A casting method includes preparing a thin shell mold which is sintered and placed in a box. Sands are buried in the box to encompass the thin shell mold. The pressure chamber is depressurized. The casting material is filled into the thin shell mold, such that the thin shell mold is disposed at a vacuum state. Then, the negative pressure of the pressure chamber is released. Then, the pressure chamber is pressurized, to form a pressure difference which presses the casting material to flow into the thin shell mold, thereby finishing the casting work. The temperature of the casting material is reduced, and the pressure in the pressure chamber is increased. Then, the casting material is cooled to form a casting product. Then, the thin shell mold is broken, and the casting product is removed.

A casting method includes preparing a thin shell mold which is sintered and placed in a box. Sands are buried in the box to encompass the thin shell mold. The pressure chamber is depressurized. The casting material is filled into the thin shell mold, such that the thin shell mold is disposed at a vacuum state. Then, the negative pressure of the pressure chamber is released. Then, the pressure chamber is pressurized, to form a pressure difference which presses the casting material to flow into the thin shell mold, thereby finishing the casting work. The temperature of the casting material is reduced, and the pressure in the pressure chamber is increased. Then, the casting material is cooled to form a casting product. Then, the thin shell mold is broken, and the casting product is removed.

A method (S) for manufacturing a part (1) out of a metal matrix composite material, including the following steps: opening (S1) a device (10) that includes a supporting portion (14) and a molding portion (14); placing (S2) a fibrous reinforcement into the device (10); sealably closing (S3) the device (10) by providing a space between the fibrous reinforcement (2) and the device portions; feeding (S4) the molten metal matrix (3) into the device (10) such as to fill the space between the fibrous reinforcement (2) and the device portions (13, 14); and applying (S5) a force onto the equipment (10) such as to impregnate the fibrous reinforcement (2) with the metal matrix (3).

A method (S) for manufacturing a part (1) out of a metal matrix composite material, including the following steps: opening (S1) a device (10) that includes a supporting portion (14) and a molding portion (14); placing (S2) a fibrous reinforcement into the device (10); sealably closing (S3) the device (10) by providing a space between the fibrous reinforcement (2) and the device portions; feeding (S4) the molten metal matrix (3) into the device (10) such as to fill the space between the fibrous reinforcement (2) and the device portions (13, 14); and applying (S5) a force onto the equipment (10) such as to impregnate the fibrous reinforcement (2) with the metal matrix (3).

The casting of metals or salt and products made by casting metals or salts are described. For example, a method for casting metals or salts includes evacuating a mold that is pressurized with an inert gas and coupled to a pressurized source of molten metal or salt, wherein the pressurization of the source is sufficiently high to drive the molten metal or salt into the mold in response to the evacuation.

A method for vacuum smelting and variable pressure solidification forming aluminum alloy piece with ultra-thin wall and high gas tightness is provided, in which an induction heating furnace is set in a vacuum tank, a quartz crucible with thickness of 58 mm is used; a preheated aluminum alloy ingot is placed in the crucible, side doors of the tank is closed, and a vacuuming processing is performed for the tank; the melt is filled from the bottom layer of the casting; when the melt reaches to the top, the main valve and the air-release valve are turned on until the inside and outside pressures are consistent, and then the casting is taken out. The requirement of high air tightness for vacuum tank is reduced, and aluminum alloy casting with high quality can be obtained at lower cost.

A method for vacuum smelting and variable pressure solidification forming aluminum alloy piece with ultra-thin wall and high gas tightness is provided, in which an induction heating furnace is set in a vacuum tank, a quartz crucible with thickness of 58 mm is used; a preheated aluminum alloy ingot is placed in the crucible, side doors of the tank is closed, and a vacuuming processing is performed for the tank; the melt is filled from the bottom layer of the casting; when the melt reaches to the top, the main valve and the air-release valve are turned on until the inside and outside pressures are consistent, and then the casting is taken out. The requirement of high air tightness for vacuum tank is reduced, and aluminum alloy casting with high quality can be obtained at lower cost.

The invention relates to a method for producing a vehicle wheel from a light-metal material, in which the light-metal material is introduced in liquid form into a mold cavity of a casting mold. The vehicle wheel is produced by means of pressurized casting, wherein the casting mold is temperature-controlled in different regions to different temperatures.

A continuous precision forming device and process for an amorphous alloy is provided. By means of the device, when a melting platform with an alloy melt is rotated from the melting position to a position just below the forming mould (9), temperature of the alloy melt can be in the range of the overcooled liquid zone temperature of the alloy melt, and then a loading rod (7) drives the forming mould (9) to proceed with pressing forming. According to the process, press-forming is carried out in a certain temperature interval in the amorphous alloy melt solidification process, and the heating, cooling, solidification and forming in the forming process are coordinated, such that continuous forming of the amorphous alloy is achieved.

A continuous precision forming device and process for an amorphous alloy is provided. By means of the device, when a melting platform with an alloy melt is rotated from the melting position to a position just below the forming mould (9), temperature of the alloy melt can be in the range of the overcooled liquid zone temperature of the alloy melt, and then a loading rod (7) drives the forming mould (9) to proceed with pressing forming. According to the process, press-forming is carried out in a certain temperature interval in the amorphous alloy melt solidification process, and the heating, cooling, solidification and forming in the forming process are coordinated, such that continuous forming of the amorphous alloy is achieved.