There is provided a method of treating a nickel base super alloy (NiSa) article. First, the NiSa article having fine grains is obtained. The NiSa article has a uniform distribution of the fine grains and substantially uniform mechanical properties throughout. One or more regions within the NiSa article are mechanically deformed. Then, the NiSa article is heat treated to obtain coarse grains in the one or more regions, the coarse grains having a size that is larger than that of the fine grains of the NiSa article outside of the one or more regions.

A powder metal composition for high wear and temperature applications is made by atomizing a melted iron based alloy including 3.0 to 7.0 wt. % carbon; 10.0 to 25.0 wt. % chromium; 1.0 to 5.0 wt. % tungsten; 3.5 to 7.0 wt. % vanadium; 1.0 to 5.0 wt. % molybdenum; not greater than 0.5 wt. % oxygen; and at least 40.0 wt. % iron. The high carbon content reduces the solubility of oxygen in the melt and thus lowers the oxygen content to a level below which would cause the carbide-forming elements to oxidize during atomization. The powder metal composition includes metal carbides in an amount of at least 15 vol. %. The microhardness of the powder metal composition increases with increasing amounts of carbon and is typically about 800 to 1,500 Hv50.

A powder metal composition for high wear and temperature applications is made by atomizing a melted iron based alloy including 3.0 to 7.0 wt. % carbon; 10.0 to 25.0 wt. % chromium; 1.0 to 5.0 wt. % tungsten; 3.5 to 7.0 wt. % vanadium; 1.0 to 5.0 wt. % molybdenum; not greater than 0.5 wt. % oxygen; and at least 40.0 wt. % iron. The high carbon content reduces the solubility of oxygen in the melt and thus lowers the oxygen content to a level below which would cause the carbide-forming elements to oxidize during atomization. The powder metal composition includes metal carbides in an amount of at least 15 vol. %. The microhardness of the powder metal composition increases with increasing amounts of carbon and is typically about 800 to 1,500 Hv50.

This invention aims at providing a carbon-coated metal powder having few impurities, a narrower particle size distribution, and sintering properties particularly suitable as a conductive powder of a conductive paste for forming internal conductors in a ceramic multilayer electronic component obtained by co-firing multilayered ceramic sheets and internal conductor layers; a conductive paste containing the carbon-coated metal powder; a multilayer electronic component using the conductive paste; and a method for manufacturing the carbon-coated metal powder. The carbon-coated metal powder has specific properties in TMA or ESCA measurements. The carbon-coated metal powder can be obtained by melting and vaporizing a metallic raw material in a reaction vessel, conveying the generated metal vapor into a cooling tube and rapidly cooling the metal vapor by endothermically decomposing a carbon source supplied into the cooling tube, and forming a carbon coating film on metal nuclei surfaces in parallel with generation of the metal nuclei.

This invention aims at providing a carbon-coated metal powder having few impurities, a narrower particle size distribution, and sintering properties particularly suitable as a conductive powder of a conductive paste for forming internal conductors in a ceramic multilayer electronic component obtained by co-firing multilayered ceramic sheets and internal conductor layers; a conductive paste containing the carbon-coated metal powder; a multilayer electronic component using the conductive paste; and a method for manufacturing the carbon-coated metal powder. The carbon-coated metal powder has specific properties in TMA or ESCA measurements. The carbon-coated metal powder can be obtained by melting and vaporizing a metallic raw material in a reaction vessel, conveying the generated metal vapor into a cooling tube and rapidly cooling the metal vapor by endothermically decomposing a carbon source supplied into the cooling tube, and forming a carbon coating film on metal nuclei surfaces in parallel with generation of the metal nuclei.

Techniques are disclosed for milling an iron-containing raw material in the presence of a nitrogen source to generate anisotropically shaped particles that include iron nitride and have an aspect ratio of at least 1.4. Techniques for nitridizing an anisotropic particle including iron, and annealing an anisotropic particle including iron nitride to form at least one a″-Fe16N2 phase domain within the anisotropic particle including iron nitride also are disclosed. In addition, techniques for aligning and joining anisotropic particles to form a bulk material including iron nitride, such as a bulk permanent magnet including at least one a″-Fe16N2 phase domain, are described. Milling apparatuses utilizing elongated bars, an electric field, and a magnetic field also are disclosed.

Techniques are disclosed for milling an iron-containing raw material in the presence of a nitrogen source to generate anisotropically shaped particles that include iron nitride and have an aspect ratio of at least 1.4. Techniques for nitridizing an anisotropic particle including iron, and annealing an anisotropic particle including iron nitride to form at least one a″-Fe16N2 phase domain within the anisotropic particle including iron nitride also are disclosed. In addition, techniques for aligning and joining anisotropic particles to form a bulk material including iron nitride, such as a bulk permanent magnet including at least one a″-Fe16N2 phase domain, are described. Milling apparatuses utilizing elongated bars, an electric field, and a magnetic field also are disclosed.

A heat conductive paste including silver fine particles having an average particle diameter of primary particles of 40 to 350 nm, a crystallite diameter of 20 to 70 nm, and a ratio of the average particle diameter to the crystallite diameter of 1 to 5, an aliphatic primary amine and a compound having at least one phosphoric acid group. The heat conductive paste includes 1 to 40 parts by mass of the aliphatic primary amine and 0.001 to 2 parts by mass of the compound having at least one phosphoric acid group based on 100 parts by mass of the silver fine particles. The heat conductive paste has a high conductivity.

Zinc is added to a metal magnetic alloy powder including iron and silicon. An element is formed using this magnetic material, and a coil is formed inside or on the surface of the element.

Zinc is added to a metal magnetic alloy powder including iron and silicon. An element is formed using this magnetic material, and a coil is formed inside or on the surface of the element.