A ratio of an angle of 2 to 15° is 50% or more in an arbitrary surface of the tungsten material, the angle being formed between a specific crystal orientation of a first crystal grain and a specific crystal orientation of a second crystal grain adjacent to the first crystal grain.

A ratio of an angle of 2 to 15° is 50% or more in an arbitrary surface of the tungsten material, the angle being formed between a specific crystal orientation of a first crystal grain and a specific crystal orientation of a second crystal grain adjacent to the first crystal grain.

The present invention can provide light-colored magnetic particles having a zirconium oxide coating layer formed on a magnetic core, and having a silver coating layer formed on the zirconium oxide coating layer, and a part of the surface of the zirconium oxide coating layer is exposed to the outside, but chemical resistance is excellent, and thus the magnetic particles hardly cause a change of magnetic characteristics so as to be suitable for security elements.

The present disclosure discloses a method for coating a magnetic powder core with sodium silicate, including: using polyoxyethylene laurylether phosphate as a dispersant for sodium silicate and lignosulfonate as a dispersant for a metal magnetic powder, mixing a dispersed sodium silicate solution and a dispersed metal magnetic powder, coating the dispersed metal magnetic powder, and drying: adding an insulating adhesive and a lubricant, subjecting the resulting mixture to a compression molding, and finally, carrying out a high-temperature annealing treatment to obtain a sodium silicate coated magnetic powder core.

The present disclosure discloses a method for coating a magnetic powder core with sodium silicate, including: using polyoxyethylene laurylether phosphate as a dispersant for sodium silicate and lignosulfonate as a dispersant for a metal magnetic powder, mixing a dispersed sodium silicate solution and a dispersed metal magnetic powder, coating the dispersed metal magnetic powder, and drying: adding an insulating adhesive and a lubricant, subjecting the resulting mixture to a compression molding, and finally, carrying out a high-temperature annealing treatment to obtain a sodium silicate coated magnetic powder core.

The present invention relates to an alloy with formula of RE-M-B—Fe as defined herein and oxygen content less than 0.9 wt %, wherein said RE is in the range of 29.0 weight % to 33.0 weight %; M is in the range of 0.25 weight % to 1.0 weight %; B is in the range of 0.8 weight % to 1.1 weight %; and Fe makes up the balance. The present invention also relates to a method for preparing a RE-M-Fe—B magnetic powder, as defined herein comprising the steps of: (a) melt spinning a RE-M-Fe—B alloy composition to obtain a melt-spun powder; (b) pressing the melt-spun powder of step (a) to obtain a compact body; (c) hot deforming the compact body of step (b) to obtain a die-upset magnet; (d) crushing the die-upset magnet of step (c) to obtain a powder; (e) milling and sieving the powder of step (d); and (f) passivating the powder of step (e) to obtain a magnetic powder; wherein: each of steps (d) to (f) is performed under a low oxygen environment and transfer between each of steps (d) to (f) is a sealed transfer; and wherein the oxygen content of the low oxygen environment and during each sealed transfer is below 0.5 weight %.

The present invention relates to an alloy with formula of RE-M-B—Fe as defined herein and oxygen content less than 0.9 wt %, wherein said RE is in the range of 29.0 weight % to 33.0 weight %; M is in the range of 0.25 weight % to 1.0 weight %; B is in the range of 0.8 weight % to 1.1 weight %; and Fe makes up the balance. The present invention also relates to a method for preparing a RE-M-Fe—B magnetic powder, as defined herein comprising the steps of: (a) melt spinning a RE-M-Fe—B alloy composition to obtain a melt-spun powder; (b) pressing the melt-spun powder of step (a) to obtain a compact body; (c) hot deforming the compact body of step (b) to obtain a die-upset magnet; (d) crushing the die-upset magnet of step (c) to obtain a powder; (e) milling and sieving the powder of step (d); and (f) passivating the powder of step (e) to obtain a magnetic powder; wherein: each of steps (d) to (f) is performed under a low oxygen environment and transfer between each of steps (d) to (f) is a sealed transfer; and wherein the oxygen content of the low oxygen environment and during each sealed transfer is below 0.5 weight %.

The present invention relates to an alloy with formula of RE-M-B—Fe as defined herein and oxygen content less than 0.9 wt %, wherein said RE is in the range of 29.0 weight % to 33.0 weight %; M is in the range of 0.25 weight % to 1.0 weight %; B is in the range of 0.8 weight % to 1.1 weight %; and Fe makes up the balance. The present invention also relates to a method for preparing a RE-M-Fe—B magnetic powder, as defined herein comprising the steps of: (a) melt spinning a RE-M-Fe—B alloy composition to obtain a melt-spun powder; (b) pressing the melt-spun powder of step (a) to obtain a compact body; (c) hot deforming the compact body of step (b) to obtain a die-upset magnet; (d) crushing the die-upset magnet of step (c) to obtain a powder; (e) milling and sieving the powder of step (d); and (f) passivating the powder of step (e) to obtain a magnetic powder; wherein: each of steps (d) to (f) is performed under a low oxygen environment and transfer between each of steps (d) to (f) is a sealed transfer; and wherein the oxygen content of the low oxygen environment and during each sealed transfer is below 0.5 weight %.

A tantalum powder, a tantalum powder compact, a tantalum powder sintered body, a tantalum anode, an electrolytic capacitor and a preparation method for tantalum powder. The tantalum powder contains boron element, and the tantalum powder has a specific surface area of greater than or equal to 4 m.sup.2/g; the ratio of the boron content of the tantalum powder to the specific surface area of the tantalum powder is 2˜16; the boron content is measured in weight ppm, and the specific surface area is measured in m.sup.2/g; Powder that can pass through a ρ-mesh screen in the tantalum powder accounts for over 85% of the total weight of the tantalum powder, where ρ=150˜170; and the tantalum powder with high CV has a low leakage current and dielectric loss, and good moldability.

A tantalum powder, a tantalum powder compact, a tantalum powder sintered body, a tantalum anode, an electrolytic capacitor and a preparation method for tantalum powder. The tantalum powder contains boron element, and the tantalum powder has a specific surface area of greater than or equal to 4 m.sup.2/g; the ratio of the boron content of the tantalum powder to the specific surface area of the tantalum powder is 2˜16; the boron content is measured in weight ppm, and the specific surface area is measured in m.sup.2/g; Powder that can pass through a ρ-mesh screen in the tantalum powder accounts for over 85% of the total weight of the tantalum powder, where ρ=150˜170; and the tantalum powder with high CV has a low leakage current and dielectric loss, and good moldability.