A method of manufacturing a catalyst article, the method comprising: providing a complex of a polyphenol and a PGM, the polyphenol comprising an ester functional group, the PGM comprising palladium; providing a support material; applying the complex to the support material to form a loaded support material; disposing the loaded support material on a substrate; and heating the loaded support material to form nanoparticles of the PGM on the support material.

Generally, it is disclosed a catalyst for use in a hydrotreating hydrocarbon feedstocks and the method of making such catalyst. It is generically provided that the catalyst comprises at least one Group VIB metal component, at least one Group VIII metal component, about (1) to (about (30) wt % C, and preferably about (1) to about (20) wt % C, and more preferably about (5) to about 15 wt % C of one or more sulfur containing organic additive and a titanium-containing carrier component, wherein the amount of the titanium component is in the range of about (3) to (about (60) wt %, expressed as an oxide (Ti0.sub.2) and based on the total weight of the catalyst. The titanium-containing carrier is formed by co-extruding or precipitating a titanium source with a Al203 precursor to form a porous support material comprising Al.sub.20.sub.3 or by impregnating a titanium source onto a porous support material comprising Al.sub.20.sub.3.

A highly active hydroprocessing catalyst that comprises an inorganic oxide support particle having been impregnated with a metals-impregnation solution comprising a complexing agent and a hydrogenation metal that is further incorporated with an organic additive blend.

The present invention relates to a diesel oxidation catalyst comprising a carrier body having a length L extending between a first end face and a second end face, and differently composed material zones A and B arranged on the carrier body, wherein material zone A comprises platinum and palladium applied to a cerium-titanium mixed oxide, and material zone B comprises platinum and palladium applied to a carrier oxide B.

An alumina grain has a single-crystal structure and has an approximate regular octahedral stereoscopic morphology. Eight sides of the alumina grain belong to the {111} family of crystal planes of γ-state alumina, and the grain size is 5-100 μm. The alumina grain is unique in crystal plane exposure and distribution, simple and feasible in preparation, and low in cost, and has higher operability, and thus has good application prospect in the field of catalysis and adsorption.

In a method, device, catalyst and a method for producing a catalyst for the catalytic conversion of a substance mixture containing glycerol to propanol in a fixed-bed reactor, substrates of the catalyst have inorganic materials and/or metal oxides. The substrates have a pore diameter at the surface of between 10 and 25 angstroms, preferably between 12 and 20 angstroms, particularly preferably 15 angstroms.

A highly active hydroprocessing catalyst that comprises a doped support impregnated with at lease one hydrogenation metal component and filled with an organic additive blend. The catalyst is made by providing a doped support particle followed by impregnating the doped support particle with a metal impregnation solution to provide a metal-impregnated doped support particle. The metal-impregnated doped support particle is dried but not calcined and impregnated with an organic additive blend component.

The present invention relates to a method for producing supported catalysts, comprising: providing a metal foam element A, which consists of metallic cobalt, an alloy of nickel and cobalt, or an arrangement of layers of nickel and cobalt, lying one over the other; applying an aluminum-containing powder MP to metal foam element A in order to obtain metal foam element AX; thermally treating metal foam element AX to achieve alloy formation between metal foam element A and aluminum-containing powder MP, in order to obtain metal foam element B; oxidatively treating metal foam element B, in order to obtain metal foam element C; and applying a catalytically active layer, comprising at least one support oxide and at least one catalytically active component, to at least part of the surface of metal foam element C, in order to obtain a supported catalyst. The present invention further relates to the supported catalysts that can be obtained using the method and to the use of said supported catalysts in chemical transformations.

A method comprising a) contacting a solvent, a carboxylic acid, and a peroxide-containing compound to form an acidic mixture wherein a weight ratio of solvent to carboxylic acid in the acidic mixture is from about 1:1 to about 100:1; b) contacting a titanium-containing compound and the acidic mixture to form a solubilized titanium mixture wherein an equivalent molar ratio of titanium-containing compound to carboxylic acid in the solubilized titanium mixture is from about 1:1 to about 1:4 and an equivalent molar ratio of titanium-containing compound to peroxide-containing compound in the solubilized titanium mixture is from about 1:1 to about 1:20; and c) contacting a chromium-silica support comprising from about 0.1 wt. % to about 20 wt. % water and the solubilized titanium mixture to form an addition product and drying the addition product by heating to a temperature in a range of from about 50° C. to about 150° C. and maintaining the temperature in the range of from about 50° C. to about 150° C. for a time period of from about 30 minutes to about 6 hours to form a pre-catalyst.

This invention provides a preparation method of a catalyst for preferential oxidization of CO in a hydrogen-enriched atmosphere, and a catalyst product obtained from the method and its applications thereof. Particularly, in this invention, a wide-temperature catalyst for preferential oxidization of CO in a hydrogen-enriched atmosphere is obtained by depositing one or more of an iron oxide, cobalt oxide, and nickel oxide as a promoter onto the surface of a supported Pt-group noble metal catalyst precursor via chemical vapor deposition or atomic layer deposition. In the wide-temperature catalyst, the active noble metal component has a content of 0.1 to 10 wt %, and the promoter has a content of 0.1 to 10 wt % in terms of the metal element thereof. In the reaction of preferential oxidation of CO in a hydrogen-enriched atmosphere, the catalyst prepared by this invention can exhibit excellent catalytic performance and can achieve high conversion of CO with high selectivity in a wide temperature range of −80 to 200° C., for example. Also, the catalyst can remain stable for a long time even in a case where steam and CO.sub.2 are present in the hydrogen-enriched atmosphere.