A casting method of an active metal includes, in an induction melting furnace using a water-cooled crucible, tapping a molten metal into a mold from a tapping hole provided at a bottom of the water-cooled copper crucible to cast an ingot of the active metal. In conducting the casting under a casting condition in which the ingot has a diameter (D) of 10 mm or more and a ratio (H/D) of an ingot height H to the ingot diameter D of 1.5 or more and a weight of the molten metal tapped in the casting is 200 kg or less, a temperature of the molten metal in the casting is set to be higher than the melting point of the active metal and a casting velocity V (mm/sec) is controlled to satisfy V0.1H in relation with the ingot height H by adjusting an opening diameter of the tapping hole.

A casting method of an active metal includes, in an induction melting furnace using a water-cooled crucible, tapping a molten metal into a mold from a tapping hole provided at a bottom of the water-cooled copper crucible to cast an ingot of the active metal. In conducting the casting under a casting condition in which the ingot has a diameter (D) of 10 mm or more and a ratio (H/D) of an ingot height H to the ingot diameter D of 1.5 or more and a weight of the molten metal tapped in the casting is 200 kg or less, a temperature of the molten metal in the casting is set to be higher than the melting point of the active metal and a casting velocity V (mm/sec) is controlled to satisfy V0.1H in relation with the ingot height H by adjusting an opening diameter of the tapping hole.

A molding machine cylinder comprising a lining layer having a structure comprising 20-50% by area of tungsten carbide particles and 1-10% by area of tungsten-based metal carboboride particles in a nickel-based alloy matrix, and containing 1-7.5% by mass of Fe, can be produced by a centrifugal casting method comprising a first step of heating at higher than 1140 C. and lower than 1200 C., and a second step of heating at 1080-1140 C. after melting the raw material powder.

A molding machine cylinder comprising a lining layer having a structure comprising 20-50% by area of tungsten carbide particles and 1-10% by area of tungsten-based metal carboboride particles in a nickel-based alloy matrix, and containing 1-7.5% by mass of Fe, can be produced by a centrifugal casting method comprising a first step of heating at higher than 1140 C. and lower than 1200 C., and a second step of heating at 1080-1140 C. after melting the raw material powder.

Provided is a titanium cast product made of commercially pure titanium, the titanium cast product being produced by electron-beam remelting or plasma arc melting, comprising: a melted and resolidified layer in a range of 1 mm or more in depth at a surface serving as a surface to be rolled, the melted and resolidified layer being obtained by adding one or more kinds of stabilizer elements to the surface and melting and resolidifying the surface. An average value of stabilizer element(s) concentration in a range of within 1 mm in depth is higher than stabilizer element(s) concentration in a base material by, in mass %, equal to or more than 0.08 mass % and equal to or less than 1.50 mass %. As the material containing the stabilizer element, powder, a chip, wire, or foil is used. As means for melting a surface layer, electron-beam heating and plasma arc heating are used.

Provided is a titanium cast product made of commercially pure titanium, the titanium cast product being produced by electron-beam remelting or plasma arc melting, comprising: a melted and resolidified layer in a range of 1 mm or more in depth at a surface serving as a surface to be rolled, the melted and resolidified layer being obtained by adding one or more kinds of stabilizer elements to the surface and melting and resolidifying the surface. An average value of stabilizer element(s) concentration in a range of within 1 mm in depth is higher than stabilizer element(s) concentration in a base material by, in mass %, equal to or more than 0.08 mass % and equal to or less than 1.50 mass %. As the material containing the stabilizer element, powder, a chip, wire, or foil is used. As means for melting a surface layer, electron-beam heating and plasma arc heating are used.

Disclosed herein are aluminum alloys with scandium as the alloying element. The alloys have a high scandium content, as measured by atomic percentage, and are highly uniform, as described herein. Methods of forming articles from these alloys are also disclosed, such articles including sputtering targets that can be used to form thin films containing high amounts of scandium.

A molding machine cylinder comprising a lining layer having a structure comprising 20-50% by area of tungsten carbide particles and 1-10% by area of tungsten-based metal carboboride particles in a nickel-based alloy matrix, and containing 1-7.5% by mass of Fe, can be produced by a centrifugal casting method comprising a first step of heating at higher than 1140 C. and lower than 1200 C., and a second step of heating at 1080-1140 C. after melting the raw material powder.

A molding machine cylinder comprising a lining layer having a structure comprising 20-50% by area of tungsten carbide particles and 1-10% by area of tungsten-based metal carboboride particles in a nickel-based alloy matrix, and containing 1-7.5% by mass of Fe, can be produced by a centrifugal casting method comprising a first step of heating at higher than 1140 C. and lower than 1200 C., and a second step of heating at 1080-1140 C. after melting the raw material powder.

A NiTi-based alloy material includes a matrix phase consisting essentially of a NiTi-based alloy and having a B2 type crystal structure. A nonmetallic inclusion is present in the matrix phase, in which 99% by mass or more of the nonmetallic inclusion is a TiC-based inclusion having a NaCl type crystal structure, the TiC-based inclusion has a lattice misfit (?) in a range of 0.4238 or more and 0.4259 or less. The lattice misfit (?) is represented by Expression ?=(a1?a2)/a2, where a1 is a lattice constant (?) of the TiC-based inclusion and a2 is a lattice constant (?) of the matrix phase.