A ultrasonic welding method of joining dissimilar-material workpieces, such as sheet materials, and the joined components formed thereby. The method includes applying ultrasonic energy to a thermoplastic piece to fill a hole of a dissimilar piece to form a weld point that is made up with polymer from the thermoplastic piece. In general, the geometry of the thermoplastic piece is not altered during the process. The dissimilar piece generally has a higher melting temperate and can be metal, thermoset polymers, or other thermoplastic material. The welded pieces can be arranged in a lap, laminate, or double lap configuration. In some embodiments, the hole of the dissimilar sheet material includes undercut features that improve the mechanical interlock between the dissimilar pieces. In some embodiments, the weld point has a mushroom cap to improve mechanical interlock.

A ultrasonic welding method of joining dissimilar-material workpieces, such as sheet materials, and the joined components formed thereby. The method includes applying ultrasonic energy to a thermoplastic piece to fill a hole of a dissimilar piece to form a weld point that is made up with polymer from the thermoplastic piece. In general, the geometry of the thermoplastic piece is not altered during the process. The dissimilar piece generally has a higher melting temperate and can be metal, thermoset polymers, or other thermoplastic material. The welded pieces can be arranged in a lap, laminate, or double lap configuration. In some embodiments, the hole of the dissimilar sheet material includes undercut features that improve the mechanical interlock between the dissimilar pieces. In some embodiments, the weld point has a mushroom cap to improve mechanical interlock.

The disclosure relates to an alternative joining method and to the use of the shaped part produced by means of the alternative joining method in drive technology and connection technology.

The disclosure relates to an alternative joining method and to the use of the shaped part produced by means of the alternative joining method in drive technology and connection technology.

This invention relates to the production of cured polymeric skin materials. In particular, the invention relates to methods and substrates for the production of skin materials, for example, for use in building, furniture, and as architectural components for example in roofing materials such as roofing tiles, or for brick wall effect materials.

A golf club head includes a striking face, a crown and a sole. The crown and/or the sole includes an FRP member formed by a fiber reinforced plastic that contains a fiber and a matrix resin. The FRP member has an average flexural modulus of greater than or equal to 25 GPa. The fiber may contain a carbon fiber. The carbon fiber may have a tensile elastic modulus of greater than or equal to 300 GPa. The fiber may contain a metallic fiber. The FRP member may have a resin content of less than or equal to 40% by weight. The matrix resin may have a glass transition temperature of higher than or equal to 150 C.

A golf club head includes a striking face, a crown and a sole. The crown and/or the sole includes an FRP member formed by a fiber reinforced plastic that contains a fiber and a matrix resin. The FRP member has an average flexural modulus of greater than or equal to 25 GPa. The fiber may contain a carbon fiber. The carbon fiber may have a tensile elastic modulus of greater than or equal to 300 GPa. The fiber may contain a metallic fiber. The FRP member may have a resin content of less than or equal to 40% by weight. The matrix resin may have a glass transition temperature of higher than or equal to 150 C.

The present invention relates to vacuum forming process for moulding a thermoset material and a start-up process for moulding a thermoset material. The present invention also relates to articles produced by the vacuum forming process.

Making a carbon aerogel involves 3-D printing an ink to make a printed part, removing the solvent from the printed part, and carbonizing the printed part (with the solvent removed) to make the aerogel. The ink is based on a solution of a resorcinol-formaldehyde resin (RF resin), water, and an organic thickener. Advantageously, the RF resin contains an acid catalyst, which tends to produce carbon aerogels with higher surface areas upon activation than those produced from methods involving an ink composition containing a base catalyzed resin.

A golf club head includes a striking face, a crown and a sole. The crown and/or the sole includes an FRP member formed by a fiber reinforced plastic that contains a fiber and a matrix resin. The FRP member has an average flexural modulus of greater than or equal to 25 GPa. The fiber may contain a carbon fiber. The carbon fiber may have a tensile elastic modulus of greater than or equal to 300 GPa. The fiber may contain a metallic fiber. The FRP member may have a resin content of less than or equal to 40% by weight. The matrix resin may have a glass transition temperature of higher than or equal to 150 C.