The present invention discloses a microcrystalline glass, a microcrystalline glass product, and a manufacturing method therefor. The main crystal phase of the microcrystalline glass comprises lithium silicate and a quartz crystal phase. The haze of the microcrystalline glass of the thickness of 0.55 mm is below 0.6%. The microcrystalline glass comprises the following components in percentage by weight: SiO.sub.2: 65-85%; Al.sub.2O.sub.3: 1-15%; Li.sub.2O: 5-15%; ZrO.sub.2: 0.1-10%; P.sub.2O.sub.5: 0.1-10%; K.sub.2O: 0-10%; MgO: 0-10%; ZnO: 0-10%. A four-point bending strength of the microcrystalline glass product is more than 600 Mpa.

The present invention provides a microcrystalline glass product. The microcrystalline glass product includes the following components in percentage by weight: SiO.sub.2: 45-70%; Al.sub.2O.sub.3: 8-18%; Li.sub.2O: 10-25%; ZrO.sub.2: 5-15%; P.sub.2O.sub.5: 2-10%; and Y.sub.2O.sub.3: greater than 0 but less than or equal to 8%. Through reasonable component design, the microcrystalline glass and the microcrystalline glass product obtained in the present invention have excellent mechanical and optical properties and are suitable for electronic devices or display devices.

A chemically strengthened bioactive glass-ceramic composition as defined herein. Also disclosed are methods of making and using the disclosed compositions.

To provide An Al.sub.2O.sub.3-free dental lithium silicate glass composition comprising the following components: SiO.sub.2: 60.0 to 80.0% by weight Li.sub.2O: 10.0 to 17.0% by weight K.sub.2O: 0.5 to 10.0% by weight a nucleating agent: 1.0 to 6.0% by weight a colorant: 0.0 to 10.0% by weight, and, a metal oxide Me(tetravalent)O.sub.2: 5.0 to 10.0% by weight.

ZrO.sub.2-toughened glass ceramics having high molar fractions of tetragonal ZrO.sub.2 and fracture toughness value of greater than 1.8 MPa.Math.m.sup.1/2. The glass ceramic may also include also contain other secondary phases, including lithium silicates, that may be beneficial for toughening or for strengthening through an ion exchange process. Additional second phases may also decrease the coefficient of thermal expansion of the glass ceramic. A method of making such glass ceramics is also provided.

The present invention discloses a glass-ceramic article and a glass-ceramic for an electric device cover plate, the glass-ceramic comprises, as a predominant crystalline phase, lithium silicate and the quartz crystalline phase, and has a composition expressed in weight percent including: SiO.sub.2: 65-85%, Al.sub.2O.sub.3: 1-15%, Li.sub.2O: 5-15%, ZrO.sub.2: 0.1-10%, P.sub.2O.sub.5: 0.1-10%, K.sub.2O: 0-10%, MgO: 0-10%, ZnO: 0-10%, and Na.sub.2O: 0-5%, wherein (SiO.sub.2+Al.sub.2O.sub.3+Li.sub.2O+ZrO.sub.2)/P.sub.2O.sub.5 is 40-90, the falling ball test height is 700 mm or more. By reasonable component design, the present invention achieves excellent mechanical properties of the glass-ceramic and the glass-ceramic article of the present invention and obtains the glass-ceramic or the glass-ceramic article suitable for electronic devices at a lower cost.

A chemically strengthened bioactive glass-ceramic composition as defined herein. Also disclosed are methods of making and using the disclosed compositions.

The application relates to bond materials for a grinding wheel, in particular a glass ceramic and a preparation method thereof, and a bond for the composite grinding wheel. The glass ceramic is prepared from raw materials comprising kaolin, silica, diboron trioxide, lithium superoxide, albite, potassium feldspar, talc, dolomite, phosphorus pentoxide, and yttrium oxide. A glass ceramic composed entirely of microcrystalline phases is obtained from the glass prepared by the above raw materials at 900-1020 C., achieving a complete conversion of the glass phase at a low temperature. The application also provides a bond for a composite grinding wheel, comprising glass ceramic and glass with mass ratio of (20-50):(50-80), the glass phase having a low flow temperature and, together with the glass ceramic phase, forming encapsulation of the abrasive particles, realizing low-temperature sintering of the grinding wheel. Microcrystalline phase in the bond results in high mechanical strength for the obtained grinding wheel.

The invention relates to glass articles suitable for use as electronic device housing/cover glass which comprise a glass ceramic material. Particularly, a cover glass comprising an ion-exchanged glass ceramic exhibiting the following attributes (1) optical transparency, as defined by greater than 90% transmission at 400-750 nm; (2) a fracture toughness of greater than 0.6 MPa.Math.m.sup.1/2; (3) a 4-point bend strength of greater than 350 MPa; (4) a Vickers hardness of at least 450 kgf/mm.sup.2 and a Vickers median/radial crack initiation threshold of at least 5 kgf; (5) a Young's Modulus ranging between about 50 to 100 GPa; (6) a thermal conductivity of less than 2.0 W/m C., and (7) and at least one of the following attributes: (i) a compressive surface layer having a depth of layer (DOL) greater and a compressive stress greater than 400 MPa, or, (ii) a central tension of more than 20 MPa.

The present invention relates to a precision component and also to a glass-ceramic which can be used for producing the precision component.