Described is a process of producing a multilayer lignocellulosic composite comprising one or more lignocellulosic composite layers or a single-layer lignocellulosic composite, wherein a high-frequency electrical field is applied and wherein a binder comprising for hardening the binder via esterification at least one, two or more compounds having two or more hydroxy groups and additionally one, two or more compounds having two or more carboxyl groups is provided or prepared. Furthermore described is a lignocellulosic com-posite, which is preparable according to said process, a construction product comprising such lignocellulosic composite and the use of such lignocellulosic composite as a building element in a construction product. Moreover is described a binder for producing a lignocellulosic composite.

Described is a process of producing a multilayer lignocellulosic composite comprising one or more lignocellulosic composite layers or a single-layer lignocellulosic composite, wherein a high-frequency electrical field is applied and wherein a binder comprising for hardening the binder via esterification at least one, two or more compounds having two or more hydroxy groups and additionally one, two or more compounds having two or more carboxyl groups is provided or prepared. Furthermore described is a lignocellulosic composite, which is preparable according to said process, a construction product comprising such lignocellulosic composite and the use of such lignocellulosic composite as a building element in a construction product. Moreover is described a binder, for producing a lignocellulosic composite.

A non-carbohydrate polyhydroxy component(s) is used in a binder composition to facilitate manufacture of wood particle boards.

Provided are a structure and a method of forming a structure that includes a core made, at least in part, of a rice hull composition. The rice hull composition including a combination of separate, unground rice hulls; ground rice hulls; and a rice hull powder, that each have a different particle size. A polymeric binder, such as a recycled plastic polymeric binder binds the separated unground rice hulls, the ground rice hulls and the rice hull powder together.

This invention discloses adhesive compositions useful for providing cohesive strength to particles, for example a mat of wood particles produced while making particleboard prior to curing. The adhesive compositions has a) one or more biopolymers and b) one or more monomers or oligomers. An oligomer may have a degree of polymerization of 4 or less. The weight ratio of the monomer/oligomer to the biopolymer is optionally between 30:70 and 80:20. Optionally, the adhesive compositions may be combined with an isocyanate. The adhesive composition may be used to make no added formaldehyde wood composites such as particleboard.

An adhesive composition is disclosed, and includes an aldehyde-based resin selected from the group consisting of urea-formaldehyde resins, melamine-formaldehyde resins, melamine-urea-formaldehyde resins, phenol-containing resins, and mixtures, combinations, and sub-combinations thereof, and a formaldehyde scavenger selected from the group consisting of chitosan, nano-chitosan, functionalized chitosan, and mixtures, combinations, and sub-combinations thereof.

A sheet manufacturing apparatus according to the invention has a mixing unit that mixes fiber and resin powder in air; and a sheet forming unit that forms a sheet by laying and heating the mixture mixed by the mixing unit; the grindability index of the resin contained in the resin powder being 0.8 or less.

A method to process cellulose fibres, preferably including wood fibres, comprises the steps: Deriving first fibres having a first property from a first raw material comprising cellulose fibres, Milling the first fibres to provide milled fibres, preferably with an average characteristic fibre dimension greater than 100 m, Drying the first fibres to provide dried fibres having a residual moisture less than 10% by weight, Adding one or more polymers, preferably including Lignin, to the dried fibres to provide a predetermined mixture including a polymer weight fraction of at least 5%, Processing the predetermined mixture to provide granules with an average characteristic granule dimension between 2 to 6 mm.

A wood chip material, especially a fireproof water resistant wood chip material, especially a fireproof water resistant wood chip material to make oriented strand boards which consists of a mixture containing 30 to 43 weight percent of wood chips, 53 to 61.9 weight percent of an aqueous solution of silicate, 2 to 5 weight percent of aluminium hydroxide, 1 to 3 weight percent of water, 0.1 to 1 weight percent of a stabilizer of the aqueous solution of silicate, and a hardener of the aqueous solution of sodium silicate in the concentration of 0.5 to 5 weight percent to the pure aqueous solution of sodium silicate providing always that the density of the aqueous solution of sodium silicate ranges from 1370 to 1400 kg/m.sup.3 and the SiO.sub.2 to NA.sub.2O molar ratio in the aqueous solution of sodium silicate ranges from 3.2 to 3.4. A method of production of a wood chip material, especially method of production of a fireproof water resistant wood chip material, especially method of production of a fireproof water resistant wood chip material to make oriented strand boards according to which, as the first step, the aluminium hydroxide is mixed with water, then wood chips are added into the mixture and everything is stirred thoroughly in such a manner that a wood chip mixture is formed, then the stabilizer of the aqueous solution of sodium silicate is added in the aqueous solution of silicate and after that the hardener of the aqueous solution of sodium silicate is admixed in this solution. Then the solution is stirred for 1 to 10 minutes until a binding solution is formed. Then the wood chip mixture is poured, at continuous stirring, in the binding solution and everything is stirred thoroughly again. Then the resulting mixture is poured in the place of application.

A method for producing a Zostera marina fiber object includes mixing natural fibers with a solid binding agent and a fire retardant, heating the mixture above a melting and/or softening point temperature of the binding agent, forming the mixture into the shape of the natural fiber object and applying a coating of the fire retardant to the surface of the natural fiber object.