A method for producing an oligosilane which includes a reaction step of producing an oligosilane by dehydrogenative coupling of hydrosilane. The reaction step is carried out in the presence of a catalyst containing at least one transition element selected from the group consisting of Periodic Table group 3 transition elements, group 4 transition elements, group 5 transition elements, group 6 transition elements, and group 7 transition elements. Also disclosed is a method for producing a catalyst for dehydrogenative coupling that produces an oligosilane by dehydrogenative coupling of hydrosilane.

Methods of simultaneously converting butanes and methanol to olefins over Ti-containing zeolite catalysts are described. The exothermicity of the alcohols to olefins reaction is matched by endothermicity of dehydrogenation reaction of butane(s) to light olefins resulting in a thermo-neutral process. The Ti-containing zeolites provide excellent selectivity to light olefins as well as exceptionally high hydrothermal stability. The coupled reaction may advantageously be conducted in a staged reactor with methanol/DME conversion zones alternating with zones for butane(s) dehydrogenation. The resulting light olefins can then be reacted with iso-butane to produce high-octane alkylate. The net result is a highly efficient and low cost method for converting methanol and butanes to alkylate.

A catalytic proppant and methods for making and using same are disclosed herein. The catalytic proppant can include a proppant support containing silica and alumina. The proppant support can have a macropore concentration of about 15% to about 45%, a mesopore concentration of about 20% to 50%, and a micropore concentration of about 8% to about 30% based on the total pore volume of the proppant support. The proppant support can also have a surface area of about 0.5 m.sup.2/g to about 50 m.sup.2/g. The catalytic proppant can have a long term permeability at 7,500 psi of at least about 10 D in accordance with ISO 13503-5.

A method of making a multifunctional catalyst for upgrading pyrolysis oil includes contacting a zeolite support with a solution including at least a first metal catalyst precursor and a second metal catalyst precursor, the first metal catalyst precursor, the second metal catalyst precursor, or both, including a heteropolyacid. Contacting the zeolite support with the solution deposits or adsorbs the first metal catalyst precursor and the second catalyst precursor onto outer surfaces and pore surfaces of the zeolite support to produce a multifunctional catalyst precursor. The method further includes removing excess solution from the multifunctional catalyst precursor and calcining the multifunctional catalyst precursor to produce the multifunctional catalyst comprising at least a first metal catalyst and a second metal catalyst deposited on the outer surfaces and pore surfaces of the zeolite support.

A method of making a multifunctional catalyst for upgrading pyrolysis oil includes contacting a hierarchical mesoporous zeolite support with a solution including at least a first metal catalyst precursor and a second metal catalyst precursor, each or both of which may include a heteropolyacid. The hierarchical mesoporous zeolite support may have an average pore size of from 2 nm to 40 nm. Contacting the hierarchical mesoporous zeolite support with the solution deposits or adsorbs the first metal catalyst precursor and the second catalyst precursor onto outer surfaces and pore surfaces of the hierarchical mesoporous zeolite support to produce a multifunctional catalyst precursor. The method further includes removing excess solution and calcining the multifunctional catalyst precursor to produce the multifunctional catalyst comprising at least a first metal catalyst and a second metal catalyst deposited on the outer surfaces and pore surfaces of the hierarchical mesoporous zeolite support.

A process for converting a feedstock comprising an organic compound to a conversion product by contacting said feedstock at organic compound conversion conditions with a catalyst comprising a mordenite zeolite having a mesoporous surface area of greater than 30 m.sup.2/g and an average primary crystal size as measured by TEM of less than 80 nm.

Embodiments of zeolite composite catalysts and methods of producing the zeolite composite catalysts are provided, where the methods comprise dissolving in an alkaline solution a catalyst precursor comprising at least one mesoporous zeolite while heating, stirring, or both to yield a dissolved zeolite solution, where the mesoporous zeolite has a molar ratio of SiO.sub.2/Al.sub.2O.sub.3 of at least 30, where the mesoporous zeolite comprises zeolite beta, adjusting the pH of the dissolved zeolite solution, aging the pH adjusted dissolved zeolite solution to yield solid zeolite composite from the dissolved zeolite solution, and calcining the solid zeolite composite to produce the zeolite composite catalyst, where the zeolite composite catalyst has a mesostructure comprising at least one disordered mesophase and at least one ordered mesophase, and where the zeolite composite catalyst has a surface area defined by the Brunauer-Emmett-Teller (BET) analysis of at least 600 m.sup.2/g.

The present invention relates to a process for producing monoaromatic hydrocarbons from a hydrocarbon feed comprising polyaromatics, the process comprising contacting said feed in the presence of hydrogen with a M/zeolite catalyst under hydrocracking process conditions.

The present invention relates to a process for producing monoaromatic hydrocarbons from a hydrocarbon feed comprising polyaromatics, the process comprising contacting said feed in the presence of hydrogen with a M/A/zeolite catalyst under hydrocracking process conditions.

The present invention provides an iron-loaded aluminosilicate zeolite having a maximum pore opening defined by eight tetrahedral atoms and having the framework type CHA, AEI, AFX, ERI or LTA, wherein the iron (Fe) is present in a range of from about 0.5 to about 5.0 wt. % based on the total weight of the iron-loaded aluminosilicate zeolite, wherein an ultraviolet-visible absorbance spectrum of the iron-loaded synthetic aluminosilicate zeolite comprises a band at approximately 280 nm, wherein a ratio of an integral, peak-fitted ultraviolet-visible absorbance signal measured in arbitrary units (a.u.) for the band at approximately 280 nm to an integral peak-fitted ultraviolet-visible absorbance signal measured in arbitrary units (a.u.) for a band at approximately 340 nm is >about 2. The present invention further provides a method of making an metal-loaded aluminosilicate zeolite having a maximum pore opening defined by eight tetrahedral atoms from pre-existing aluminosilicate zeolite crystallites, wherein the metal is present in a range of from 0.5 to 5.0 wt. % based on the total weight of the metal-loaded aluminosilicate zeolite.