A catalyst and a process for using the catalyst are presented. The catalyst is a heterogeneous catalyst and includes active metal halides bonded to functional groups. The functional groups are bonded to a polymeric backbone to form the structure supporting the catalyst. The catalyst is useful for the dimerization of acetylene to convert the acetylene to a larger hydrocarbon, and in particular to dimerize acetylene to vinylacetylene.

A catalyst and a process for using the catalyst are presented. The catalyst is a heterogeneous catalyst and includes active metal halides bonded to functional groups. The functional groups are bonded to a polymeric backbone to form the structure supporting the catalyst. The catalyst is useful for the dimerization of acetylene to convert the acetylene to a larger hydrocarbon, and in particular to dimerize acetylene to vinylacetylene.

A catalysator element comprising a mixed metal oxide compound for conversion of nitrogen oxides (NO.sub.x). Methods for the preparation of the present mixed metal oxide compound for use in the present catalysator element and to exhaust systems for a combustion engine comprising the present catalysator element for conversion of (NO.sub.x) in exhaust gasses. Specifically, a catalysator element for conversion of nitrogen oxides (NOx) comprises a solid support coated with a calcined mixed metal oxide hydrotalcite-like compound. The calcined mixed metal oxide hydrotalcite-like compound comprises at least one bivalent metal (M.sup.2+) and at least one trivalent metal (M.sup.3+).

A hydrothermal method of preparing uniform, monodisperse ceramic lanthanum hydroxyl carbonate (LaCO.sub.3OH) having cherry-blossom-like nanogears and/or nanocubes is described. The method produced a hexagonal crystal with a crystal lattice in which at least on lanthanum ion is substituted with calcium ion. The ceramic nanoparticles produced by the method are good catalyst for the reduction of nitrogen oxides with a hydrocarbon. A method of reducing exhaust gases is described.

A hydrothermal method of preparing uniform, monodisperse ceramic lanthanum hydroxyl carbonate (LaCO.sub.3OH) having cherry-blossom-like nanogears and/or nanocubes is described. The method produced a hexagonal crystal with a crystal lattice in which at least on lanthanum ion is substituted with calcium ion. The ceramic nanoparticles produced by the method are good catalyst for the reduction of nitrogen oxides with a hydrocarbon. A method of reducing exhaust gases is described.

A hydrothermal method of preparing uniform, monodisperse ceramic lanthanum hydroxyl carbonate (LaCO.sub.3OH) having cherry-blossom-like nanogears and/or nanocubes is described. The method produced a hexagonal crystal with a crystal lattice in which at least on lanthanum ion is substituted with calcium ion. The ceramic nanoparticles produced by the method are good catalyst for the reduction of nitrogen oxides with a hydrocarbon. A method of reducing exhaust gases is described.

A hydrothermal method of preparing uniform, monodisperse ceramic lanthanum hydroxyl carbonate (LaCO.sub.3OH) having cherry-blossom-like nanogears and/or nanocubes is described. The method produced a hexagonal crystal with a crystal lattice in which at least on lanthanum ion is substituted with calcium ion. The ceramic nanoparticles produced by the method are good catalyst for the reduction of nitrogen oxides with a hydrocarbon. A method of reducing exhaust gases is described.

The present disclosure relates to a method for producing lanthanide doped layered double hydroxides (Ln-doped LDHs). The method includes the steps of preparing a carbonate free alkaline solution; preparing a solution of metal salts comprising a salt of a lanthanide; co-precipitating the alkaline solution and the solution of metal salts to form a mixture and Ln-doped LDH precipitate wherein the pH of the mixture is maintained at a constant value; aging the precipitate; and separating the precipitate from the solution. The alkaline solution is an aqueous ammonia solution. The present disclosure is also related to lanthanide-doped layered double hydroxides (La-doped LDHs) obtainable by such a method, as well as to the use of the lanthanide-doped layered double hydroxides obtainable by such a method.

The present disclosure relates to a method for producing lanthanide doped layered double hydroxides (Ln-doped LDHs). The method includes the steps of preparing a carbonate free alkaline solution; preparing a solution of metal salts comprising a salt of a lanthanide; co-precipitating the alkaline solution and the solution of metal salts to form a mixture and Ln-doped LDH precipitate wherein the pH of the mixture is maintained at a constant value; aging the precipitate; and separating the precipitate from the solution. The alkaline solution is an aqueous ammonia solution. The present disclosure is also related to lanthanide-doped layered double hydroxides (La-doped LDHs) obtainable by such a method, as well as to the use of the lanthanide-doped layered double hydroxides obtainable by such a method.

Provided is a formed body containing at least one carbonate compound (A1) selected from Na.sub.2CO.sub.3 or K.sub.2CO.sub.3, the formed body having a volume of pores with a pore diameter of from 0.05 m to 10 m of from 0.10 mL/g to 0.30 mL/g and a crushing strength of from 1.8 kgf to 10.0 kgf.