The present invention provides a metal foam production method that enables a foaming process to be performed at low cost and enables controlling of the shape of metal foam. According to the present invention, a mold that transmits light and a precursor prepared by mixing a metal with a foaming agent are used, and a metal foam is produced by irradiating the precursor with a light transmitted through the mold to thereby heat and foam the precursor so as to obtain a metal foam, while controlling the shape of the metal foam by the mold.

Provided is a method for producing a sliding member formed by impregnating a porous base member made of a bronze-based alloy with a resin material, the sliding member including a sliding surface where both the porous base member and the resin material are exposed, the method including: a step of preparing a back metal layer; a porous base member formation step of forming the porous base member by depositing particles of the bronze-based alloy on a surface of the back metal layer and sintering the particles; an impregnation step of impregnating the porous base member with the resin material; a deformation step of deforming an end edge of the back metal layer in a direction away from the sliding surface; and a cutting step of cutting the porous base member impregnated with the resin material to form the sliding surface.

A display apparatus includes a display panel to display an image and a cushion plate disposed under the display panel. The cushion plate has an adhesive member and a porous member including a body portion area and a side portion area disposed along a side face of the body portion area. A thickness of the side portion area is smaller than a thickness of the body portion area. A porosity of the side portion area is lower than a porosity of the body portion area.

A display apparatus includes a display panel to display an image and a cushion plate disposed under the display panel. The cushion plate has an adhesive member and a porous member including a body portion area and a side portion area disposed along a side face of the body portion area. A thickness of the side portion area is smaller than a thickness of the body portion area. A porosity of the side portion area is lower than a porosity of the body portion area.

In a method of manufacturing open-cell bodies, individual parts of an open pore plastic in a size which corresponds to the size of the bodies to be manufactured while taking account of the shrinkage on a sintering or an open pore plastic element having predetermined break points which take account of the size and geometrical design of bodies to be manufactured are/is in filtrated and coated with a suspension in which at least one powdery material is contained. Organic components are expelled after a first heat treatment. Subsequently, a sintering is carried out. Parts of porous plastic provided with the suspension are separated before the first heat treatment or wherein, afterwards the open-cell element which is obtained from the plastic element from the material with which the bodies are formed is cut by forces and thereby separated bodies can be obtained.

A method of: providing an emulsion having a zinc powder and a liquid phase; drying the emulsion to form a sponge; sintering the sponge in an inert atmosphere to form a sintered sponge; heating the sintered sponge in an oxidizing atmosphere to form an oxidized sponge having zinc oxide on the surface of the oxidized sponge; and heating the oxidized sponge in an inert atmosphere at above the melting point of the zinc. A method of: providing an emulsion comprising a zinc powder and a liquid phase; placing the emulsion into a mold, wherein the emulsion is in contact with a metal substrate; and drying the emulsion to form a sponge.

A method of: providing an emulsion having a zinc powder and a liquid phase; drying the emulsion to form a sponge; sintering the sponge in an inert atmosphere to form a sintered sponge; heating the sintered sponge in an oxidizing atmosphere to form an oxidized sponge having zinc oxide on the surface of the oxidized sponge; and heating the oxidized sponge in an inert atmosphere at above the melting point of the zinc. A method of: providing an emulsion comprising a zinc powder and a liquid phase; placing the emulsion into a mold, wherein the emulsion is in contact with a metal substrate; and drying the emulsion to form a sponge.

A method of making a light weight component is provided. The method including the steps of: forming a metallic foam core into a desired configuration; applying an external metallic shell to an exterior surface of the metallic foam core after it has been formed into the desired configuration; and attenuating the component to a desired frequency by forming a plurality of openings in the external metallic shell.

Disclosed are methods of making porous zinc electrodes. Taken together, the steps are: forming a mixture of water, a soluble compound that increases the viscosity of the mixture, an insoluble porogen, and metallic zinc powder; placing the mixture in a mold to form a sponge; optionally drying the sponge; placing the sponge in a metal mesh positioned to allow air flow through substantially all the openings in the mesh; heating the sponge in an inert atmosphere at a peak temperature of 200 to 420° C. to fuse the zinc particles to each other to form a sintered sponge; and heating the sintered sponge in an oxygen-containing atmosphere at a peak temperature of 420 to 700° C. to form ZnO on the surfaces of the sintered sponge. The heating steps burn out the porogen.

Disclosed are methods of making porous zinc electrodes. Taken together, the steps are: forming a mixture of water, a soluble compound that increases the viscosity of the mixture, an insoluble porogen, and metallic zinc powder; placing the mixture in a mold to form a sponge; optionally drying the sponge; placing the sponge in a metal mesh positioned to allow air flow through substantially all the openings in the mesh; heating the sponge in an inert atmosphere at a peak temperature of 200 to 420° C. to fuse the zinc particles to each other to form a sintered sponge; and heating the sintered sponge in an oxygen-containing atmosphere at a peak temperature of 420 to 700° C. to form ZnO on the surfaces of the sintered sponge. The heating steps burn out the porogen.