Magnetic copper-nickel-tin-manganese alloys are disclosed. Also disclosed are processing steps that can be performed for maintaining and/or changing various magnetic or mechanical properties of the alloys. Further described herein are methods for using such an alloy, including various articles produced therefrom.

A casting method includes: forming a seed, the seed having a first end and a second end, the forming including bending a seed precursor; placing the seed second end in contact or spaced facing relation with a chill plate; contacting the first end with molten material; and cooling and solidifying the molten material so that a crystalline structure of the seed propagates into the solidifying material. The forming further included reducing a thickness of the seed proximate the first end relative to a thickness of the seed proximate the second end.

A method for producing a metal film from an over 50% nickel alloy melts more than one ton of the alloy in a furnace, followed by VOD or VLF system treatment, then pouring off to form a pre-product, followed by re-melting by VAR and/or ESU. The pre-product is annealed 1-300 hours between 800 and 1350 C. under air or protection gas, then hot-formed between 1300 and 600 C., such that the pre-product then has 1-100 mm thickness after the forming and is not recrystallized, recovered, and/or (dynamically) recrystallized having a grain size below 300 m. The pre-product is pickled, then cold-formed to produce a film having 10-600 m end thickness and a deformation ratio greater than 90%. The film is cut into 5-300 mm strips, annealed 1 second to 5 hours under protection gas between 600 and 1200 C. in a continuous furnace, then recrystallized to have a high cubic texture proportion.

It is an objective of the invention to provide a Ni-based superalloy cast article exhibiting the corrosion resistance compatible or superior to the conventional ordinary precision cast articles and reducing the cost than the conventional ones while maintaining the mechanical properties compatible to the conventional ones. There is provided a Ni-based superalloy cast article including: 12.1 to 16 mass % of Cr; 4 to 16 mass % of Co; 3 to 5 mass % of Al; 2.1 to 3.3 mass % of Ti; 3.5 to 9 mass % of W; 1 to 2.4 mass % of Mo; 1.2 mass % or less of Nb; 0.005 to 0.05 mass % of B; 0.03 to 0.2 mass % of C; more than 0 mass % and 0.005 mass % or less of O; and the balance being Ni and impurities.

A method for producing cast items in a casting method, wherein a charge of a conductive material is introduced into the sphere of influence of at least one alternating electromagnetic field, so that the charge is kept in a levitating state. The melt is poured into moulds in order to produce turbine blades, prostheses or turbocharger impellers.

A method for producing cast items in a casting method, wherein a charge of a conductive material is introduced into the sphere of influence of at least one alternating electromagnetic field, so that the charge is kept in a levitating state. The melt is poured into moulds in order to produce turbine blades, prostheses or turbocharger impellers.

The present invention relates to an alloy which has the following composition:

Cu.sub.47 at %(x+y+z)(Ti.sub.aZr.sub.b).sub.cNi.sub.7 at %+xSn.sub.1 at %+ySi.sub.z

where
c=43-47 at %, a=0.65-0.85, b=0.15-0.35, where a+b=1.00;
x=0-7 at %;
y=0-3 at %, z=0-3 at %, where y+z4 at %.

A casting method for titanium and titanium alloys, the casting method including obtaining an investment casting mold composition having calcium aluminate and aluminum oxide, the calcium aluminate combined with a liquid to produce a slurry of calcium aluminate, and wherein the solids in the final calcium aluminate/liquid mixture with large scale alumina is about 71% to about 90%. The method further includes pouring the investment casting mold composition into a vessel containing a fugitive pattern, curing the investment casting mold composition to form a mold, removing the fugitive pattern from the mold, firing the mold, preheating the mold to a mold casting temperature, pouring molten titanium or titanium alloy into the preheated mold, solidifying the molten titanium or titanium alloy and forming a solidified titanium or titanium alloy casting, and removing the solidified titanium or titanium alloy casting from the mold.

An advantage of the invention is to provide a master alloy used in a casting of a modified copper alloy, grains of which can be refined during a melt-solidification, and also a method of casting a modified copper alloy using the same.

In order to achieve the advantage, master alloy for casting a copper alloy in a form of Cu: 40 to 80%, Zr: 0.5 to 35% and the balance of Zn; and Cu: 40 to 80%, Zr: 0.5 to 35%, P: 0.01 to 3% and the balance of Zn are used, and thus grain-refined copper alloy casting products are obtained.

The invention relates to the foundry field, and in particular to a foundry process comprising the preheating of a mold (1) up to a first temperature, the casting of a metal in the liquid state, at a second temperature above the first temperature, in the mold kept in a main furnace (100) at the first temperature since the preheating, the difference between the first temperature and second temperature being no more than 80 C., the cooling and solidification of the metal in the mold (1) kept in the main furnace (100) at a pressure of less than 0.1 Pa at least since the casting, the removal of the mold (1) from the main furnace (100), and the demolding of the solidified metal.