The invention relates to a porous separation article having a fluoropolymer, polyamide, PEEK, or PEKK binder interconnecting one or more types of interactive powdery materials or fibers. The interconnectivity is such that the binder connects the powdery materials or fibers in discrete spots rather than as a complete coating, allowing the materials or fibers to be in direct contact with, and interact with a fluid. The resulting article is a formed multicomponent, interconnected web, with porosity. The separation article is useful in water purification, as well as in the separation of dissolved or suspended materials in both aqueous and non-aqueous systems in industrial uses. The separation article can function at ambient temperature, as well as at elevated temperatures.

The present disclosure relates to a method for forming a transport mechanism for transporting at least one of a gas or a liquid. The method may comprise using a 3D printing operation to form the mechanism with an inlet and an outlet, and controlling the 3D printing operation to create the mechanism as an engineered surface structure formed in a layer-by-layer process. The method may further comprise controlling the 3D printing operation such that the engineered surface structure includes a plurality of cells propagating periodically in three dimensions, with non-intersecting, non-flat, continuously curving wall portions which form two non-intersecting domains, and where the wall portions have openings forming a plurality of flow paths extending in three orthogonal dimensions throughout from the inlet to the outlet, and such that the engineered cellular structure has wall portions having a mean curvature other than zero.

The present invention relates to a membrane and a method for manufacturing a membrane for filtering a fluid, said membrane comprising: a substrate having a three-dimensional structure and consisting of an one-piece ceramic porous body; and at least one separating filtering layer having a porosity that is lower than that of the substrate, in which the three-dimensional structure of the substrate is produced by forming elemental layers that are stacked and connected in series with one another, by repeating steps: a) depositing a continuous bed of powder at least partially consisting of a powder intended for forming the ceramic porous body; b) locally consolidating, part of the deposited material such as to create the elemental layer, and simultaneously linking the elemental layer thus formed with the preceding layer such as to gradually grow the desired three-dimensional shape.

A process for making an iron oxide impregnated carbon nanotube membrane. In this template-free and binder-free process, iron oxide nanoparticles are homogeneously dispersed onto the surface of carbon nanotubes by wet impregnation. The amount of iron oxide nanoparticles loaded on the carbon nanotubes range from 0.25-80% by weight per total weight of the doped carbon nanotubes. The iron oxide doped carbon nanotubes are then pressed to form a carbon nanotube disc which is then sintered at high temperatures to form a mixed matrix membrane of iron oxide nanoparticles homogeneously dispersed across a carbon nanotube matrix. Methods of characterizing porosity, hydrophilicity and fouling potential of the carbon nanotube membrane are also described.

A method of making a ceramic honeycomb article which includes: applying at least one green membrane coating layer on a green substrate, the green substrate comprising a plurality of cells comprised of a plurality of interior channels and a plurality of porous interior walls between the channels; drying the at least one green membrane coating layer on the green substrate to produce a green coated substrate; and firing the green coated substrate into a porous substrate, wherein applying the at least one green membrane coating layer and the drying the at least one green membrane coating layer are repeated from 2 to 10 times prior to firing to form multiple green membrane coating layers on the green substrate and wherein the firing the green coated substrate forms a ceramic honeycomb article comprised of the porous substrate and multiple fired coating layers on the porous substrate.

Zeolite membrane sheets for separation of mixtures containing water are provided, as well as methods for making the same. Thin, but robust, zeolite membrane sheets having an inter-grown zeolite crystal film directly on a thin, less than 200 micron thick, porous support sheet free of any surface pores with a size above 10 microns. The zeolite membrane film thickness is less than about 10 microns above the support surface and less than about 5 microns below the support surface. Methods of preparing the membrane are disclosed which include coating of the support sheet surface with a seed coating solution containing the parent zeolite crystals with mean particle sizes from about 0.5 to 2.0 microns at loading of 0.05-0.5 mg/cm2 and subsequent growth of the seeded sheet in a growth reactor loaded with a growth solution over a temperature range of about 45 C. to about 120 C.

Described herein is a cordierite membrane coated on a monolith substrate formed from cordierite. The membrane coating is formed from cordierite particles which have been processed to have a median particle size diameter of between 1 and 3 microns with a narrow particle size distribution suitable for forming a cordierite membrane on a cordierite monolith substrate. After the cordierite membrane is formed on the cordierite monolith substrate, the cordierite membrane monolith has a pore size of less than 1 micron.

Titanium dioxide/sulfonated graphene oxide/silver nanoparticle composite membrane and its preparation method and application are disclosed. Mixing graphene oxide, sodium chloroethanesulfonate, and sodium hydroxide uniformly in the water, and then adding concentrated nitric acid to obtain sulfonated graphene oxide; mixing the aqueous solution of said sulfonated graphene oxide with the aqueous solution of silver nitrate, stirring in the dark, then adding ascorbic acid, and continuing to stir to obtain a silver nanoparticle/sulfonated graphene oxide composite material; dispersing said silver nanoparticle/sulfonated graphene oxide composite material in water, and then deposited on said titanium dioxide nanorods arrays by vacuum deposition, and vacuum dried to obtain titanium dioxide/sulfonated graphene oxide/silver nanoparticle composite membrane. The membrane possessed photocatalytic effect under UV light and special wettability: super-hydrophobic oil under water/super-hydrophobic under oil, which could in situ separation and degradation of oil/water emulsion.

A process for making an iron oxide impregnated carbon nanotube membrane. In this template-free and binder-free process, iron oxide nanoparticles are homogeneously dispersed onto the surface of carbon nanotubes by wet impregnation. The amount of iron oxide nanoparticles loaded on the carbon nanotubes range from 0.25-80% by weight per total weight of the doped carbon nanotubes. The iron oxide doped carbon nanotubes are then pressed to form a carbon nanotube disc which is then sintered at high temperatures to form a mixed matrix membrane of iron oxide nanoparticles homogeneously dispersed across a carbon nanotube matrix. Methods of characterizing porosity, hydrophilicity and fouling potential of the carbon nanotube membrane are also described.

The invention relates to a power distribution system (1), especially a Power-over-Ethernet system, comprising at least one dominant sensor, which may be located within a powered device (4) like a lighting device, and at least one non-dominant sensor, which may be located within another powered device (4), wherein the power distribution system is adapted such that in a system low power mode the at least one dominant sensor (6) consumes power provided by a power providing unit (3) and the at least one non-dominant sensor (6) does not consume the provided power and that the power distribution system (1) switches from the system low power mode to a system high power mode, if the at least one dominant sensor (6) has sensed an event. Since in the system low power mode the at least one non-dominant sensor does not consume power, the power consumption can be reduced.