The disclosure relates to a powdery filament composition for 3D printing, a 3D printer, and a method of additively manufacturing an object by the 3D printer, and more particularly to a powdery filament composition for 3D printing, which is suitable for home use because it does not produce toxic substances, a 3D printer, the size of which is suitable for home use because it does not require high power energy, high-temperature processing and the like conditions for additive manufacturing, and a method of additively manufacturing an object by the 3D printer.

A material for producing a three-dimensionally printed part including a metal material and at least one sintering aid in an amount effective to give the three-dimensionally printed part a density of between about 90% and about 100% after sintering is disclosed. A method of printing a three-dimensional part including selecting a metal material, incorporating at least one sintering aid into the metal material to form a print material, and printing the three-dimensional part is also disclosed. A method of producing a sintered metal part including providing a metal material for the sintered metal part incorporating boron as a first sintering aid, incorporating phosphorus as a second sintering aid, forming the metal part in a predetermined form the metal material, and heating the formed metal part to a sintering temperature is also disclosed. Three-dimensionally printed parts are also disclosed.

A material for producing a three-dimensionally printed part including a metal material and at least one sintering aid in an amount effective to give the three-dimensionally printed part a density of between about 90% and about 100% after sintering is disclosed. A method of printing a three-dimensional part including selecting a metal material, incorporating at least one sintering aid into the metal material to form a print material, and printing the three-dimensional part is also disclosed. A method of producing a sintered metal part including providing a metal material for the sintered metal part incorporating boron as a first sintering aid, incorporating phosphorus as a second sintering aid, forming the metal part in a predetermined form the metal material, and heating the formed metal part to a sintering temperature is also disclosed. Three-dimensionally printed parts are also disclosed.

A soft magnetic composite comprising an iron or iron alloy ferromagnetic material coated with an oxide material. An interface between the ferromagnetic material and the layer of oxide contains antiphase domain boundaries. Two processes for producing a soft magnetic composite are also provided. One process includes depositing an oxide layer onto an iron or iron alloy ferromagnetic material by molecular beam epitaxy at a partial oxygen pressure of from 1×10.sup.−5 Torr to 1×10.sup.−7 Torr to form a coated composite. The other process includes milling an iron or iron alloy ferromagnetic material powder and an oxide powder by high-energy milling to form a mixture; compacting the mixture and curing in an inert gas atmosphere at a temperature from 500° C. to 1200° C. to form a soft magnetic composite.

A soft magnetic composite comprising an iron or iron alloy ferromagnetic material coated with an oxide material. An interface between the ferromagnetic material and the layer of oxide contains antiphase domain boundaries. Two processes for producing a soft magnetic composite are also provided. One process includes depositing an oxide layer onto an iron or iron alloy ferromagnetic material by molecular beam epitaxy at a partial oxygen pressure of from 1×10.sup.−5 Torr to 1×10.sup.−7 Torr to form a coated composite. The other process includes milling an iron or iron alloy ferromagnetic material powder and an oxide powder by high-energy milling to form a mixture; compacting the mixture and curing in an inert gas atmosphere at a temperature from 500° C. to 1200° C. to form a soft magnetic composite.

A method of producing nanoscale materials comprising the steps of entraining liquid droplets containing at least one nanoparticle precursor within a gaseous stream, and passing said gaseous stream containing said liquid droplets through a non-thermal equilibrium plasma whereby said plasma interacts with said at least one nanoparticle precursor to produce nanoparticles within said droplets without substantial evaporation of the droplets and conveying the thus produced nanoparticles within said gaseous stream downstream of said plasma.

A method of producing nanoscale materials comprising the steps of entraining liquid droplets containing at least one nanoparticle precursor within a gaseous stream, and passing said gaseous stream containing said liquid droplets through a non-thermal equilibrium plasma whereby said plasma interacts with said at least one nanoparticle precursor to produce nanoparticles within said droplets without substantial evaporation of the droplets and conveying the thus produced nanoparticles within said gaseous stream downstream of said plasma.

A powder production method includes providing an elongated workpiece and repeatedly contacting an outer surface of the elongated workpiece with a reciprocating cutter according to a predetermined at least one frequency to produce a powder. The powder includes a plurality of particles, wherein at least 95% of the produced particles have a diameter or maximum dimension ranging from about 10 μm to about 200 μm. A system for producing powders having a plurality of particles including a cutter and at least one controller is also provided herein.

A powder production method includes providing an elongated workpiece and repeatedly contacting an outer surface of the elongated workpiece with a reciprocating cutter according to a predetermined at least one frequency to produce a powder. The powder includes a plurality of particles, wherein at least 95% of the produced particles have a diameter or maximum dimension ranging from about 10 μm to about 200 μm. A system for producing powders having a plurality of particles including a cutter and at least one controller is also provided herein.

A high saturation, low loss magnetic material suitable for high frequency electrical devices, including power converters, transformers, solenoids, motors, and other such devices.