A virus removal membrane includes cellulose, and a primary-side surface through which the protein-containing solution is to be applied and a secondary-side surface from which a permeate that has permeated the virus removal membrane is to be flowed, wherein a bubble point is 0.5 MPa or more and 1.0 MPa or less; and when a solution containing gold colloids having a diameter of 30 nm is applied through the primary-side surface to the virus removal membrane to allow the virus removal membrane to capture the gold colloids for measurement of brightness in a cross section of the virus removal membrane, a value obtained by dividing a standard deviation of a value of an area of a spectrum of variation in the brightness by an average of the value of the area of the spectrum of variation in the brightness is 0.01 or more and 0.30 or less.

Polymer-based membranes and methods for fabricating membranes are described. The methods include forming a casting solution featuring a polyvinylidene fluoride (PVDF)-based solvent and a polyvinylpyrrolidone (PVP)-based modifying agent, dispersing the casting solution to form a first element, generating a plurality of active sites on a surface of the first element, and forming a polymer-based membrane by exposing the surface of the first element to a fluorosilane composition to form a fluorosilane layer on the surface, where the fluorosilane composition includes a silane compound having at least one alkyl substituent that includes between 9 and 21 fluorine atoms.

The invention relates to the providing of hydrophobic and hydrophilic polymer-based hollow fiber membranes containing a water-insoluble antioxidant; in particular, the invention relates to the providing of hollow fiber membranes for the extracorporeal treatment of blood, wherein the hollow fiber membranes have improved biocompatibility relative to treatment blood, in particular improved complement activation and lower platelet loss vis-à-vis treatment blood. At the same time, the elution of hydrophilic polymers from the lumen of the hollow fiber membrane is reduced.

A carbon molecular sieve (CMS) membrane having improved separation characteristics for separating olefins from their corresponding paraffins is comprised of carbon with at most trace amounts of sulfur and a group 13 metal. The CMS membrane may be made by pyrolyzing a precursor polymer devoid of sulfur in which the precursor polymer has had a group 13 metal incorporated into it, wherein the metal is in a reduced state. The pyrolyzing for the precursor having the group 13 metal incorporated into it is performed in a nonoxidizing atmosphere and at a heating rate and temperature such that the metal in a reduced state (e.g., covalently bonded to carbon or nitrogen or in the metal state).

The invention relates to a method for manufacturing a hollow fiber membrane bundle from a plurality of polysulfone and PVP-based hollow fiber membranes which encompasses the providing of a spinning solution comprising a polysulfone-based material, in particular polysulfone, a vinylpyrrolidone-based polymer, in particular polyvinylpyrrolidone, an aprotic solvent, in particular dimethylacetamide, providing a coagulant liquid comprising water and an aprotic solvent, in particular dimethylacetamide, co-extruding the spinning solution and the coagulant liquid through a concentric annular spinneret into a hollow strand, whereby the cavity of the strand is filled with coagulant liquid, conducting the strand through a precipitation gap, introducing the strand into a precipitating bath comprised substantially of water so as to obtain a hollow fiber membrane, conducting the hollow fiber membranes through at least one rinsing bath and drying the hollow fiber membrane obtained, arranging the resulting hollow fiber membranes into a hollow fiber membrane bundle, and treating the hollow fiber membrane bundle with water vapor.

Provided is a porous hollow fiber membrane made of a thermoplastic resin, wherein a membrane thickness is 0.050 mm or larger and 0.25 mm or smaller, and when a strength coefficient is defined as K=(compressive strength)/((membrane thickness)/(inside diameter/2)).sup.3, K=1.7 or more.

Provided herein are one-step methods for fabricating an asymmetric mixed-matrix membrane and the asymmetric mixed matrix membrane so fabricated. In the one step method an asymmetric polymer film is formed from a liquid polymer solution and a ligand precursor simultaneously with the formation of metal-organic framework filler particles therein. Also provided is a method for separating a mixture of gases or of liquids by flowing the mixture through the asymmetric mixed matrix membrane.

The invention is in the field of methods for preparing polymer films, and of such polymer films. The method involves phase separation and requires only aqueous solution, eliminating the need for organic solvents. The aqueous phase separation involves contacting a polymer solution comprising a trigger-responsive polymer with an aqueous coagulation solution in which the trigger-responsive polymer is not soluble.

The present invention provides a porous hollow fiber membrane including a polysulfone-based polymer and a hydrophilic polymer, and having a dense layer in a section from an outer surface portion to a center region of a membrane thickness, a thickness of the dense layer being 10 to 30 μm, and a ratio of a pore having a pore size of more than 50 nm and a ratio of a pore having a pore size of 10 nm or smaller in the dense layer being 25 to 40% and 20% or less, respectively.

The disclosure provides a method for preparing a hollow fiber membrane by melt spinning-stretching and selective swelling, including: preparing a nascent hollow fiber by melt spinning in an inert gas protective atmosphere by using an amphiphilic block copolymer as a film forming material, and stretching the nascent hollow fiber in the cooling process, a stretch rate being controlled at 200-540 mm/min, and a stretch ratio being controlled at 150-600%; immersing the obtained hollow fiber in a swelling solvent, and treating the hollow fiber in a water bath at 65° C. for 1 h; and then transferring the hollow fiber into a long-chain alkane solvent, treating the hollow fiber at the same temperature for 1-12 h, and after the completion of the treatment, immediately taking out the hollow fiber and drying the hollow fiber to obtain the hollow fiber membrane with a bicontinuous porous structure. By combining the melt spinning-stretching and the selective swelling, the method of the disclosure can synchronously and continuously improve the permeability and selectivity of the hollow fiber membrane. The treatment in the long-chain alkane solvent can make the polar chain excessively enriched on the surface of the membrane migrate inward, thereby improving the performance of the hollow fiber membrane.