A catalyst for a selective conversion of hydrocarbons. The catalyst includes a first component selected from the group consisting of Group VIII noble metals and mixtures thereof, a second component selected from the group consisting of alkali metals or alkaline-earth metals and mixtures thereof, and a third component selected from the group consisting of tin, germanium, lead, indium, gallium, thallium and mixtures thereof. The catalyst is a support formed as a spherical catalyst particle with a median diameter between 1.6 mm and 2.5 mm and an apparent bulk density between 0.6 and 0.3 g/cc. Also a process of using such a catalyst for a selective hydrocarbon conversion reaction and a process for regenerating such a catalyst by removing coke from same.

Shaped porous carbon products and processes for preparing these products are provided. The shaped porous carbon products can be used, for example, as catalyst supports and adsorbents. Catalyst compositions including these shaped porous carbon products, processes of preparing the catalyst compositions, and various processes of using the shaped porous carbon products and catalyst compositions are also provided.

A catalyst for a selective conversion of hydrocarbons. The catalyst includes a first component selected from the group consisting of Group VIII noble metals and mixtures thereof, a second component selected from the group consisting of alkali metals or alkaline-earth metals and mixtures thereof, and a third component selected from the group consisting of tin, germanium, lead, indium, gallium, thallium and mixtures thereof. The catalyst is a support formed as a spherical catalyst particle with a median diameter between 1.6 mm and 2.5 mm and an apparent bulk density between 0.6 and 0.3 g/cc. Also a process of using such a catalyst for a selective hydrocarbon conversion reaction and a process for regenerating such a catalyst by removing coke from same.

The invention relates to CuAlMn shaped catalyst bodies in extruded form, and to a process for their preparation. The shaped catalyst body is suitable for the hydrogenation of organic compounds containing a carbonyl function, in particular for the hydrogenation of aldehydes, ketones and carboxylic acids and/or their esters. In particular, the shaped catalyst body is suitable for the hydrogenation of fatty acids or their esters, such as fatty acid methyl esters, to form the corresponding alcohols and dicarboxylic acid anhydrides, such as maleic anhydride, or esters of di-acids and di-alcohols, such as butane diol.

Process for preparing a hydrocracking catalyst carrier which process comprises subjecting a carrier comprising an amorphous binder and zeolite Y having a silica to alumina molar ratio of at least 10 to calcination at a temperature of from 700 to 900 C., hydrocracking catalyst carrier comprising amorphous binder and zeolite Y having a silica to alumina molar ratio of at least 10, the infrared spectrum of which catalyst has a peak at 3690 cm.sup.1, substantially reduced peaks at 3630 cm.sup.1 and 3565 cm.sup.1 and no peak at 3600 cm.sup.1, hydrocracking catalyst carrier comprising an amorphous binder and zeolite Y having a silica to alumina molar ratio of at least 10, which catalyst has an acidity as measured by exchange with perdeuterated benzene of at most 20 micromole/gram, hydrocracking catalyst derived from such carrier and hydrocracking process with the help of such catalyst.

The present invention provides catalyst comprising metal modified zeolite, particularly Group IIIA or Group IIB metal modified zeolite, or a Group IIIA metal and Group IIB metal modified zeolite for reforming of heart cut naphtha stream. The present disclosure also relates to a process for synthesis of the catalyst. The present disclosure further relates to a process for reforming of heart cut naphtha stream, with high selectivity towards aromatics and good activity using the catalytic system, in the absence of hydrogen.

An enzyme immobilized on a porous structure can oxidize phenol compounds.

Fischer-Tropsch process for the synthesis of hydrocarbons by bringing a feedstock including synthesis gas into contact with a catalyst prepared by the following: a porous support is brought into contact with a cobalt metal salt of which the melting point of the cobalt metal salt is between 30 and 150 C. for between 5 minutes and 5 hours, in order to form a solid mixture, the weight ratio of said cobalt metal salt to the porous oxide support being between 0.1 and 1; the solid mixture obtained is heated with stirring under atmospheric pressure at a temperature between the melting point of the cobalt metal salt and 200 C. for a period of time of between 30 minutes and 12 hours; the solid obtained is calcined at a temperature above 200 C. and below or equal to 1100 C.

Shaped porous carbon products and processes for preparing these products are provided. The shaped porous carbon products can be used, for example, as catalyst supports and adsorbents. Catalyst compositions including these shaped porous carbon products, processes of preparing the catalyst compositions, and various processes of using the shaped porous carbon products and catalyst compositions are also provided.

The invention relates to a method for producing a pellet, in particular for a catalytic convertor and/or static mixer. The method comprises a trimming and/or deforming of at least one layer of metal foam material into a pellet shape.