The invention provides a heat-shrinkable polyester-based film roll obtained by winding a heat-shrinkable polyester-based film with a shrinkage ratio of 30% or more in a film main shrinkage direction in hot water at 90° C. for 10 seconds. The film roll has a winding length of 2000-25000 m and a width of 400-2500 mm. The film has a thickness of 5-40 μm. In thickness unevenness in a width direction of the film on a surface layer of the film roll, there are positions having concave thickness patterns, and in a concave portion that has a maximum thickness difference (maximum concave portion), thickness unevenness in the maximum concave portion, which is obtained from the maximum thickness difference in the maximum concave portion and an average thickness of the film is 10% or less. The winding hardness of the surface layer of the film roll is 400-800.

The invention provides a heat-shrinkable polyester-based film roll obtained by winding a heat-shrinkable polyester-based film with a shrinkage ratio of 30% or more in a film main shrinkage direction in hot water at 90° C. for 10 seconds. The film roll has a winding length of 2000-25000 m and a width of 400-2500 mm. The film has a thickness of 5-40 μm. In thickness unevenness in a width direction of the film on a surface layer of the film roll, there are positions having concave thickness patterns, and in a concave portion that has a maximum thickness difference (maximum concave portion), thickness unevenness in the maximum concave portion, which is obtained from the maximum thickness difference in the maximum concave portion and an average thickness of the film is 10% or less. The winding hardness of the surface layer of the film roll is 400-800.

A film for coating a metal sheet, the film satisfying that: a ratio (E.sub.MD/E.sub.TD) of a Young's modulus E.sub.MD in a lengthwise direction to a Young's modulus E.sub.TD in a width direction is 1.1 to 4.0; and a thermal shrinkage rate, measured by a thermo-mechanical analyzer, in both lengthwise and width directions at 200° C. is equal to or smaller than 20%.

The present disclosure provides a dual layer heat shrink tube having: an inner polymeric layer with a thickness t.sub.1 and an outer diameter D.sub.1; and an outer, expanded polymeric layer with a thickness t.sub.2′ and an outer diameter D.sub.2′ obtained by expanding a polymer tube from D.sub.2 to D.sub.2′ and t.sub.2 to t.sub.2′ at a selected temperature so that D.sub.2′−2(t.sub.2′)>D.sub.1, wherein a ring cut from a cross-section of the dual layer heat shrink tube, slit into a rectangle and gripped at cut ends by tension grips within a DMA, and subjected to a temperature sweep of 3° C./min at a frequency of 1 Hz from the onset of a melting endotherm of the inner polymeric layer to that of the outer, expanded polymeric layer is greater than 1° C. and less than 12° C. The disclosure further provides associated methods for preparing and using such tubes, as well as to products comprising such tubes.

[PROBLEMS] It is an object of the present invention to provide a heat-shrinkable polyester-based film roll which can reduce defects caused during a heat shrinking step due to the variation of a heat shrinkage rate in the heat-shrinkable polyester-based film roll having the longitudinal direction as the main shrinkage direction, specifically, defects of the film when covering an object by a wrap-around method and heat-shrunk. [SOLUTIONS] A heat-shrinkable polyester-based film roll, comprising a core; and a heat-shrinkable polyester-based film having a longitudinal direction as a main shrinkage direction that is wound around the core; wherein the film (roll) satisfy predetermined polyester composition, and all samples cutout every about 100 m have a heat shrinkage rate measured by immersion in hot water of 90° C. for 10 seconds of 30% or more and 80% or less and ±3% or less of an average in the longitudinal direction.

[PROBLEMS] It is an object of the present invention to provide a heat-shrinkable polyester-based film roll which can reduce defects caused during a heat shrinking step due to the variation of a heat shrinkage rate in the heat-shrinkable polyester-based film roll having the longitudinal direction as the main shrinkage direction, specifically, defects of the film when covering an object by a wrap-around method and heat-shrunk. [SOLUTIONS] A heat-shrinkable polyester-based film roll, comprising a core; and a heat-shrinkable polyester-based film having a longitudinal direction as a main shrinkage direction that is wound around the core; wherein the film (roll) satisfy predetermined polyester composition, and all samples cutout every about 100 m have a heat shrinkage rate measured by immersion in hot water of 90° C. for 10 seconds of 30% or more and 80% or less and ±3% or less of an average in the longitudinal direction.

At least one infrared element arrangement having at least one infrared element (3) comprising a plurality of infrared radiators (4) is mounted on a frame moveable with respect to a synthetic filter fabric mounted to a filtering surface. The frame may have wheels or the like such that the infrared radiators may be moved along the length of the filtering surface to heat the synthetic filter fabric (6) to a temperature of 100 to 160° C. for shrinking the fabric (6) on the filtering surface (5).

At least one infrared element arrangement having at least one infrared element (3) comprising a plurality of infrared radiators (4) is mounted on a frame moveable with respect to a synthetic filter fabric mounted to a filtering surface. The frame may have wheels or the like such that the infrared radiators may be moved along the length of the filtering surface to heat the synthetic filter fabric (6) to a temperature of 100 to 160° C. for shrinking the fabric (6) on the filtering surface (5).

A process of heat shrinking an article is provided. The process includes shaping a thermoplastic vulcanizate (TPV) into an article, the TPV having: a partially vulcanized rubber dispersed in a continuous thermoplastic phase, wherein more than 5 wt % of the rubber is extractable in boiling xylene, and wherein the thermoplastic phase comprises a thermoplastic resin having a Tm>110° C. and a propylene-based elastomer (PBE) having a Tm<110° C.; and heating the article to a temperature between about 100° C. and 250° C. to shrink the article.

The embodiments relate to a heat shrinkable film and a process for regenerating a polyester container using the same. The heat shrinkable film comprises a copolymerized polyester resin comprising a diol component and a dicarboxylic acid component and has a heat shrinkage rate of 30% or more in the main shrinkage direction upon thermal treatment at a temperature of 80° C. for 10 seconds, a melting point of 190° C. or higher as measured by differential scanning calorimetry, and a peak temperature (Tp) of 95° C. to 115° C. as measured in the endothermic and exothermic curve (heat flow) by differential scanning calorimetry. It not only solves the environmental problem by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.