article by high pressure die casting or semi-solid casting. The composition comprises a particulate refractory material, a binder composition comprising at least one hydrophilic polymer, comprising at least one polysaccharide or polysaccharide derivative; and at least one pozzolanic additive. The mould comprises a core for defining an internal cavity of the article and the core comprises a solidified core composition. The solidified core composition comprises a particulate refractory material and a binder composition, degrades in water such that a cylinder of the solidified core composition having a maximum height of 80 mm and a maximum diameter of 50 mm disintegrates in no more than 10 minutes when immersed in water at a temperature of 20° C. and stirred at a speed of 60 rpm, and has a flexural strength of at least 300 N/cm.sup.2. The invention also resides in a method for producing an article by high pressure die casting or semi-solid casting.

An expandable aggregate mixture for a mold, which contains an aggregate, a water-soluble binder, a water-soluble foaming agent, water, and spherical metal oxide particles.