A method for preparing a heterogeneous catalyst. The method comprises steps of: (a) combining (i) a support, (ii) an aqueous solution of a noble metal compound and (iii) a C.sub.2-C.sub.18 thiol comprising at least one hydroxyl or carboxylic acid substituent; to form a wet particle and (b) removing water from the wet particle by drying followed by calcination to produce the catalyst.

A method for preparing a heterogeneous catalyst. The method comprises steps of: (a) combining (i) a support, (ii) an aqueous solution of a noble metal compound and (iii) a C.sub.2-C.sub.18 thiol comprising at least one hydroxyl or carboxylic acid substituent; to form a wet particle and (b) removing water from the wet particle by drying followed by calcination to produce the catalyst.

The present invention relates to a particulate filter, in particular a particulate filter for use in an emission treatment system of an internal combustion engine. The particulate filter provides an advantageous combination of low back pressure and high fresh filtration efficiency.

The present invention relates to a particulate filter, in particular a particulate filter for use in an emission treatment system of an internal combustion engine. The particulate filter provides an advantageous combination of low back pressure and high fresh filtration efficiency.

A catalyst molded body, a production method thereof and a method for preparing cyclic ketone using the same, including: (a) producing a mixed powder including a catalyst powder and a binder; (b) producing a slurry by mixing an aqueous alkali hydroxide solution with the mixed powder; and obtaining a catalyst molded body by molding and heat-treating the slurry.

A catalyst molded body, a production method thereof and a method for preparing cyclic ketone using the same, including: (a) producing a mixed powder including a catalyst powder and a binder; (b) producing a slurry by mixing an aqueous alkali hydroxide solution with the mixed powder; and obtaining a catalyst molded body by molding and heat-treating the slurry.

The present disclosure provides methods for fabricating catalysts for ammonia decomposition. The method may comprise (a) subjecting a catalyst support to one or more physical or chemical processes to optimize one or more pores, morphologies, and/or surface chemistry or property of the catalyst support; (b) depositing a composite support material on the catalyst support, wherein the composite support material comprises a morphology or surface chemistry or property; and (c) depositing one or more active metals on at least one of the composite support material and the catalyst support, wherein the one or more active metals comprise one or more nanoparticles configured to conform to the morphology of the composite support material and/or catalyst support material, thereby optimizing one or more active sites on the nanoparticles for ammonia processing.

An embodiment of the present invention provides a MXene nanodot core-carbon shell multifunctional catalyst including a MXene nanodot core and a carbon shell surrounding the MXene nanodot core. By introducing the carbon shell surrounding the nanodot core, the stability of the catalyst is ensured, thereby providing effects in that the catalyst may function under various conditions.

A process for the production of a catalyst comprising the steps of: dissolving the requisite quantities of copper nitrate and nickel nitrate in de-ionised water to provide a sub-0.30 molar aqueous solution of copper nitrate and nickel nitrate together in the ratio required; providing an ammoniacal solution by adding concentrated aqueous solution of ammonia in a quantity equal to between six and ten times the quantity required to realise both a 1:6 molar ratio for Cu.sup.2+ to ammonia and a 1:6 molar ratio for Ni.sup.2+ to ammonia; loading gamma alumina with 1 to 30% w/w of copper and nickel in a weight ratio of nickel to copper of 1:5 to 2:1 by suspending the requisite quantity of gamma alumina in said ammoniacal solution to achieve the required loading of copper and nickel; stirring the resulting gamma alumina suspension for at least 4 h at room temperature; then the volatile components evaporate under ambient conditions leaving dry loaded gamma alumina, which is calcined at a temperature of at least 260° C. for at least 30 min with a constant heating up rate; a catalyst or catalyst mixture, the catalyst or each catalyst in the catalyst mixture being obtainable by the above-mentioned process; and the use of the catalyst or catalyst mixture for the conversion of exhaust gases from an internal combustion engine into carbon dioxide, water and nitrogen.

A process for the production of a catalyst comprising the steps of: dissolving the requisite quantities of copper nitrate and nickel nitrate in de-ionised water to provide a sub-0.30 molar aqueous solution of copper nitrate and nickel nitrate together in the ratio required; providing an ammoniacal solution by adding concentrated aqueous solution of ammonia in a quantity equal to between six and ten times the quantity required to realise both a 1:6 molar ratio for Cu.sup.2+ to ammonia and a 1:6 molar ratio for Ni.sup.2+ to ammonia; loading gamma alumina with 1 to 30% w/w of copper and nickel in a weight ratio of nickel to copper of 1:5 to 2:1 by suspending the requisite quantity of gamma alumina in said ammoniacal solution to achieve the required loading of copper and nickel; stirring the resulting gamma alumina suspension for at least 4 h at room temperature; then the volatile components evaporate under ambient conditions leaving dry loaded gamma alumina, which is calcined at a temperature of at least 260° C. for at least 30 min with a constant heating up rate; a catalyst or catalyst mixture, the catalyst or each catalyst in the catalyst mixture being obtainable by the above-mentioned process; and the use of the catalyst or catalyst mixture for the conversion of exhaust gases from an internal combustion engine into carbon dioxide, water and nitrogen.