To provide a zirconia sintered body having both excellent translucency and bending strength, specifically a zirconia sintered body having both translucency and strength suitable as a denture for front tooth, and a process for its production. A translucent zirconia sintered body containing more than 4.0 mol % and at most 6.5 mol % of yttria and less than 0.1 wt % of alumina, and having a relative density of at least 99.82%, a total light transmittance of at least 37% and less than 40% to light with a wavelength of 600 nm at a thickness of 1.0 mm, and a bending strength of at least 500 MPa, and a process for its production.

A dental all-ceramic restoration and manufacturing method thereof; the outer surface of the dental all-ceramic restoration has neither visible marks remaining from the removal of the connecting bars (7) nor local grinding traces and chipping, and is smooth with uniform structure. The manufacturing method thereof is wet-forming or milling. No connecting bars are needed to connect the dental restoration bodies (3) with a surrounding mould blank or ceramic blank. This eliminates the need for manually cutting off the connecting bars (7) to separate the forming body from the surrounding ceramic blank, further grinding and polishing process to treat the excessively rough outer surface, and thereby reducing the risk of chipping and premature failure. In the manufacturing processes thereof, the hardened ceramic green body (2) made by wet-forming technique has more homogenous microstructure and less particle packing defects than the dry-pressed blanks and partially sintered blanks. Furthermore, higher surface smoothness can be obtained by milling unsintered hardened ceramic green body than by milling partially sintered blanks. The dental all-ceramic restoration has a high degree of surface finish, and can be directly used without polishing, veneering or glazing.

To provide a two-paste type sealer composition for root canal filling consisting of a first paste containing a polymer (a) of an acid group-containing polymerizable monomer in which a portion or the entirety of the acidic group in a molecule forms a salt with an alkaline metal, a non-acid reactive powder (b) and water (c), wherein the pH of the first paste is in the range from 3.5 to 5.5, and a second paste containing an acid reactive inorganic powder (d), water (c) and a thickener (e), wherein, a cured product of a kneaded material of the first paste and the second paste comprises 3 to 20 part by weight of the polymer (a), 15 to 60 part by weight of the water (c), and 30 to 70 part by weight of the acid reactive inorganic powder (d).

The invention refers to a method for producing a dental restoration comprising a lithium silicate glass or glass ceramic as well as a dental restoration inself. The invention further refers to a ingot with the same composition having a defined strength.

Body made of a ceramic material, the body having as an integral part thereof a surface region reaching from the surface of the body down to a predetermined depth. According to the invention, the surface region is enriched with a magnesium component thereby forming a hydrophilic surface area.

A method for decreasing dental hypersensitivity, including sizing a plurality of non-functionalized microbeads to be between 0.01 μm to 3 μm in diameter, suspending the plurality of non-functionalized microbeads in a fluid matrix to define a dental delivery composition, introducing the dental delivery composition into an oral cavity, introducing respective non-functionalized microbeads into a dental tubule, adhering respective functionalized microbeads each other and to the dental tubule to define an aggregate, and occluding the dental tubule with the aggregate.

The present invention relates to a kit of parts comprising a dental mill blank comprising a porous zirconia material and a colouring solution for colouring the porous zirconia material. The porous zirconia material comprises Zr oxide calculated as ZrO2: from 80 to 97 wt.-%, Al oxide calculated as Al2O3: from 0 to 0.15 wt.-%, Y oxide calculated as Y2O3: from 1 to 10 wt.-%, Bi oxide calculated as Bi2O3: from 0.01 to 0.2 wt.-%, the porous zirconia material not comprising Fe calculated as Fe2O3 in an amount of more than 0.01 wt.-%, wt.-% with respect to the weight of the porous zirconia material. The colouring solution comprises solvent(s), colouring agent(s) comprising metal ions selected from Tb, Er, Pr, Mn or combinations thereof, the solution not comprising Fe ions in an amount of more than 0.01 wt.-%, the solution not comprising Bi ions in an amount of more than 0.01 wt.-%, wt.-% with respect to the weight of the colouring solution. The invention also relates to a process of producing a dental restoration, the process comprising the steps: providing a dental mill blank comprising a porous zirconia material as described in any of the preceding claims, machining an article out of the porous zirconia material, the article having the shape of a dental restoration with an outer and inner surface, providing a colouring solution as described in any of the preceding claims, applying the colouring solution to at least portions of the surface of the article having the shape of a dental restoration.

A prosthesis that contains zirconia and supplements a defective portion of a natural bone, and that is changed to a color approximate to that of the natural bone by a heat treatment after a γ-ray sterilization treatment. The color approximate to that of the natural bone has an L* value of 60 to 90, an a* value of −5 to 10, and a b* value of −5 to 10 in the L*a*b* color space. The highest temperature in the heat treatment is 100° C. to 300° C. The prosthesis is a fixture of a dental implant embedded into and bonded to a natural bone, an abutment, an implant crown, and the like.

Described herein is a dental filler material having a core made of a core material and a shell made of a shell material, where the shell material coats or covers at least a portion of the core.

The invention relates to a screw and corresponding screw driver for driving the screw into a dental implant at an angle from the longitudinal axis of the implant. The screw has a polygonal interface and the screw driver has a matching interface for driving the screw to rotate.