Disclosed are thermoplastic vulcanizates comprising a plastic phase and a rubber phase and process for preparing such thermoplastic vulcanizates, wherein the plastic phase comprises a thermoplastic polymer and the rubber phase comprises a carboxylated nitrile rubber.

Textile compositions comprising at least one filamentous fungus are disclosed, as are methods for making and using such textile compositions. Embodiments of the textile compositions generally include at least one of a plasticizer, a polymer, and a crosslinker, in addition to the filamentous fungus. The disclosed textile compositions are particularly useful as analogs or substitutes for conventional textile compositions, including but not limited to leather.

A laminated foam sheet having a polyethylene resin foam layer and an antistatic polyethylene layer laminated on one or both sides thereof is produced by coextruding melts for respective layers, wherein the melt for the antistatic layer contains a polyethylene resin, an ionomer resin antistatic agent and a specific amount of volatile plasticizer blend containing an alcohol and a saturated hydrocarbon or a dialkyl ether. The antistatic layer of the obtained laminated foam sheet has specific morphology.

Provided are devices that are configured for gastric retention for a period of at least six hours (or at least three hours if the subject is in the fasted state) while maintaining their structural integrity and releasing or holding an active or diagnostic agent into or in gastric fluid of a human subject over that period, as well as methods of delivering an agent over an extended period by orally administering such devices to a subject, uses of an enteric polymer in the formation of devices that deliver an agent over an extended period of time, and methods of making such devices.

A polymer composition for producing gel extruded articles is described. The polymer composition contains polyethylene particles combined with a plasticizer and one or more shutdown reducing additives. The shutdown reducing additives decrease the shutdown temperature of polymer articles made from the polymer composition. In one embodiment, the polymer composition is used to form a porous membrane for use of a battery separator.

The present invention relates to drinking straws that are made from biodegradable material or bioplastics. The process to manufacture the present invention can use waste lipid wax byproducts. The present invention can incorporate chemical modification of corn or hemp fiber waste, and is comprised of wax byproduct, xanthan gum, carnauba wax and stearic acid. Stearin, hardener and plasticizers are mixed with corn or soy wax. A binder ingredient can be added to the waxes and fiber mixture, resulting in a smooth and hard, durable and biodegradable material with a high melting point. This material is then processed using an extrusion method, whereby the mixed ingredients are forced through an opening in a perforated plate or die with a design specific to form a straw, and then cut into a specific size by blades. The extruder consists of a large, rotating screw tightly fitting within a stationary barrel, at the end of which is the die. Extrusion enables mass production of food via a continuous, efficient system that ensures uniformity of the final product.

An example of a multi-fluid kit for three-dimensional (3D) printing includes an elasticity agent to be applied to at least a portion of a build material composition during 3D printing and a fusing agent to be applied to the at least the portion of the build material composition during 3D printing. The elasticity agent includes a plasticizer having: a formula (I): wherein n is an integer ranging from 3 to 8; or a formula (II): wherein m is an integer ranging from 3 to 8. The fusing agent includes an energy absorber.

A polyolefin multilayer microporous film includes a first layer containing ultra-high molecular weight polypropylene and high density polyethylene, formed on each side of a second layer containing ultra-high molecular weight polyethylene and high density polyethylene. In the first layer, 30% to 60% thereof is a region in which the polypropylene content is less than 20% as determined by AFM-IR from the displacement of an AFM cantilever measured between when laser is irradiated at 1465 cm-1 and when laser is irradiated at 1376 cm-1. For regions wherein the polypropylene content is 20% or higher, the mean of the maximum diameters is 0.1 μm to 10 μm. At 90° C., the film has an elongation at puncture of 0.40 mm/μm or greater.

A laminated foam sheet having a polyethylene resin foam layer and an antistatic polyethylene layer laminated on one or both sides thereof is produced by coextruding melts for respective layers, wherein the melt for the antistatic layer contains a polyethylene resin, an ionomer resin antistatic agent and a specific amount of volatile plasticizer blend containing an alcohol and a saturated hydrocarbon or a dialkyl ether. The antistatic layer of the obtained laminated foam sheet has specific morphology.

A non-conductive rubber hose is provided exhibiting lower conductivity compared to conventional EPDM hose, and reduced stiffness compared to conventional non-conductive thermoplastic hose. The hose is useful for applications such as in hydraulics for boom trucks, and for coolant in plasma cutting tools.