A method for the manufacturing of an object. The method includes receiving a desired alloy composition for the object, depositing a plurality of foils in a stack to form the object, applying heat to the stack at a first temperature to bond the plurality of foils to each other, and applying heat to the stack at a second temperature to homogenize the composition of the stack. The homogenized stack has the desired alloy composition.

A part includes a sheet metal component having a predefined shape and at least one additively manufactured reinforcement deposited on, metallurgically bonded to, and extending along a surface of the sheet metal component. The at least one additively manufactured reinforcement can be a directed energy deposition (DED) reinforcement rib. Also, the at least one additively manufactured reinforcement can be deposited on the piece of sheet metal before the piece of sheet metal is formed into the predefined shape, or in the alternative, the at least one additively manufactured reinforcement can be deposited on the piece of sheet metal after the piece of sheet metal is formed into the predefined shape.

Process for manufacturing a multilayer strip or sheet, comprising the successive steps of: casting a brazing aluminum alloy in the form of a casting slab; sawing the casting slab to obtain sawn brazing alloy layers; bonding a core aluminum alloy layer with at least one sawn brazing aluminum alloy layer to obtain a multilayer assembly; preheating the multilayer assembly; hot-rolling the multilayer assembly to obtain a multilayer strip or sheet, the first hot-rolling pass inducing a reduction in thickness of the multilayer assembly greater than or equal to 0.5% of the thickness of the multilayer assembly before said hot-rolling pass.

An aluminum alloy brazing sheet has a 3XXX, 1XXX or 6XXX core, an interliner and a 4XXX brazing layer without added Mg. The interliner has Bi and Mg, the magnesium migrating to the surface of the brazing sheet during brazing and reducing the aluminum oxide to facilitate brazing without flux in a controlled inert atmosphere with reduced oxygen.

An adhesive composition including an epoxy-based adhesive polymer and a phosphorous element-containing compound; a process for making the adhesive composition; a process for increasing the corrosion resistance property of the adhesive composition; and a process for bonding a metal substrate with the adhesive composition to increase the corrosion resistance of the substrate by at least 40 percent.

An aluminum alloy brazing sheet used for brazing of an aluminum material in an inert gas atmosphere or in vacuum is formed of a two-layer material in which a brazing material and a core material are stacked. The core material is formed of an aluminum alloy and has a grain size of 20 to 300 μm, and the aluminum alloy contains Mn of 0.50 to 2.00 mass %, Mg of 0.40 to 2.00 mass %. Si of 1.50 mass % or less, Fe of 1.00 mass % or less, and Ti of 0.10 to 0.30 mass %, with the balance being aluminum and inevitable impurities. The brazing material is formed of an aluminum alloy containing Si of 4.00 to 13.00 mass % with the balance being aluminum and inevitable impurities. In a drop-type fluidity test, a ratio α (α=K.sub.a/K.sub.b) of a fluid coefficient K.sub.a is 0.50 or more.

An aluminum alloy brazing sheet used for brazing of an aluminum material in an inert gas atmosphere or in vacuum is formed of a two-layer material in which a brazing material and a core material are stacked in this order. The core material is formed of an aluminum alloy and has a grain size of 20 to 300 μm, and the aluminum alloy contains Mn of 0.50 to 2.00 mass %, Mg of 0.40 to 2.00 mass %, Si of 1.50 mass % or less, and Fe of 1.00 mass % or less, with the balance being aluminum and inevitable impurities. The brazing material is formed of an aluminum alloy containing Si of 4.00 to 13.00 mass % with the balance being aluminum and inevitable impurities, and, in a drop-type fluidity test, a ratio α (α=K.sub.a/K.sub.b) of a fluid coefficient K.sub.a is 0.50 or more.

In a brazing sheet manufacturing method, a cladding slab is prepared by overlaying at least a core-material slab composed of an aluminum material and a filler-material slab composed of an Al—Si series alloy, in which a metal element that oxidizes more readily than Al is included in at least one of the slabs. A clad sheet is prepared by hot rolling this cladding slab, which then has at least a core material layer composed of the core-material slab and a filler material layer composed of the filler-material slab and disposed on at least one side of the core material. Then, a surface of the clad sheet is etched using a liquid etchant that contains an acid. Subsequently, the clad sheet is cold rolled to a desired thickness. In flux-free brazing, such a brazing sheet is capable of curtailing degradation in brazeability caused by fluctuations in dew point and oxygen concentration.

An aluminum alloy brazing sheet including a core material and a brazing material provided on at least one surface of the core material. The brazing material includes 5.0-9.0 mass % Si, 0.10-0.90 mass % Mg, and 0.05-0.60 mass % Bi, and further includes at least one of 0.80 mass % or less Mn and 0.60 mass % or less Ti, with the remainder being Al and inevitable impurities.

An aluminum alloy brazing sheet has a 3XXX, 1XXX or 6XXX core, an interliner and a 4XXX brazing layer without added Mg. The interliner has Bi and Mg, the magnesium migrating to the surface of the brazing sheet during brazing and reducing the aluminum oxide to facilitate brazing without flux in a controlled inert atmosphere with reduced oxygen.