The present invention relates to a method for producing an oxide catalyst containing Mo, V, Sb, and Nb, the method including a raw material preparation step of obtaining an aqueous mixed liquid containing Mo, V, Sb, and Nb, an aging step of subjecting the aqueous mixed liquid to aging at more than 30° C., a drying step of drying the aqueous mixed liquid, thereby obtaining a dried powder, and a calcination step of calcining the dried powder, thereby obtaining the oxide catalyst, and a method for producing an unsaturated nitrile or an unsaturated acid by using the catalyst.

Redox catalysts having surface medication, methods of making redox catalysts with surface modification, and uses of the surface modified redox catalysts are provided. In some aspects, the redox catalysts include a core oxygen carrier region such as CaMnO.sub.3, BaMnO.sub.3−δ, SrMnO.sub.3−δ, Mn.sub.2SiO.sub.4, Mn.sub.2MgO.sub.4−δ, La.sub.0.8Sr.sub.0.2O.sub.3−δ, La.sub.0.8Sr.sub.0.2FeO.sub.3−δ, Ca.sub.9Ti.sub.0.1Mn.sub.0.9O.sub.3−δ, Pr.sub.6O.sub.11−δ, manganese ore, or a combination thereof; and an outer shell having an average thickness of about 1-100 monolayers surrounding the outer surface of the core region. The outer shell can include, for example a salt selected such as Li.sub.2WO.sub.4, Na.sub.2WO.sub.4, K.sub.2WO.sub.4, SrWO.sub.4, Li.sub.2MoO.sub.4, Na.sub.2MoO.sub.4, K.sub.2MoO.sub.4, CsMoO.sub.4, Li.sub.2CO.sub.3, Na.sub.2CO.sub.3, K.sub.2CO.sub.3, or a combination thereof.

Redox catalysts having surface medication, methods of making redox catalysts with surface modification, and uses of the surface modified redox catalysts are provided. In some aspects, the redox catalysts include a core oxygen carrier region such as CaMnO.sub.3, BaMnO.sub.3−δ, SrMnO.sub.3−δ, Mn.sub.2SiO.sub.4, Mn.sub.2MgO.sub.4−δ, La.sub.0.8Sr.sub.0.2O.sub.3−δ, La.sub.0.8Sr.sub.0.2FeO.sub.3−δ, Ca.sub.9Ti.sub.0.1Mn.sub.0.9O.sub.3−δ, Pr.sub.6O.sub.11−δ, manganese ore, or a combination thereof; and an outer shell having an average thickness of about 1-100 monolayers surrounding the outer surface of the core region. The outer shell can include, for example a salt selected such as Li.sub.2WO.sub.4, Na.sub.2WO.sub.4, K.sub.2WO.sub.4, SrWO.sub.4, Li.sub.2MoO.sub.4, Na.sub.2MoO.sub.4, K.sub.2MoO.sub.4, CsMoO.sub.4, Li.sub.2CO.sub.3, Na.sub.2CO.sub.3, K.sub.2CO.sub.3, or a combination thereof.

Included herein are methods for photodriven hydrogenation of N.sub.2, the methods comprising, for example: hydrogenating N.sub.2 to NH.sub.3 in the presence of a light, an organic transfer agent, and a first metal-containing catalyst; wherein: the transfer agent and the first catalyst are in a solution; the transfer agent comprises n chemically transferable electrons and protons, n being an integer equal to or greater than 1; the step of hydrogenating comprises at least one charge-transfer reaction via which the transfer agent donates at least one electron and at least one proton to one or more other chemical species; the step of hydrogenating comprises at least one photochemical reaction; and the light is characterized by energy sufficient to drive the at least one photochemical reaction. Also disclosed herein are methods comprising regenerating a spent-transfer agent back into the transfer agent.

