Disclosed are a ferrite catalyst and preparation methods thereof. The catalyst is provided with a formula below, wherein A is Mg atom, Zn atom or a mixture of both atoms at any ratio; D is one or more atoms selected from the group consisting of Ni, Co, W, Mn, Ca, Mo or V atom; Z is a catalyst carrier, which is one or more selected from the group consisting of calcium phosphate, calcium dihydrogen phosphate, aluminum phosphate, aluminum dihydrogen phosphate, ferric phosphate, magnesium phosphate, zinc phosphate, Mg—Al hydrotalcite, calcium carbonate, magnesium carbonate; a=0.01-0.6; b=0-0.30; c is a number balancing each valence; x, y represent the amounts of principal catalyst and carrier Z respectively, wherein the weight ratio y/x=0.5:1-7:1.
x(FeA.sub.aD.sub.bO.sub.c)/yZ

A system and a method for isomerizing a 2-butene feed stream to form a 1-butene product stream are provided. An exemplary method includes calcining the red mud, flowing a butene feedstock over the red mud in an isomerization reactor, and separating 1-butene from a reactor effluent.

A system and a method for isomerizing a 2-butene feed stream to form a 1-butene product stream are provided. An exemplary method includes calcining the red mud, flowing a butene feedstock over the red mud in an isomerization reactor, and separating 1-butene from a reactor effluent.

The disclosure provides an improved endothermic hydrocarbon conversion process that comprises reacting a hydrocarbon with a multi-component catalyst bed, and regenerating the catalyst bed with air, where the air used in regeneration step and hydrocarbon are at low air to hydrocarbon ratios and optionally at near-atmospheric pressures.

The disclosure provides an improved endothermic hydrocarbon conversion process that comprises reacting a hydrocarbon with a multi-component catalyst bed, and regenerating the catalyst bed with air, where the air used in regeneration step and hydrocarbon are at low air to hydrocarbon ratios and optionally at near-atmospheric pressures.

The invention relates to a catalyst for preparation of butadiene by oxydehydrogenation of butene in a fluidized bed reactor, a method of preparing the same, and use of the same, wherein a method according to an embodiment of the invention comprises: reacting a metal precursor with an alkaline substance to obtain a slurry containing insoluble compound, followed by filtering and washing the slurry; adding a binder and deionized water, followed by agitation to regulate the solid content of the slurry to 10-50%; subjecting the slurry to spray drying granulation, wherein the temperature at the feed port is controlled between 200-400° C., and the temperature at the discharge port is controlled between 100-160° C., to obtain catalyst microspheres; and drying the catalyst microspheres at 80-200° C. for 1-24 h, and then calcining the catalyst microspheres at 500-900° C. for 4-24 h to obtain a catalyst having a general formula of FeXaYbZcOd, comprising Fe, Mg, Zn, Bi, Mo, Mn, Ni, Co, Ba, Ca, and other metals. The catalyst microspheres prepared according to the exemplary method exhibit high mobility, desirable particle size distribution, extremely high mechanical strength and catalytic activity, and are applicable to industrial production of butadiene by oxydehydrogenation of butene in a fluidized bed. When this catalyst is used to prepare butadiene by oxydehydrogenation of butene, the yield of butadiene is 76-86%, and the selectivity to butadiene is 94-97%.

The invention relates to a catalyst for preparation of butadiene by oxydehydrogenation of butene in a fluidized bed reactor, a method of preparing the same, and use of the same, wherein a method according to an embodiment of the invention comprises: reacting a metal precursor with an alkaline substance to obtain a slurry containing insoluble compound, followed by filtering and washing the slurry; adding a binder and deionized water, followed by agitation to regulate the solid content of the slurry to 10-50%; subjecting the slurry to spray drying granulation, wherein the temperature at the feed port is controlled between 200-400° C., and the temperature at the discharge port is controlled between 100-160° C., to obtain catalyst microspheres; and drying the catalyst microspheres at 80-200° C. for 1-24 h, and then calcining the catalyst microspheres at 500-900° C. for 4-24 h to obtain a catalyst having a general formula of FeXaYbZcOd, comprising Fe, Mg, Zn, Bi, Mo, Mn, Ni, Co, Ba, Ca, and other metals. The catalyst microspheres prepared according to the exemplary method exhibit high mobility, desirable particle size distribution, extremely high mechanical strength and catalytic activity, and are applicable to industrial production of butadiene by oxydehydrogenation of butene in a fluidized bed. When this catalyst is used to prepare butadiene by oxydehydrogenation of butene, the yield of butadiene is 76-86%, and the selectivity to butadiene is 94-97%.

Methods for bi-reforming with a red mud catalyst support composition, one method including providing a methane feed in the presence of carbon dioxide and steam to react over the red mud catalyst support composition at increased temperature and increased pressure to produce synthesis gas comprising H.sub.2 and CO, the composition comprising red mud material produced from an alumina extraction process from bauxite ore.

Methods for bi-reforming with a red mud catalyst support composition, one method including providing a methane feed in the presence of carbon dioxide and steam to react over the red mud catalyst support composition at increased temperature and increased pressure to produce synthesis gas comprising H.sub.2 and CO, the composition comprising red mud material produced from an alumina extraction process from bauxite ore.

A process for preparing C.sub.2 to C.sub.5 olefins includes introducing a feed stream comprising hydrogen and at least one carbon-containing component selected from the group consisting of CO, CO.sub.2, and mixtures thereof into a reaction zone. The feed stream is contacted with a hybrid catalyst in the reaction zone, and a product stream is formed that exits the reaction zone and includes C.sub.2 to C.sub.5 olefins. The hybrid catalyst includes a methanol synthesis component and a solid microporous acid component that is selected from molecular sieves having 8-MR access and having a framework type selected from the group consisting of CHA, AEI, AFX, ERI, LTA, UFI, RTH, and combinations thereof. The methanol synthesis component comprises a metal oxide support and a metal catalyst. The metal oxide support includes titania, zirconia, hafnia or mixtures thereof, and the metal catalyst includes zinc.