The present invention relates to a method for the manufacture of a hot-dip coated steel sheet coated with a zinc or an aluminum based coating including the provision of a specific steel sheet, a recrystallization annealing with specific heating, soaking and cooling sub-steps using an inert gas and a hot-dip coating; the hot dip coated steel sheet and the use of the hot-dip coated steel sheet.

Provided is a steel sheet having excellent image clarity after painting, including: carbon (C): 0.001% to 0.03%, silicon (Si): 0.001% to 0.35%, manganese (Mn): 0.05% to 2.2%, phosphorus (P): 0.003% to 0.1%, sulfur (S): 0.001% or 0.025%, aluminum (Al): 0.01% to 0.1%, nitrogen (N): 0.001% to 0.007%, and a remainder of iron (Fe) and inevitable impurities. The microstructure of the steel sheet mainly is ferrite phases. An R-cube texture of a surface layer of the steel sheet is 5% or less by area %.

A hot-dip coated steel product including: a steel product; and a coating layer including a Zn—Al—Mg alloy layer disposed on a surface of the steel product, in which the Zn—Al—Mg alloy layer includes a Zn phase, an Al phase, and a MgZn.sub.2 phase, and contains a Mg—Sn intermetallic compound phase in the Zn phase, and the coating layer has a chemical composition satisfying a predetermined average composition, a total area proportion of the Al phase and the MgZn.sub.2 phase is 70% or more, an area proportion of the Zn phase is 30% or less, an average value of cumulative circumferential lengths of the Al phase is less than 88 mm/mm.sup.2, and a total frequency in number of the Al phase having a circumferential length of 50 μm or more is less than 100.

The present invention provides an iron-aluminum-based plated steel sheet, and a manufacturing method therefor, the iron-aluminum-based plated steel sheet comprising a base steel sheet and a plated layer formed on the surface of the base steel sheet, wherein the alloy plated layer comprises: a diffusion layer comprising an Fe—Al-based intermetallic compound having a cubic structure; and an alloyed layer formed on the diffusion layer and composed of an alloy phase differing from that of the cubic structure, the thickness of the diffusion layer is 3-20 μm, and the thickness of the diffusion layer is greater than 50% of the total thickness of the plated layer.

A method of manufacturing a steel sheet plated with an Al—Fe alloy for hot forming. The method includes: aluminum-plating and coiling a base steel sheet to obtain an aluminum-plated steel sheet, where an amount of the aluminum-plating is 30 to 200 g/m.sup.2 based on one surface of the base steel sheet, and tension in the coiling is 0.5 to 5 kg/mm.sup.2; after the aluminum-plating, performing cooling to 250° C. at a rate of 20° C./sec or less; annealing the aluminum-plated steel sheet to obtain the steel sheet plated with the Al—Fe alloy; and cooling the steel sheet plated with the Al—Fe alloy. The annealing is carried out for 30 minutes to 50 hours within a heating temperature range of 550 to 750° C. in a batch annealing furnace.

An adhesive composition including an epoxy-based adhesive polymer and a phosphorous element-containing compound; a process for making the adhesive composition; a process for increasing the corrosion resistance property of the adhesive composition; and a process for bonding a metal substrate with the adhesive composition to increase the corrosion resistance of the substrate by at least 40 percent.

Provided is a plated steel to be used for automobiles, electric home appliances, building materials and the like and, more specifically, to a zinc alloy-plated steel having excellent corrosion resistance and surface smoothness, and a method for manufacturing the same.

A coated steel substrate has a steel substrate having a surface. A coating layer is atop the surface. The coating layer includes: aluminum activated by indium; and a ceramic binder. The coating also may comprise of multiple layers with different properties to facilitate the galvanic protection capability.

A method of forming a shaped steel object is provided. The method includes cutting a blank from an alloy composition including 0.05-0.5 wt. % carbon, 4-12 wt. % manganese, 1-8 wt. % aluminum, 0-0.4 wt. % vanadium, and a remainder balance of iron. The method also includes heating the blank until the blank is austenitized to form a heated blank, transferring the heated blank to a press, forming the heating blank into a predetermined shape to form a stamped object, and decreasing the temperature of the stamped object to a temperature between a martensite start (Ms) temperature of the alloy composition and a martensite final (Mf) temperature of the alloy composition to form a shaped steel object comprising martensite and retained austenite.

A device including a hard shield material; a layer including aluminum or copper; and a silicon layer having a first thickness is disclosed. The device can also include a silicon layer having a second thickness. A method of making the device is also disclosed.