A hardfacing metal composition and method of restoring worn work string tubing by application of a hardfacing metal to the worn regions of the work string tubing.

A hardfacing metal composition and method of restoring worn work string tubing by application of a hardfacing metal to the worn regions of the work string tubing.

Disclosed is an additive manufacturing process for making shingles and roof tiles. The entire shingle, including the substrate, can be manufactured on location, or a substrate can be manufactured at a manufacturing plant and then colored and textured on location to provide a wide variety of shapes and colors of shingles and roof tiles. Costs for inventory and shipping are reduced and a greater variety of shapes and colors can be provided for the shingles and roof tiles. The additive manufacturing equipment can be mounted on a truck so that the additive manufacturing techniques can be a mobile application of the additive manufacturing technology.

A hardfacing metal composition and method of restoring worn work string tubing by application of a hardfacing metal to the worn regions of the work string tubing.

A method for manufacturing a dissimilar metal joint product including joining a first member made of non-ferrous metal and having an end surface and a first surface adjacent to the end surface and a second member made of steel, the method includes: spraying a metal powder capable of being joined to the second member to the end surface and the first surface of the first member at a low temperature and at a high speed to form a coating to extend over the end surface and the first surface; disposing the first member and the second member such that the coating and the second member are close to or contact with each other; and performing fillet welding between the coating and the second member.

A hardfacing metal composition and method of restoring worn work string tubing by application of a hardfacing metal to the worn regions of the work string tubing.

An arc welding method alternately generates a short-circuit state and an arc state. In the method, short circuits are generated also in the arc period. This more than doubles the total number of short circuits, which is the sum of the short circuits generated in the short circuit period and those generated in the arc period. This enables a thin plate to be arc welded at a higher speed, while reducing its burn-through.

An automotive framework member 1 includes a first steel sheet 10, a second steel sheet 20, and a first weld metal part 40 joining an interface between the first steel sheet 10 and the second steel sheet 20, in which tensile strength of the first steel sheet 10 is 1.0 GPa or more and 1.6 GPa or less, tensile strength of the second steel sheet 20 is 1.8 GPa or more and 2.5 GPa or less, the first steel sheet 10 includes a groove part 18, the second steel sheet 20 is overlapped with the groove part 18, and a minimum Vickers hardness of a region within 4 mm of a periphery of the first weld metal part 40 of the second steel sheet 20 is 80% or more of a hardness of an outside of the region of the second steel sheet 20.

An automotive framework member 1 includes a first steel sheet 10, a second steel sheet 20, and a first weld metal part 40 joining an interface between the first steel sheet 10 and the second steel sheet 20, in which tensile strength of the first steel sheet 10 is 1.0 GPa or more and 1.6 GPa or less, tensile strength of the second steel sheet 20 is 1.8 GPa or more and 2.5 GPa or less, the first steel sheet 10 includes a groove part 18, the second steel sheet 20 is overlapped with the groove part 18, and a minimum Vickers hardness of a region within 4 mm of a periphery of the first weld metal part 40 of the second steel sheet 20 is 80% or more of a hardness of an outside of the region of the second steel sheet 20.

This wire for gas-shielded arc welding is a wire for joining a plurality of thin steel sheets by gas-shielded arc welding, the wire including, in mass %, with respect to a total mass of the wire: C: 0.06 to 0.15%; Si: more than 0 to 0.18%; Mn: 0.3 to 2.2%; Ti: 0.06 to 0.30%; Al: 0.001 to 0.30%; and B: 0.0030 to 0.0100%, in which Si, Mn, Ti, and Al satisfy Expressions (1) and (2).

SiMn0.30Expression (1)

(Si+Mn/5)/(Ti+Al)3.0Expression (2)