Provided in this disclosure are oxidative dehydrogenation catalysts that include a mixed metal oxide having the empirical formula:

Mo.sub.1.0V.sub.0.12-0.49Te.sub.0.05-0.17Nb.sub.0.10-0.20O.sub.d

wherein d is a number to satisfy the valence of the oxide. The oxidative dehydrogenation catalyst is characterized by having XRD diffraction peaks (2θ degrees) at 22±0.2, 27±0.2, 28.0±0.2, and 28.3±0.1. The disclosure also provides methods of making the catalysts that include wet ball milling.

Provided in this disclosure are oxidative dehydrogenation catalysts that include a mixed metal oxide having the empirical formula:

Mo.sub.1.0V.sub.0.12-0.49Te.sub.0.05-0.17Nb.sub.0.10-0.20O.sub.d

wherein d is a number to satisfy the valence of the oxide. The oxidative dehydrogenation catalyst is characterized by having XRD diffraction peaks (2θ degrees) at 22±0.2, 27±0.2, 28.0±0.2, and 28.3±0.1. The disclosure also provides methods of making the catalysts that include wet ball milling.

A method for producing an ammoxidation catalyst, the method including: a step (i) of preparing a starting material slurry comprising molybdenum, bismuth, iron, and a carboxylic acid compound; a step (ii) of stirring the starting material slurry in a temperature range of 30 to 50° C. for 20 minutes to 8 hours, thereby preparing a precursor slurry; a step of spray-drying the precursor slurry, thereby obtaining a dried particle; and a step of calcining the dried particle.

A method for producing an ammoxidation catalyst, the method including: a step (i) of preparing a starting material slurry comprising molybdenum, bismuth, iron, and a carboxylic acid compound; a step (ii) of stirring the starting material slurry in a temperature range of 30 to 50° C. for 20 minutes to 8 hours, thereby preparing a precursor slurry; a step of spray-drying the precursor slurry, thereby obtaining a dried particle; and a step of calcining the dried particle.

Carbon nanofiber doped alumina (Al—CNF) supported MoCo catalysts in hydrodesulfurization (HDS), and/or boron doping, e.g., up to 5 wt % of total catalyst weight, can improve catalytic efficiency. Al-CNF-supported MoCo catalysts, (Al-CNF-MoCo), can reduce the sulfur concentration in fuel, esp. liquid fuel, to below the required limit in a 6 h reaction time. Thus, Al-CNF-MoCo has a higher catalytic activity than Al-MoCo, which may be explained by higher mesoporous surface area and better dispersion of MoCo metals on the AlCNF support relative to alumina support. The BET surface area of Al-MoCo may be 75% less than Al-CNF-MoCo, e.g., 166 vs. 200 m.sup.2/g. SEM images indicate that the catalyst nanoparticles can be evenly distributed on the surface of the CNF. The surface area of the AlMoCoB5% may be 206 m.sup.2/g, which is higher than AlMoCoB0% and AlMoCoB2%, and AlMoCoB5% has the highest HDS activity, removing more than 98% sulfur and below allowed levels.

Carbon nanofiber doped alumina (Al—CNF) supported MoCo catalysts in hydrodesulfurization (HDS), and/or boron doping, e.g., up to 5 wt % of total catalyst weight, can improve catalytic efficiency. Al-CNF-supported MoCo catalysts, (Al-CNF-MoCo), can reduce the sulfur concentration in fuel, esp. liquid fuel, to below the required limit in a 6 h reaction time. Thus, Al-CNF-MoCo has a higher catalytic activity than Al-MoCo, which may be explained by higher mesoporous surface area and better dispersion of MoCo metals on the AlCNF support relative to alumina support. The BET surface area of Al-MoCo may be 75% less than Al-CNF-MoCo, e.g., 166 vs. 200 m.sup.2/g. SEM images indicate that the catalyst nanoparticles can be evenly distributed on the surface of the CNF. The surface area of the AlMoCoB5% may be 206 m.sup.2/g, which is higher than AlMoCoB0% and AlMoCoB2%, and AlMoCoB5% has the highest HDS activity, removing more than 98% sulfur and below allowed levels.