A modified UZM-14 zeolite is described. The modified UZM-14 zeolite has a Modification Factor of 6 or more. The modified UZM-14 zeolite may have one or more of: a Si/Al.sub.2 ratio of 14 to 30; a total pore volume in a range of 0.5 to 1.0 cc/g; at least 5% of a total pore volume being mesopores having a diameter of 10 nm of less; a cumulative pore volume of micropores and mesopores having a diameter of 100 Å or less of 0.25 cc/g or more; or a Collidine IR Bronsted acid site distribution greater than or equal to an area of 3/mg for a peak in a range of 1575 to 1700 cm.sup.−1 after desorption at 150° C. Processes of making the modified UZM-14 zeolite and transalkylation processes using the modified UZM-14 zeolite are also described.

A MXene support for a noble metal that forms a catalyst having active sites comprising single metal-layer nanostructures. The catalyst is stable under conditions for methane conversion to higher hydrocarbons and provides reduced coke formation. The results show a supported metal catalyst using the MXene where Pt atoms form one or more layers of atoms on the surface of the Mo.sub.2TiC.sub.2T.sub.x support after it is reduced at 750° C. The catalyst shows high selectivity for C.sub.2-hydrocarbons with reduced coke formation, which can cost effectively convert methane into other valuable products.

The present invention relates to a catalyst for producing olefins from dehydrogenation of alkane having 2 to 5 carbon atoms and a method for producing olefins using said catalyst, wherein said catalyst comprises a hierarchical zeolite nanosheet having a silica to alumina (SiO.sub.2/AI.sub.2O.sub.3) ratio more than 120 and group X metal(s) in a range of 0.3 to 5% by weight. The catalyst according to the conversion of precursor to yields and high olefins selectivity.

A hydrocarbon feed stream, particularly one comprising heavier hydrocarbons, may be converted to valuable products such as motor gasoline and/or lubricating oil by employing one or more large pore zeolitic catalysts, which may be prepared from a precursor zeolite. In some examples, a large pore zeolitic catalyst may be utilized to selectively reduce the endpoint of a hydrocarbon composition.

In a method, device, catalyst and a method for producing a catalyst for the catalytic conversion of a substance mixture containing glycerol to propanol in a fixed-bed reactor, substrates of the catalyst have inorganic materials and/or metal oxides. The substrates have a pore diameter at the surface of between 10 and 25 angstroms, preferably between 12 and 20 angstroms, particularly preferably 15 angstroms.

Metal-organic framework materials (MOFs) are highly porous entities comprising a multidentate organic ligand coordinated to multiple metal centers. MOFs having ambient condition stability may comprise a plurality of metal clusters comprising one or more M.sub.4O clusters (M is a metal), and a plurality of 4-pyrazolecarboxylate ligands coordinated to the plurality of metal clusters to define an at least partially crystalline network structure having a plurality of internal pores. The MOFs may have a Pa3 symmetry, which upon activation may convert into Fm3m symmetry. Methods for synthesizing the MOFs may comprise combining a metal source, such as a preformed metal cluster, with 4-pyrazolecarboxylic acid, and reacting the preformed metal cluster with the 4-pyrazolecarboxylic acid to form a MOF having an at least partially crystalline network structure with a plurality of internal pores defined therein and comprising a plurality of metal clusters coordinated to a multidentate organic ligand comprising 4-pyrazolecarboxylate.

Incorporating a bimetal to a lamellar MFI zeolite structure includes providing a bimetallic-incorporated lamellar zeolite catalyst including a sodium source, aluminum source, silicon source, surfactant, sulfuric acid, deionized water, metal source, and molecular template; dissolving the sodium source in the deionized water creating a basic solution; adding the sulfuric acid, aluminum source, molecular template, and silicon source to the basic solution creating a mixture and adding the metal source to the mixture; dissolving the surfactant in the deionized water creating a surfactant solution; combining the surfactant solution and basic solution; heating the combined surfactant solution and basic solution in a rotating autoclave creating a metal-containing zeolite including the surfactant and molecular template in a structure of the metal-containing zeolite; removing a synthesized zeolite from the autoclave; drying the synthesized zeolite and creating a dry zeolite powder; calcining the dry zeolite powder creating a bimetal-containing lamellar MFI zeolite for chemical activation.

A catalyst for preparing a synthesis gas includes: a mesoporous Al.sub.2O.sub.3 support including mesopores having a pore size of about 1 nm to about 30 nm; metal nanoparticles supported in the mesopores of the mesoporous Al.sub.2O.sub.3 support wherein the metal nanoparticles have a particle size of less than or equal to about 20 nm; and a metal oxide coating layer including particles wherein the metal oxide coating layer is coated on the surface of the mesoporous Al.sub.2O.sub.3 support and includes mesopores having a pore size of about 2 nm to about 50 nm.

The present invention relates to a process for producing a diene, preferably a conjugated diene, more preferably 1,3-butadiene, comprising the dehydration of at least one alkenol having a number of carbon atoms greater than or equal to 4, in the presence of a catalytic material comprising at least one crystalline metalosilicate in acid form, preferably a macroporous zeolite, more preferably a zeolite with a FAU, BEA or MTW structure. Preferably, said alkenol having a number of carbon atoms greater than or equal to 4 may be obbtained directly through biosynthetic processes, or through catalytic dehydration processes of at least one diol. When said alkenol is a butenol, said diol is preferably a butanediol, more preferably 1,3-butanediol, even more preferably bio-1,3-butanediol, i.e. 1,3-butanediol deriving from biosynthetic processes. When said alkenol is 1,3-butanediol, or bio-1,3-butanediol, the diene obtained with the process according to the present invention is, respectively, 1,3-butadiene, or bio-1,3-butadiene.

A porous substrate susceptible to one or both of hydroxylation and alkoxylation by a first protic solvent is exposed to a first relative pressure of the first protic solvent. The porous substrate includes a first plurality of pores having a first average pore diameter and a second plurality of pores having a second average pore diameter that is greater than the first average pore diameter. The first relative pressure is effective to one or both of hydroxylate or alkoxylate substantially only pores of the first average pore diameter to form a first modified porous substrate. The first modified porous substrate is reacted with a first functionalizing reagent that is effective to functionalize one or both of hydroxylated or alkoxylated surfaces, thereby functionalizing substantially only the first plurality of the pores, to form a first functionalized porous substrate.