A rotary plasma reactor system is provided. In another aspect, a plasma reactor is rotatable about a generally horizontal axis within a vacuum chamber. A further aspect employs a plasma reactor, a vacuum chamber, and an elongated electrode internally extending within a central area of the reactor. Yet another aspect employs a plasma reactor for use in activating, etching and/or coating tumbling workpiece material.

A rotary plasma reactor system is provided. In another aspect, a plasma reactor is rotatable about a generally horizontal axis within a vacuum chamber. A further aspect employs a plasma reactor, a vacuum chamber, and an elongated electrode internally extending within a central area of the reactor. Yet another aspect employs a plasma reactor for use in activating, etching and/or coating tumbling workpiece material.

The present disclosure discloses a method for coating a magnetic powder core with sodium silicate, including: using polyoxyethylene laurylether phosphate as a dispersant for sodium silicate and lignosulfonate as a dispersant for a metal magnetic powder, mixing a dispersed sodium silicate solution and a dispersed metal magnetic powder, coating the dispersed metal magnetic powder, and drying: adding an insulating adhesive and a lubricant, subjecting the resulting mixture to a compression molding, and finally, carrying out a high-temperature annealing treatment to obtain a sodium silicate coated magnetic powder core.

The present disclosure discloses a method for coating a magnetic powder core with sodium silicate, including: using polyoxyethylene laurylether phosphate as a dispersant for sodium silicate and lignosulfonate as a dispersant for a metal magnetic powder, mixing a dispersed sodium silicate solution and a dispersed metal magnetic powder, coating the dispersed metal magnetic powder, and drying: adding an insulating adhesive and a lubricant, subjecting the resulting mixture to a compression molding, and finally, carrying out a high-temperature annealing treatment to obtain a sodium silicate coated magnetic powder core.

The present invention provides a rare earth sintered magnet which contains R (R represents one or more rare earth elements essentially including Nd), T (T represents one or more iron group elements essentially including Fe), B, M.sup.1 (M.sup.1 represents one or more elements selected from among Al, Si, Cr, Mn, Cu, Zn, Ga, Ge, Mo, Sn, W, Pb and Bi) and M.sup.2 (M.sup.2 represents one or more elements selected from among Ti, V, Zr, Nb, Hf and Ta), while comprising an R.sub.2T.sub.14B phase as the main phase. This rare earth sintered magnet is characterized in that: the M.sup.1 is in an amount of from 0.5% by atom to 2% by atom; if (R), (T), (M.sup.2) and (B) are the respective atomic percentages of the above-described R, T, M.sup.2 and B, the relational expression (1) ((T)/14)+(M.sup.2)≤(B)≤((R)/2)+((M.sup.2)/2) is satisfied; and from 0.1% by volume to 10% by volume of all grain boundary phases in the magnet is composed of an R.sub.6T.sub.13M.sup.1 phase. This rare earth sintered magnet is able to achieve excellent magnetic characteristics including a good balance between high Br and high H.sub.cJ.

The present invention provides a rare earth sintered magnet which contains R (R represents one or more rare earth elements essentially including Nd), T (T represents one or more iron group elements essentially including Fe), B, M.sup.1 (M.sup.1 represents one or more elements selected from among Al, Si, Cr, Mn, Cu, Zn, Ga, Ge, Mo, Sn, W, Pb and Bi) and M.sup.2 (M.sup.2 represents one or more elements selected from among Ti, V, Zr, Nb, Hf and Ta), while comprising an R.sub.2T.sub.14B phase as the main phase. This rare earth sintered magnet is characterized in that: the M.sup.1 is in an amount of from 0.5% by atom to 2% by atom; if (R), (T), (M.sup.2) and (B) are the respective atomic percentages of the above-described R, T, M.sup.2 and B, the relational expression (1) ((T)/14)+(M.sup.2)≤(B)≤((R)/2)+((M.sup.2)/2) is satisfied; and from 0.1% by volume to 10% by volume of all grain boundary phases in the magnet is composed of an R.sub.6T.sub.13M.sup.1 phase. This rare earth sintered magnet is able to achieve excellent magnetic characteristics including a good balance between high Br and high H.sub.cJ.

An example of a composition includes a host metal present in an amount ranging from about 95.00 weight percent to about 99.99 weight percent, based on a total weight of the composition. A flow additive is present in an amount ranging from about 0.01 weight percent to about 5.00 weight percent, based on the total weight of the composition. The flow additive consists of a metal containing compound that is reducible to an elemental metal in a reducing environment at a reducing temperature less than or equal to a sintering temperature of the host metal. The elemental metal is capable of being incorporated into a bulk metal phase of the host metal in a final metal object. The composition is spreadable, having a Hausner Ratio less than 1.25.

An example of a composition includes a host metal present in an amount ranging from about 95.00 weight percent to about 99.99 weight percent, based on a total weight of the composition. A flow additive is present in an amount ranging from about 0.01 weight percent to about 5.00 weight percent, based on the total weight of the composition. The flow additive consists of a metal containing compound that is reducible to an elemental metal in a reducing environment at a reducing temperature less than or equal to a sintering temperature of the host metal. The elemental metal is capable of being incorporated into a bulk metal phase of the host metal in a final metal object. The composition is spreadable, having a Hausner Ratio less than 1.25.

A component obtainable by a process which includes providing a composition and sintering the composition at a sintering temperature of from 1250° C. to 1400° C. for a period of from 3 to 15 minutes. The composition includes hard material particles with an inner core of fused tungsten carbide and an outer shell of tungsten carbide, and a binder metal selected from Co, Ni, Fe and alloys with at least one metal selected from Co, Ni and Fe.

The invention concerns pre-alloyed powders useful for the manufacture of metal-bonded diamond tools. A process for the synthesis of such powders is presented, characterized in that at least a major part of the phosphor is introduced by adding an aqueous solution of a phosphorus salt to one or more of the metal-bearing compounds. The powder can have a low cobalt content, or even be cobalt-free, yet remain suitable for the production of diamond-loaded segments having harness and bending characteristics approaching or exceeding that of cobalt.