A Ni-base superalloy composition to be used for powder-based additive manufacturing (AM) technology, such as selective laser melting (SLM) or electron beam melting (EBM). The cracking susceptibility during an AM process is considerably reduced by controlling the amount of elements, especially Hf, that form low-melting eutectics.

A metal component is disclosed. The metal component has a first dimension greater than 5 mm, and a second dimension greater than 5 mm. The metal component may include where the alloy includes titanium, aluminum, vanadium, carbon, nitrogen, and oxygen. The alloy may include zirconium, titanium, copper, nickel, and beryllium. The metal component is not die-cast, melt-spun, or forged. An ejector and a method for jetting the metal component is also disclosed.

A metal component is disclosed. The metal component has a first dimension greater than 5 mm, and a second dimension greater than 5 mm. The metal component may include where the alloy includes titanium, aluminum, vanadium, carbon, nitrogen, and oxygen. The alloy may include zirconium, titanium, copper, nickel, and beryllium. The metal component is not die-cast, melt-spun, or forged. An ejector and a method for jetting the metal component is also disclosed.

Provided is a stainless steel powder composition, which comprises Cr, Cu, Mn, Mo, Ni and Fe; wherein, based on a total weight of the stainless steel powder composition, a content of Cr is 20 wt% to 24 wt%, and a content of Cu is more than 0 wt% and less than or equal to 0.5 wt%, a content of Mn is more than 0 wt% and less than or equal to 2 wt%, a content of Mo is 2.25 wt% to 3 wt% and a content of Ni is 10 wt% to 15 wt%. When applying the stainless steel powder composition of the present invention to laser additive manufacturing (LAM), the produced stainless steel workpiece has enhanced tensile strength, thereby expanding the follow-up applications and increasing the commercial value.

An apparatus for laser materials processing including a laser (4) for generating a laser beam and a laser head (5) which is movable along at least one spatial direction and is connected to the laser via a light guide, and which emits a laser beam (7) capable of processing a material. The present invention also relates to an apparatus for selective laser melting or selective laser sintering having an apparatus for laser materials processing.

A lamination molding apparatus which can improve the lamination molding accuracy, is provided. A lamination molding apparatus, including a chamber covering a desired molding region, the chamber being filled with an inert gas of a predetermined concentration; and a molding table provided in the molding region, the molding table being configured so as to be capable of being moved vertically by a driving mechanism; wherein the molding table is configured to be temperature-controllable; and a thermostatic section is provided in between the molding table and the driving mechanism or in the driving mechanism, temperature of the thermostatic section being maintained substantially constant, is provided.

Described herein are compositions, methods, and systems for printing metal three-dimensional objects. In an example, described is a composition for three-dimensional printing comprising: a metal powder build material, wherein the metal powder build material has an average particle size of from about 10 μm to about 250 μm; and a binder fluid comprising: an aqueous liquid vehicle, and latex polymer particles dispersed in the aqueous liquid vehicle, wherein the latex polymer particles have an average particle size of from about 10 nm to about 300 nm.

A method is provided for forming a three-dimensional article through successive fusion of parts of a metal powder bed, which parts corresponds to successive cross sections of the three-dimensional article, the method comprising the steps of: directing the at least one electron beam from the at least one electron beam source over a work table causing a powder layer to fuse in selected locations to form a first cross section of the three-dimensional article, preheating, with the at least one electron beam, an area of non-fused powder to a temperature within a predetermined temperature range a predetermined distance in Z-direction before the area is to be fused, where the area times the distance in z-direction is defining a preheating volume of non-fused powder when the three dimensional article is finished.

An additively manufactured apparatus having a gas filled sealed cavity containing at least two additively manufactured cathodes and an additively manufactured anode spaced from the cathodes such that a continuous electric discharge of the gas stimulated between at least one of the cathodes and the anode provides a Boolean function output at the anode corresponding to electrical input signals at two of the cathodes.

A method for additively manufacturing at least a portion of a component, in particular a component of a turbomachine. The method includes the following steps: a) depositing at least one powder layer of a component material in powder form layer by layer onto a component platform in the region of a buildup and joining zone; b) locally solidifying the powder layer by selectively irradiating the same using at least one high-energy beam in the region of the buildup and joining zone, forming a component layer; c) lowering the component platform by a predefined layer thickness; and d) repeating steps a) through c) until completion of the component portion or of the component. At least one contour portion of at least one component layer is irradiated in a step b1) at least once by at least one high-energy beam in a way that allows the solidified powder layer to be locally heated, but not melted, and, in a subsequent step b2), irradiated by at least one high-energy beam in a way that allows the solidified powder layer-to be locally melted in the region of the contour portion. In addition, a device for implementing such a method.