An example of a composition includes a host metal present in an amount ranging from about 95.00 weight percent to about 99.99 weight percent, based on a total weight of the composition. A flow additive is present in an amount ranging from about 0.01 weight percent to about 5.00 weight percent, based on the total weight of the composition. The flow additive consists of a metal containing compound that is reducible to an elemental metal in a reducing environment at a reducing temperature less than or equal to a sintering temperature of the host metal. The elemental metal is capable of being incorporated into a bulk metal phase of the host metal in a final metal object. The composition is spreadable, having a Hausner Ratio less than 1.25.

An example of a composition includes a host metal present in an amount ranging from about 95.00 weight percent to about 99.99 weight percent, based on a total weight of the composition. A flow additive is present in an amount ranging from about 0.01 weight percent to about 5.00 weight percent, based on the total weight of the composition. The flow additive consists of a metal containing compound that is reducible to an elemental metal in a reducing environment at a reducing temperature less than or equal to a sintering temperature of the host metal. The elemental metal is capable of being incorporated into a bulk metal phase of the host metal in a final metal object. The composition is spreadable, having a Hausner Ratio less than 1.25.

A 3D printing module to remove un-solidified build material attached to a 3D printed part is disclosed herein. The 3D printing module comprises a platform within a housing to support a 3D printed part, a vibrating mechanism to vibrate the platform, a cleaning element to apply a cleaning stream within the housing to clean the 3D printed part, and a controller. The controller is to vibrate the platform, generate a cleaning stream in the housing, and to control at least one of the platform and the cleaning element to apply the cleaning stream to different portions of a 3D printed part on the platform.

A 3D printing module to remove un-solidified build material attached to a 3D printed part is disclosed herein. The 3D printing module comprises a platform within a housing to support a 3D printed part, a vibrating mechanism to vibrate the platform, a cleaning element to apply a cleaning stream within the housing to clean the 3D printed part, and a controller. The controller is to vibrate the platform, generate a cleaning stream in the housing, and to control at least one of the platform and the cleaning element to apply the cleaning stream to different portions of a 3D printed part on the platform.

Disclosed are interfacially modified metal particulate composite materials for use in powder metallurgy sintered products and processes.

Disclosed are interfacially modified metal particulate composite materials for use in powder metallurgy sintered products and processes.

The present disclosure relates to a method of three-dimensional (3D) printing a 3D printed object. The method comprises: selectively jetting a marking agent onto a first region of build material, wherein the build material comprises at least one meta and/or ceramic; selectively jetting a binding agent onto at least a portion of the build material; and binding the build material to form a layer; such that the marking agent is incorporated in the metal part in a predetermined arrangement that forms a detectable marker in the 3D printed object. The disclosure also relates to a multi-fluid inkjet kit for 3D printing.

The present disclosure relates to a method of three-dimensional (3D) printing a 3D printed object. The method comprises: selectively jetting a marking agent onto a first region of build material, wherein the build material comprises at least one meta and/or ceramic; selectively jetting a binding agent onto at least a portion of the build material; and binding the build material to form a layer; such that the marking agent is incorporated in the metal part in a predetermined arrangement that forms a detectable marker in the 3D printed object. The disclosure also relates to a multi-fluid inkjet kit for 3D printing.

An example of a method, for three-dimensional (3D) printing, includes applying a build material and patterning at least a portion of the build material. The patterning includes selectively applying a wetting amount of a binder fluid on the at least the portion of the build material and subsequently selectively applying a remaining amount of the binder fluid on the at least the portion of the build material. An area density in grams per meter square meter (gsm) of the wetting amount ranges from about 2 times less to about 30 times less than area density in gsm of the remaining amount.

An example of a method, for three-dimensional (3D) printing, includes applying a build material and patterning at least a portion of the build material. The patterning includes selectively applying a wetting amount of a binder fluid on the at least the portion of the build material and subsequently selectively applying a remaining amount of the binder fluid on the at least the portion of the build material. An area density in grams per meter square meter (gsm) of the wetting amount ranges from about 2 times less to about 30 times less than area density in gsm of the remaining amount.